Production process of terminal hydroxy liquid polybutadiene

A liquid polybutadiene and production process technology, which is applied in the production process field of hydroxyl-terminated liquid polybutadiene, can solve the problems of unsmooth production processes, unstable control of process parameters, unstable product quality, etc., and achieve Reduce mechanical separation methods, good drying effect, and increase the effect of sedimentation

Inactive Publication Date: 2003-09-17
SHANDONG QILU ETHYLENE CHEM
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. The product quality is unstable and fluctuates greatly;
[0006] 2. The production yield of the product is low and the production cost is high;
[0007] 3. There is emulsification phenomenon in the production process, and all links of the production process are not smooth;
[0008] 4. The formula is unreasonable, the control of process parameters is unstable, and there is no guarantee of safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Use a pump to feed butadiene into a 10% sodium hydroxide alkali washing tank, remove the polymerization inhibitor in the butadiene to below 30ppm, and then pass it into the water washing tank to remove the trace amount of alkali remaining in the butadiene, Then put it in the butadiene metering tank for later use.

[0024] The concentration of butadiene through the above-mentioned treatment is 99.5%, wherein the alkyne content is less than 50ppm, and 27.5% hydrogen peroxide and 95% ethanol are added to 1000 liters of mechanical seal according to the weight ratio of 1: 0.047: 0.8 (recommended pure amount) to react In the kettle, the temperature was raised rapidly to 117° C. within half an hour and reacted for 2.5 hours. After the polymerization reaction, the temperature of the product is lowered to 75°C. After degassing, the material is filtered from the kettle to the settling tank for sedimentation and stratification. The oil phase (glue) is moved to the water washing ta...

Embodiment 2

[0027] According to the technique of Example 1, butadiene was reacted with 27.5% hydrogen peroxide and 95% ethanol in a weight ratio of 1:0.030:0.65 (equivalent to pure amount). The reaction temperature was 119°C, and the reaction time was 2 hours.

[0028] The hydroxyl value of the product terminal hydroxyl liquid polybutadiene is 0.60mmol / g, the number average molecular weight is 3800Mn, the viscosity is 8.4(Pa.S, 40°C), the moisture is 0.05(m / m), and the peroxide<0.05%( m / m).

Embodiment 3

[0030] According to the technique of Example 1, butadiene was reacted with 27.5% hydrogen peroxide and 95% ethanol in a weight ratio of 1:0.041:0.95 (equivalent to pure amount). The reaction temperature was 115°C, and the reaction time was 3 hours.

[0031] The hydroxyl value of the product terminal hydroxyl liquid polybutadiene is 0.76mmol / g, the number average molecular weight is 3000Mn, the viscosity is 3.1 (Pa.S, 40°C), the moisture content is 0.05 (m / m), and the peroxide is less than 0.05% ( m / m).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hydroxyl valueaaaaaaaaaa
Viscosityaaaaaaaaaa
Hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

A process for preparing liquid-state hydroxy-terminated polybutadiene features that the butadiene and H2O2 as trigger take part in polymerizing reaction in organic solvent at 90-120 deg.C for 1-3 hr and the Wt ratio of butadiene, H2O2 and organic solvent is 1:(0.021-0.16):(0.5-0.95). Its advantages are short process, high output rate, and high quality of product.

Description

technical field [0001] The invention relates to a production process of hydroxyl-terminated liquid polybutadiene. Background technique [0002] Hydroxyl-terminated liquid polybutadiene, also known as polybutadiene diol, referred to as HTPB, is a liquid polymer developed in the 1960s. It can be made into a three-dimensional network structure through chain extension and cross-linking. Elastomer, because it has the same properties as solid rubber, is also called liquid rubber. In 1971, ARCO in the United States built an industrialized production device, and then the former Soviet Union, France, and Japan also had corresponding industrialized devices put into production. It was first used as a solid rocket propellant and a rocket engine lining. In addition to military use, it also has many uses in civilian use: (1) Modifier of rubber and plastic; (2) Electrical potting material; (3) Sealing material; (4) Adhesive; (5) Casting tires and repairing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F136/06
Inventor 常传新刘洪华于志清杨洪胜崔文军周文凭张传芬
Owner SHANDONG QILU ETHYLENE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com