Phosphorous epoxy resin composition

A technology of epoxy resin and composition, which is applied in the direction of epoxy resin glue, epoxy resin coating, adhesive type, etc., can solve the problems of poor heat resistance and human hazards, and achieve high dimensional stability and low Effects of hygroscopicity and excellent electrical characteristics

Active Publication Date: 2009-08-05
ELITE MATERIAL
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of bromine-based halogen compounds, combined with flame-retardant additives such as antimony trioxide, can make the flame-retardant properties of epoxy resin laminates meet the requirements of, for example, UL94V-0 grades, but containing Bromine-based halogen compounds will cause bromine to decompose when heated, and their heat resistance will deteriorate under long-term use, and flame retardants containing halogen components or antimony trioxide will produce dioxin and oxocene under high-temperature combustion. Compounds that are threatening to human health will undoubtedly bring serious harm to human beings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorous epoxy resin composition
  • Phosphorous epoxy resin composition
  • Phosphorous epoxy resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1、2

[0073] Embodiment 1, 2 and comparative examples 1 to 6

[0074] According to the composition and ratio shown in Table 1, the epoxy resin varnish was prepared in a container equipped with a stirrer and a condenser at room temperature.

[0075] Table 1 Example 1 Example 2 Comparative example 1 Comparative example 2 Comparative example 3 Comparative example 4 Comparative Example 5 Comparative Example 6 Phosphorus-containing epoxy resin (weight%) 51.5 48.7 52.6 49.2 46.3 43.6 41.3 62.8 Hardener 1 (% by weight) 12.4 7.9 8.9 9.7 10.5 15 Hardener 2 (wt%) 14.6 11.1 Hardener 3 (% by weight) 2.6 4.9 Hardener 4 (wt%) 25.7 25 31.5 34.4 37 39.3 41.3 12.6 Hardening Accelerator (wt%) 0.1 0.12 0.1 0.09 0.09 0.08 0.08 0.13 Epoxy resin 1 (weight %) Epoxy resin 2 (weight %) 7.9 9.4

[0076] Epoxy resin 3 (weight%) 7.7 7.4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The phosphorus-containing epoxy resin composition of the present invention comprises: (A) phosphorus-containing epoxy resin, (B) curing agent, (C) one or more epoxy resins and (D) inorganic filler material; Wherein with component ( Based on the total weight of A), (B) and (C), the hardener of the component (B) includes 15 to 30% by weight of a benzoxazine compound, and 2.5 to 9% by weight of styrene-maleic di anhydride copolymer. The phosphorus-containing epoxy resin composition of the present invention uses a specific content of benzoxazine compound and styrene-maleic anhydride copolymer as a hardener, not only has good flame retardancy and heat resistance, but also has a high dimension Stability, low moisture absorption and excellent electrical properties are suitable for making prepregs, adhesive sheets, semiconductor packaging materials, copper foil laminates, printed circuit boards, and semiconductor packaging substrates.

Description

technical field [0001] The present invention relates to a phosphorus-containing epoxy resin composition, in particular to a phosphorus-containing epoxy resin composition using a benzoxazine compound as a hardener. Background technique [0002] Due to the characteristics of easy processing, high safety, excellent mechanical properties and chemical properties, epoxy resin is widely used in fields such as coating, electrical insulation, civil engineering and construction materials, adhesives and laminated products. Among them, the laminated board made of epoxy resin has strong adhesion to reinforcing materials such as glass fiber cloth, no volatile matter is produced during hardening, and the forming shrinkage is small, so the laminated board obtained has a wide range of applications. The advantages of excellent mechanical strength, good electrical insulation, and good chemical resistance have greatly improved the reliability of laminated boards, making epoxy resin laminated bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08K5/357C09D163/00C09K3/10C09J163/00C09J7/00B05D1/18B05D7/14
Inventor 何昇骏周立明谢镇宇余利智钟新龙巫勤富钟明全林育德
Owner ELITE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com