Activating method for nonmetallic base material surface chemical coated metal

A technology for plating metal and substrate surface, applied in liquid chemical plating, metal material coating process, coating and other directions, can solve the problems of high product cost, low activity, poor activation effect, etc., to reduce production costs , Guaranteed activation effect, good activation effect

Inactive Publication Date: 2005-07-27
HUNAN CORUN NEW ENERGY CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this activation method has a relatively simple process, if a single silver active solution is used, not only the amount of silver nitrate is large, but also the activation effect is found to be poor in actual production, resulting in large areas of missed plating in subsequent electroless plating, which cannot be used in production; If a single palladium activation solution is used, due to the high price and scarcity of palladium, the product cost is high and the product market competitiveness is not strong
Therefore, it has been proposed to use a new activation process of non-precious metals one after another. Gao Deshu et al. (Research on Colloidal Activation Solution for Non-metallic Plating [J], Surface Technology, 1993, 22) impregnated the ABS plastic substrate with nickel and copper hydroxide colloidal solution, with NaBH 4 Reduction of divalent nickel and copper to metal state, and then electroless plating, achieves a certain effect, but the binding force of the coating is poor, the activity is far lower than the activator made of palladium salt, and it is difficult to achieve complete coverage, and there are reports (non-metallic materials Research on Activation Process of Electroless Nickel Plating, Material Protection, Volume 34, Issue 2, February 2001) Activate ceramics or sodium glass with high concentration ammonium nickel salt, and then heat the adsorbed nickel salt at a temperature above 200°C It can be decomposed into a substance with high catalytic activity, and then the chemical plating can also receive a good chemical plating effect, but its high pyrolysis temperature cannot be used for polyurethane sponge, non-woven fabrics, cotton cloth, chemical fiber fabrics, fiber nets , fiber cloth and other substrates with low thermal degradation temperature, the application range is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Prepare an aqueous solution with silver nitrate and ammonia water, wherein the total concentration of silver is 0.6g / L, adjust to a pH value of 10 and keep it to obtain a colloidal silver activation solution; prepare an aqueous solution with palladium chloride and hydrochloric acid, and the total concentration of palladium is 0.03 g / L, pH value is 3.0, makes palladium chloride solution activation solution; The polyurethane sponge after sensitization is immersed in colloidal silver activation solution, and activation temperature is 40 ℃, according to the immersion time of every square meter substrate 20 Seconds to calculate the required time, and then immerse in the palladium chloride solution activation solution, the activation temperature is 45°C, the required time is calculated according to the immersion time of 2 minutes per square meter of substrate, the activated substrate is chemically copper-plated, no Missing spots.

Embodiment 2

[0018] Be mixed with silver nitrate, ammoniacal liquor to make aqueous solution, make the total concentration of silver in the solution be 2g / L, be adjusted to pH value 12 and keep, make colloidal silver activation solution; Be mixed with palladium chloride, hydrochloric acid aqueous solution, the total concentration of palladium is 0.06g / L, pH value is 2.5, prepared palladium chloride aqueous activation solution; immerse the sensitized ceramics into the colloidal silver activation solution, the activation temperature is 55°C, and the immersion time per square meter of substrate is 10 seconds. The required time, and then immersed in the activation solution of palladium chloride aqueous solution, the activation temperature is 55 ° C, the required time is calculated according to the immersion time of 30 seconds per square meter of the substrate, the activated substrate is chemically nickel-plated, and there is no missing plating spot.

Embodiment 3

[0020] Prepare an aqueous solution with silver nitrate and ammonia water, make the total concentration of silver in the solution be 0.3g / L, adjust the pH value to be alkaline and keep it, and obtain a colloidal silver activation solution; prepare an aqueous solution with palladium chloride and hydrochloric acid, wherein the palladium The total concentration is 0.012g / L, and the palladium chloride aqueous solution activation solution is obtained; the non-woven fabric after the sensitization is immersed in the palladium chloride aqueous solution activation solution, the activation temperature is 42 ° C, and the immersion time per square meter of substrate Calculate the required time in 100 seconds, and then immerse in the colloidal silver activation solution. The activation temperature is 45°C. The required time is calculated according to the immersion time of 30 seconds per square meter of substrate. After activation, the substrate is chemically plated with cobalt without leakage...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention was about a technology of Ag-Pa compound activation, the non-metal material was activated by Ag and Pa, the other metal was plating the surface of it. Ag concentration of activate solution was 0.06-2g / L, Pa concentration of activate solution was 0.006-0.06g / L, the activate time was more than 10 seconds while the material activated in the Ag activate solution, more than 20 seconds in the Pa activate solution, the activate temperature was 40-60 deg.C. Its advantages include good activation, saving the use level of metal; fit for a lot of material; suit for the technology plating in the later process; fit for commercial production.

Description

technical field [0001] The invention relates to a method for chemically plating metal on the surface of a non-metal substrate, in particular to an activation method for chemically plating metal. technical background [0002] Electroless metal plating is a commonly used metal coating method, which can be carried out on metal and non-metal substrates. Before electroless plating on the surface of the non-metallic substrate to make it conductive, the non-substrate must be activated, and a catalyst that can catalyze the electroless plating must be deposited on its surface, otherwise the subsequent electroless plating cannot be carried out. As a pretreatment of electroless plating, the traditional activation process is to treat the substrate with SnCl 2 After the solution is sensitized, it is activated by a single noble metal solution such as palladium or silver. For example, Liu Shaozhi disclosed in his Chinese patent "A Fabric for Shielding Electromagne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/18C23C18/30
Inventor 陶维正唐振武易保华贺持缓刘畅李国良戴桂中唐发德邓美华
Owner HUNAN CORUN NEW ENERGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products