High-humic-acid soft soil curing agent adopting solid waste inorganic binder and preparation method of high-humic-acid soft soil curing agent

A technology of inorganic binder and humic acid, applied in chemical instruments and methods, organic fertilizers, applications, etc., can solve problems such as large environmental impact, achieve simple construction process, good economic and environmental benefits, and improve the effect of compactness

Pending Publication Date: 2022-03-01
吉林建筑科技学院
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, strong acid is generally used to treat humic acid. Although it has a certain effect, it has a great impact on the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high humic acid soft soil curing agent using solid waste inorganic binders, comprising the following raw materials in parts by weight: 50 parts of inorganic binders, 6 parts of activators, 7 parts of ion replacement agents, and 8 parts of humic acid modifiers , 8 parts of water-repellent agent, 5 parts of early strength agent, 6 parts of water-reducing agent, 5 parts of filler, and 5 parts of air-entraining agent. The main chemical composition of steel slag is calcium oxide 35%-41%, magnesium oxide 7%-12%, silicon dioxide 9%-11%. The main chemical composition of calcined coal gangue powder is 50%-65% of silica, 15%-35% of alumina, and 2%-15% of iron oxide. The main chemical composition of blast furnace slag is calcium oxide 38%-42%, silicon dioxide 33%-35%, alumina 12%-17%. The inorganic binder includes the following raw materials by weight: 8 parts of steel slag, 7 parts of quicklime, 25 parts of Portland cement, 5 parts of calcined coal gangue powder, and 5 parts o...

Embodiment 2

[0034] A high humic acid soft soil curing agent using solid waste inorganic binders, comprising the following raw materials in parts by weight: 45 parts of inorganic binders, 7 parts of activators, 6 parts of ion replacement agents, and 10 parts of humic acid modifiers , 8 parts of water-repellent agent, 5 parts of early strength agent, 8 parts of water-reducing agent, 6 parts of filler, and 5 parts of air-entraining agent. The inorganic binder includes the following raw materials in parts by weight: 7 parts of steel slag, 6 parts of quicklime, 24 parts of Portland cement, 4 parts of calcined coal gangue powder, and 4 parts of blast furnace slag. 75% or more, steel slag, blast furnace slag, quicklime, and calcined coal gangue powder are sent to a ball mill to grind for 12 minutes, and then stirred with Portland cement to obtain an inorganic binder. The water reducer is polycarboxylate high-efficiency water reducer and calcium lignosulfonate according to the weight ratio of 1:1...

Embodiment 3

[0041] A high humic acid soft soil curing agent using solid waste inorganic binders, comprising the following raw materials in parts by weight: 40 parts of inorganic binders, 8 parts of activators, 8 parts of ion replacement agents, and 10 parts of humic acid modifiers , 9 parts of water-repellent agent, 6 parts of early strength agent, 7 parts of water-reducing agent, 6 parts of filler, and 6 parts of air-entraining agent. The inorganic binder includes the following raw materials in parts by weight: 6 parts of steel slag, 5 parts of quicklime, 20 parts of Portland cement, 3 parts of calcined coal gangue powder, and 3 parts of blast furnace slag. 75% or more, steel slag, blast furnace slag, quicklime, and calcined coal gangue powder are sent to a ball mill to grind for 10 minutes, and then stirred with Portland cement to obtain an inorganic binder. The water reducer is polycarboxylate high-efficiency water reducer and calcium lignosulfonate according to the weight ratio of 1:1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-humic-acid soft soil curing agent adopting a solid waste inorganic binder and a preparation method of the high-humic-acid soft soil curing agent, and belongs to the technical field of curing agents. Comprising the following raw materials in parts by weight: 40-50 parts of an inorganic binding material, 6-8 parts of an exciting agent, 6-10 parts of an ion replacing agent, 8-10 parts of a humic acid modifier, 8-10 parts of a water repellent, 5-8 parts of an early strength agent, 6-10 parts of a water reducing agent, 5-8 parts of a filling agent and 5-8 parts of an air entraining agent. The invention has the following effects and advantages: when the soil containing humic acid is cured, the traditional cement is often low in strength due to the existence of humic acid. According to the invention, the influence of humic acid on soil solidification is especially solved, good economic benefits and environmental benefits are achieved, and the aspects of strength, durability, waterproofness and the like are also powerfully guaranteed.

Description

technical field [0001] The invention belongs to the technical field of curing agents, in particular to a high humic acid soft soil curing agent using solid waste inorganic binders and a preparation method thereof. Background technique [0002] In order to meet the needs of production and life, people have long applied plant fibers to improve the engineering properties of soil. With the invention of lime, lime became a soil improvement material. Since the invention of cement, cement soil has gradually gained people's attention due to its excellent reinforcement effect. Because lime soil and cement soil have good mechanical properties and water stability, and have a certain degree of frost resistance, they are widely used in the construction of roads, ports, airports and other projects. [0003] Some special soils in nature have low strength, unstable properties, expansion and contraction when exposed to water and dehydration, and cannot be directly used as filling materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K17/48C09K103/00
CPCC09K17/48C09K2103/00
Inventor 赵俭斌王启
Owner 吉林建筑科技学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com