Manufacturing method of ceramic artwork
A production method and art technology, which can be applied to clay products, other household appliances, household appliances, etc., can solve the problems of brittleness, weak three-dimensional effect, low strength, etc. Good fire and water resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] a. Ingredients: Clay includes the following raw materials in parts by weight: 30 parts of high-temperature pottery clay, 20 parts of medium-temperature china clay, 40 parts of kaolin, 10 parts of pyrophyllite, 5 parts of metal powder, 6 parts of quartz sand, 5 parts of basalt fiber, and 4 parts of carbon fiber 5 parts, 5 parts of petroleum resin, 20 parts of water.
[0031] Pulverize high-temperature clay, medium-temperature porcelain clay, kaolin, pyrophyllite, metal powder, quartz sand, basalt fiber, and carbon fiber, pass through a 150-mesh sieve, mix, add water and stir, and then pass through a 300-mesh sieve to make clay, which is product A;
[0032] b, soft mud: take product A and knead it to form product B with a moisture content of 15%;
[0033] c, mud pressing: use the mud pressing board to press the B product placed in the mold 1 into a mud board, and the mold is as follows image 3 As shown, the bottom of the mold 1 is provided with a mold cavity 2, the peri...
Embodiment 2
[0038] a. Ingredients: Clay includes the following raw materials in parts by weight: 40 parts of high-temperature pottery clay, 30 parts of medium-temperature china clay, 40 parts of kaolin, 15 parts of pyrophyllite, 8 parts of metal powder, 10 parts of quartz sand, 10 parts of basalt fiber, and 8 parts of carbon fiber 8 parts, 8 parts of petroleum resin, 50 parts of water.
[0039] Pulverize high-temperature clay, medium-temperature china clay, kaolin, pyrophyllite, metal powder, quartz sand, basalt fiber, and carbon fiber, pass through a 100-mesh sieve, mix, add water and stir, and then pass through a 200-mesh sieve to make clay, which is product A;
[0040] b. soft clay: take product A and knead it, and add iron oxide and feldspar during the kneading process to form product B with a moisture content of 24%;
[0041] c, mud pressing: use the mud pressing board to press the B product placed in the mold 1 into a mud board, and the mold is as follows image 3 As shown, the bot...
Embodiment 3
[0046] a. Ingredients: Clay includes the following raw materials in parts by weight: 35 parts of high-temperature pottery clay, 25 parts of medium-temperature china clay, 35 parts of kaolin, 13 parts of pyrophyllite, 6 parts of metal powder, 8 parts of quartz sand, 7 parts of basalt fiber, and 6 parts of carbon fiber 6 parts, 6 parts of petroleum resin, 30 parts of water.
[0047] High-temperature pottery clay, medium-temperature porcelain clay, kaolin, pyrophyllite, metal powder, quartz sand, basalt fiber, and carbon fiber are pulverized, passed through a 120-mesh sieve, mixed, stirred with water, and then passed through a 250-mesh sieve to make clay, which is product A;
[0048] b. Soft mud: take product A and knead it, and add copper oxide during the kneading process to form product B with a moisture content of 20%;
[0049] c, mud pressing: use the mud pressing board to press the B product placed in the mold 1 into a mud board, and the mold is as follows image 3 As shown...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| depth | aaaaa | aaaaa |
| depth | aaaaa | aaaaa |
Abstract