Blood filter material and process for preparing same

A technology of blood filtration and manufacturing method, which is applied in the field of blood filtration materials and its manufacturing, and can solve the problems of heterogeneous reaction of blood and decline of blood quality, and achieve the effects of excellent blood compatibility, shortened starting time, and reduced average pore size

Inactive Publication Date: 2006-12-27
DONGHUA UNIV
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polysaccharide-type coating modifier will cause a heterogeneous reaction in the blood, and the platelets will be activated, resulting in a decrease in blood quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] After the sericin on the cocoon surface was removed by the alkaline method, 29.6 grams of white silk protein obtained therein was put into 266.4 grams of 47% (percentage by weight) lithium bromide aqueous solution at 20° C., and the silk protein was dissolved after 22 hours. A silk fibroin / lithium bromide aqueous solution with a silk fibroin content of 10% is formed, diluted with water for 3 times, filtered, and passed through a dialysis bag to remove lithium bromide. Obtaining silk fibroin content is 1480 grams of the silk fibroin aqueous solution of 2% (percentage by weight).

[0026] Get the above-mentioned 450 grams of 2% (weight percent) silk fibroin aqueous solution and 4 grams of medical-grade polyurethane aqueous solution with a solid content of 25% (weight percent) and stir for 5 minutes at a temperature of 20° C. to obtain the silk fibroin used in the coating. / Polyurethane blending aqueous solution 454 grams.

[0027] At a temperature of 20°C, pour the above...

Embodiment 2

[0029] After the sericin on the surface of silkworm cocoons is removed by soap boiling, 10 grams of white silk protein obtained therein is put into 200 grams of 47% (percentage by weight) lithium bromide aqueous solution at 25° C., and the silk protein dissolves after 15 hours. , forming a silk fibroin / lithium bromide aqueous solution with a silk fibroin content of 5% (percentage by weight), adding water to dilute 2 times, filtering, and removing lithium bromide through a dialysis bag. Obtaining silk fibroin content is 625 grams of the silk fibroin aqueous solution of 1.6% (percentage by weight).

[0030]Get the above-mentioned 625 grams of 1.6% (weight percent) silk fibroin aqueous solution and 300 grams of medical grade polyurethane aqueous solution with a solid content of 30% (weight percent) and stir for 8 minutes at a temperature of 25° C. to obtain the silk fibroin protein used for the coating. / Polyurethane blending aqueous solution 925 grams.

[0031] At 25°C, take th...

Embodiment 3

[0033] After the sericin on the cocoon surface was removed by the alkaline method, 20 grams of white silk protein obtained therein was put into 250 grams of 50% (percentage by weight) lithium bromide aqueous solution at 30° C., and the silk protein was dissolved after 15 hours. A silk fibroin / lithium bromide aqueous solution with a silk fibroin content of 8% (percentage by weight) is formed, diluted 2.5 times with water, filtered, and the lithium bromide is removed through a dialysis bag. Obtaining silk fibroin content is 1430 grams of the silk fibroin aqueous solution of 1.4% (percentage by weight).

[0034] Get above-mentioned 50 grams of 1.4% (percentage by weight) silk fibroin aqueous solution and 14 grams of medical grade polyurethane aqueous solution that solid content is 20% (percentage by weight) and stir at 30 ℃ of temperature for 8 minutes, obtain the silk fibroin protein used for coating / Polyurethane blending aqueous solution 64 grams.

[0035] At a temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a blood filtering material and its preparation method. The material is formed from filtration substrate and surface modified layer, wherein the filtration substrate is macromolecular nonwoven material processed by using melt-blowing method with density of 10-1000g/cm2, mean pore size of 0.1-100 mu m, thickness of 0.01-50mm, fiber diameter of 0.01-50 mu m; surface modified layer is formed from fibroin protein and polyurethane blended aqueous solution in 90-10:10-90 by weight; Conventional coating method is adopted, comprising blending medical polyurethane aqueous solution and self-made fibroin protein, applying the above blend on the surface of filtration substrate, drying, bonding, and curing. In the invention, the price of raw materials is low, and the products are provided with excellent blood compatibility, wettability, permeability and high filter efficiency which can be used as blood filtering materials.

Description

Technical field: [0001] The invention relates to a blood filter material and a manufacturing method thereof, in particular to a blood filter material and a manufacturing process technology of the surface coating modified by using silk fibroin / polyurethane blended aqueous solution as a coating agent. Background technique: [0002] Blood is one of the basic substances necessary to maintain human life activities. The components of blood include plasma and blood cells. Blood cells can be divided into red blood cells (6-9.5 μm), white blood cells (6-20 μm) and platelets (about 2 μm). Although blood type matching is considered in blood transfusion medicine, various transfusion reactions often occur due to transfusion of blood or blood components containing leukocytes, such as non-hemolytic febrile reaction, adult respiratory distress syndrome, platelet transfusion tolerance, etc.; In addition, viruses transmitted by blood transfusion, such as hepatitis B virus, hepatitis C virus,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/16B01D39/08
Inventor 王洪靳向煜吴海波殷保璞金雍炜
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap