Nano silver antiseptic gel for treating women's genital tract infection and its prepn and application
A technology of nano silver gel and reproductive tract infection, applied in the field of external use of antibacterial nano silver gel, can solve the problems of complex process, complex composition, no public treatment of women's lower reproductive tract infection, etc., and achieves good permeability and fast onset. , excellent curative effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0035] Ingredients: nano-silver colloid: containing nano-silver particle size 1-20 nm, nano-silver content 35000ppm, 10g;
[0036] Polyethylene glycol: 10g
[0037] Glycerin: 10g
[0038] Deionized water: 970g
[0039] Sodium dodecyl sulfonate: 0.005g
[0040] Add the above raw materials into the blender, stir for 2 hours, make it mix evenly, and form a gel; then pack it into the gel dispenser, add outer packaging, and obtain a gel containing 350ppm of nano-silver, each gel The container contains 3g of product. The gel giver, such as figure 1 As shown, it is mainly composed of cap 1, gel supply body 2, and push rod 3. The gel supply body 2 is a hollow cylinder with a length of 10-12cm and an outer diameter of 11mm. The front end is a spherical surface , there is a hole on the spherical surface, a cap 1 is placed on the hole, antibacterial nano-silver gel is housed in the gel body 2, and a push rod 3 is inserted in the middle of the gel body 2, and the push rod 3 can be us...
Embodiment 2
[0042] Ingredients: nano-silver colloid: containing nano-silver particle size 1-20 nm, nano-silver content 4000ppm, 10g;
[0043] Polycarbophil: 20g
[0044] Glycerin: 10g
[0045] Deionized water: 960g
[0046] Sodium dodecyl sulfate: 0.003g
[0047] Other conditions were the same as in Example 1, except that the stirring time was 1 hour to obtain a gel containing 40 ppm of nanosilver.
Embodiment 3
[0049] Ingredients: nano-silver colloid: containing nano-silver particle size 1-20 nm, nano-silver content 1000ppm, 10g;
[0050] Carbomer: 30g
[0051] Glycerin: 10g
[0052] Deionized water: 950g
[0053] Sodium dodecyl sulfate: 0.001g
[0054] Other conditions are with embodiment 1. Only the stirring time is 0.5 hour, and a gel containing 10 ppm of nano-silver is obtained.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com