Multi-ion mixed solution, preparation method and application thereof, and oral care product containing multi-ion mixed solution

An oral care and multi-ion technology, applied in the field of oral care, can solve the problems of slow release of active ingredients and poor fluidity, and achieve the effect of enhancing acid resistance, improving acid erosion resistance, and strengthening teeth

Pending Publication Date: 2021-12-10
四川涑爽医疗用品有限公司 +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problems of slow release of active ingredients and poor fluidity of the existing solid powder calcium-silicon-based bioactive materials, the present invention provides a multi-ion mixture, its preparation method and application, and oral care containing the multi-ion mixture. product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-ion mixed solution, preparation method and application thereof, and oral care product containing multi-ion mixed solution
  • Multi-ion mixed solution, preparation method and application thereof, and oral care product containing multi-ion mixed solution
  • Multi-ion mixed solution, preparation method and application thereof, and oral care product containing multi-ion mixed solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] This embodiment provides a method for preparing a multi-ion mixed liquid, specifically weighing the following raw materials by weight: SiO 2 30 parts, CaO 10 parts, K 2 O 10 parts and P 2 o 5 2 parts, mix each raw material component and place it at a heating temperature of 1300 ° C for 100 min to obtain a homogeneous mixture, prepare normal temperature pure water according to the ratio of 600 parts by weight of water per 100 parts by weight of raw materials, and prepare the obtained homogeneous The mixture is placed in pure water at normal temperature at the original heating temperature, and the homogeneous mixture is quenched in water to burst, and after cooling, the filtrate is collected by filtration and is the multi-ion mixture.

Embodiment 2

[0044] This embodiment provides a method for preparing a multi-ion mixed liquid, specifically weighing the following raw materials by weight: SiO 2 35 parts, CaO15 parts, K 2 O12 parts and P 2 o 5 3 parts, each raw material component is mixed and melted at 1400°C for 90 minutes to obtain a homogeneous mixture, and the ratio of 700 parts by weight of water per 100 parts by weight of raw materials is used to prepare normal temperature pure water, and the obtained homogeneous The mixture is placed in pure water at normal temperature at the original heating temperature, and the homogeneous mixture is quenched in water to burst, and after cooling, the filtrate is collected by filtration and is the multi-ion mixture.

Embodiment 3

[0046] This embodiment provides a method for preparing a multi-ion mixed liquid, specifically weighing the following raw materials by weight: SiO 2 40 parts, CaO 20 parts, K 2 O 15 parts and P 2 o 5 4 parts, mix each raw material component and place it at a heating temperature of 1500 ° C for 80 minutes to obtain a homogeneous mixture, prepare normal temperature pure water according to the ratio of 800 parts by weight of water per 100 parts by weight of raw materials, and prepare the obtained homogeneous The mixture is placed in pure water at normal temperature at the original heating temperature, and the homogeneous mixture is quenched in water to burst, and after cooling, the filtrate is collected by filtration and is the multi-ion mixture.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multi-ion mixed solution, a preparation method and application thereof, and an oral care product containing the multi-ion mixed solution, and belongs to the technical field of oral care. In order to solve the problems of slow release of effective components and poor fluidity of the existing solid powdery calcium-silicon-based bioactive material, the invention provides the preparation method of the multi-ion mixed solution. The method comprises the following steps: uniformly mixing all raw material components, and performing melting at a certain heating temperature to obtain a uniform mixture; and and putting the mixture into normal-temperature water at the original heating temperature, quenching the uniform mixture in water to explode, performing cooling, performing filtering, and collecting filtrate to obtain the multi-ion mixed solution. The liquid calcium-silicon-based bioactive material provided by the invention can be used as a special-effect active matter for preventing caries, remineralizing and resisting dentin hypersensitivity to be widely applied to various oral care products, can effectively assist in treating various symptoms such as gingivitis, periodontitis and pulpitis, is safe and non-toxic to use, and has a wide application prospect.

Description

technical field [0001] The invention belongs to the technical field of oral care, and in particular relates to a multi-ion mixed liquid, a preparation method and application thereof, and an oral care product containing the multi-ion mixed liquid. Background technique [0002] Caries is a progressive lesion of dental hard tissue caused by a combination of factors in the oral cavity, manifested as demineralization of inorganic matter and decomposition of organic matter, and with the development of the disease there is a change from color to substantial lesion evolution process. Small white spots on the teeth are a sign of demineralization, also called decalcification. This is due to the loss of calcium and phosphorus on the exposed enamel surface, poor oral hygiene, and the accumulation of plaque or bacteria to produce acid, which will slowly corrode the enamel, thereby changing the color of the tooth, which is white or yellowish. [0003] Dentin hypersensitivity, as a commo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/25A61K8/19A61K8/24A61Q11/00A61P1/02
CPCA61K8/25A61K8/19A61K8/24A61Q11/00A61P1/02
Inventor 关晴光肖丽娟李明邹萍范玉奇
Owner 四川涑爽医疗用品有限公司