A technology of wood-based panels and caragana, applied to flat products, manufacturing tools, rosin adhesives, etc., which can solve the problems of unsightly surface of the board, inability to be used to prepare furniture floors, inconvenient secondary processing, etc., and achieve light weight , reduce unit weight, low cost effect

Inactive Publication Date: 2008-03-26
INST OF PROCESS ENG CHINESE ACAD OF SCI +1
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although fly ash has the characteristics of high mechanical strength and light weight, the surface of the board prepared by this technology is not beautiful, especially it is not convenient for secondary processing, so it cannot be used to make furniture, office equipment, flooring, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1: prepare the caragana composite wood-based panel that furniture and office equipment are used

[0047] First prepare the adhesive used in this example: in a four-necked bottle, add rosin 302g, maleic anhydride 196g, ethylene glycol 124g, 1,2-propanediol 152g, phthalic anhydride 222g, nitrogen gas, Gradually raise the temperature to 160-230°C. During the reaction, remove the water released from the reaction. When the acid value reaches 50±20mgKOH / g, stop the reaction, cool down to 115°C, add 310g of styrene, stir evenly, and cool to room temperature.

[0048] The present embodiment prepares the caragana composite wood-based panel that furniture and office equipment are used and consists of:

[0049] Caragana 70 parts by weight;

[0050] 15 parts by weight of fly ash;

[0051] The present embodiment prepares 15 parts by weight of adhesive;

[0052] The initiator is benzamide peroxide, and its addition amount is 0.075 g; it is mixed and hot-pressed to form a ...

Embodiment 2

[0057] Embodiment 2: preparation is used for the caragana composite wood-based panel of floor

[0058] First prepare the adhesive used in this example: in a four-neck bottle, add rosin 302g, maleic anhydride 588g, ethylene glycol 620g, 1,2-propylene glycol 608g, phthalic anhydride 1332g, and nitrogen gas, Gradually raise the temperature to 160-230°C. During the reaction, remove the water released from the reaction. When the acid value reaches 50±20mgKOH / g, stop the reaction, lower the temperature to 105°C, add 1440g of styrene, stir evenly, and cool to room temperature.

[0059] The present embodiment prepares the caragana composite wood-based panel that is used for floor and consists of:

[0060] Caragana 80 parts by weight;

[0061] 10 parts by weight of fly ash;

[0062] This embodiment prepares 10 parts by weight of adhesive;

[0063] The initiator is benzamide peroxide, and its addition amount is 0.1 g; it is mixed and hot-pressed to form a plate.

[0064] Caragana co...

Embodiment 3

[0068] Embodiment 3: preparation is used for the caragana composite artificial of suspended ceiling

[0069] First prepare the adhesive used in this example: in a four-necked bottle, add 302g of rosin, 392g of maleic anhydride, 248g of ethylene glycol, 380g of 1,2-propylene glycol, 75g of triethylene glycol, phthalate Diformic anhydride 592g, blow nitrogen, gradually heat up to 160-230°C, during the reaction, remove the water released from the reaction, stop the reaction when the acid value reaches 50±20mgKOH / g, cool down to 95°C, add 790g of styrene , stir well, and cool to room temperature.

[0070] The present embodiment prepares the caragana composite wood-based panel that is used for suspended ceiling and consists of:

[0071] Caragana 85 parts by weight;

[0072] 10 parts by weight of fly ash;

[0073] The present embodiment prepares 5 parts by weight of adhesive;

[0074] The initiator is methyl ethyl ketone peroxide, and its addition amount is 0.1 g; it is mixed an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The present invention relates to one kind of composite intermediate peashrub board and its making process. The composite intermediate peashrub board is made with intermediate peashrub in 45-90 weight portions, fly ash in 5-35 weight portions, adhesive in 5-20 weight portions, and initiator in the amount of 0.5-3.5 wt% of the adhesive, and through the steps of cutting intermediate peashrub, dedusting, screening, peeling, milling, applying glue, drying, spreading, pre-pressing and hot pressing. The making process is simple and pollution-free, and uses no-formaldehyde adhesive. The produced composite intermediate peashrub board is environment friendly, water-proof, and suitable for in producing furniture, office equipment, floor board, etc.

Description

technical field [0001] The invention relates to a wood-based panel and a preparation method, in particular to a composite wood-based panel produced from caragana and fly ash as main raw materials and a preparation method thereof. Background technique [0002] Caragana is clustered, with strong roots, large plants and crowns, strong germination after sand burial, cold resistance, drought resistance, wind and sand resistance, and strong adaptability. It plays an important role in windbreak, sand fixation, and water and soil conservation. It is widely distributed in Leguminous shrubs in Northeast my country, North China and parts of Northwest China. Caragana is mostly planted in the "Three Norths" area by artificial direct seeding, and the survival rate of the planted forests is extremely high. In the follow-up project of the construction of the "Three North" shelterbelt system, caragana continues to be the main afforestation tree species, with great resource potential. In the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/08B27N1/02B27N3/18C09J193/04
Inventor 任天瑞何金太马海林
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap