Protection method of magnesium alloy workpiece for marine environment

A marine environment, magnesium alloy technology, applied in the plating of superimposed layers, metal material coating processes, devices for coating liquids on surfaces, etc. and other problems, to achieve the effects of surface conductivity and weight reduction, good quality consistency and high bonding strength

Pending Publication Date: 2022-05-24
CHINA ELECTRONICS TECH GRP CORP NO 14 RES INST
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of magnesium alloy parts used in the harshest marine environment, a single conductive layer or a non-conductive covering layer, cannot meet the requirements of use, and has become a bottleneck restricting its application in specific fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Taking the magnesium alloy component unit housing of the shipboard electronic equipment as an example, the following steps are implemented, and the technical solution of the present invention is specified.

[0017] 1. Acceptance: Visual inspection of the shell appearance, no heavy oil stains, scratches, bumps and other mechanical damage on the surface.

[0018] 2. Installation: Select the appropriate hanger and position to ensure good conductivity.

[0019] 3. Oil removal: neutral degreaser, chemical degreasing, until exhaustion.

[0020] 4. Hot water washing: in hot water of 60 ° C ~ 70 ° C, rinse for 10s ~ 15s.

[0021] 5. Cold water washing: secondary counter-current, rinsing 15s ~ 20s.

[0022] 6. Micro-arc oxidation: sodium aluminate 25g / L~30g / L, sodium fluoride 8g / L~10g / L, sodium hydroxide 5g / L~10g / L; solution temperature 20°C~40°C, oxidation current density 5A / dm 2 ～8A / dm 2 The oxidation time is 40min~50min, the thickness of the oxide film is 20μm~30μm, and it is not...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a protection method of a magnesium alloy workpiece for a marine environment, which adopts double-layer protection of an inner layer and an outer layer, and comprises the steps of micro-arc oxidation, conductive paint coating, baking and curing, alkaline chemical nickel plating, acidic chemical nickel plating, sealing and drying, the inner layer adopts a micro-arc oxidation film which is firmly combined with a matrix, and the outer layer adopts a micro-arc oxidation film which is firmly combined with the matrix; the outer layer adopts double-layer nickel plating of a bottom plating layer and a surface plating layer, the bottom plating layer adopts alkaline chemical nickel plating and is plated on the inner layer, the combination is firm, the surface plating layer adopts acid chemical nickel plating and is plated on the bottom plating layer, sealing treatment is performed, the porosity is reduced, the surface is compact, and the finished product is silver gray in appearance, slightly yellow, high in percent of pass, good in quality consistency and free of bubbling or layering phenomenon; through a 200 DEG C thermal shock test, the magnesium alloy micro-arc oxidation film is continuous, uniform, complete and free of pulverization, looseness and scratches, through a 672 h neutral salt spray test, the protection grade Rp is not lower than 9 grade, and the technical bottleneck that the magnesium alloy micro-arc oxidation film is difficult to be plated with a metal coating is broken through.

Description

Technical field [0001] The present invention belongs to the field of surface treatment technology, specifically relates to a marine environmental protection technology. Background [0002] Magnesium alloy is one of the lightest metal structural materials, low density than aluminum alloy, high strength and stiffness, low elastic modulus, superior damping and shock absorption performance, good thermal conductivity, machining performance and electromagnetic shielding performance, widely used in the automotive industry, aerospace and 3C product industry. [0003] Multifunctional measuring vessels are equipped with a variety of electronic equipment, which has strict weight restrictions, and the need for miniaturization and lightweighting is becoming more and more urgent. Magnesium alloys gradually replace aluminum alloys, such as TR components with a large installed number, which ensures the weight reduction effect and improves the maneuverability of the measuring ship. [0004] Magne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C28/00C25D11/30C23C18/36B05D3/02B05D7/14B05D7/24
CPCC23C28/322C23C28/345C25D11/026C25D11/30C23C18/36B05D7/14B05D7/24B05D3/0254B05D2504/00
Inventor 侯彬王伟陆洋吴礼群
Owner CHINA ELECTRONICS TECH GRP CORP NO 14 RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap