Xylem filber-polyvinyl chloride composite material and method for producing the same

A technology of lignocellulosic material and polyvinyl chloride, which is applied in the field of composite materials and their preparation, can solve the problems of toxic gas, a large amount of black smoke, high flammability, and achieves the effects of easy operation, simple preparation method and low equipment requirements.

Inactive Publication Date: 2008-05-07
NORTHEAST FORESTRY UNIVERSITY
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of high flammability of wood fiber-polyvinyl chloride composite material, which will prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Specific embodiment 1: The wood fiber-polyvinyl chloride composite material of this embodiment is composed of 100 to 600 parts of polyvinyl chloride resin, 30 to 700 parts of wood fiber material, 3 to 145 parts of intumescent flame retardant, 1 parts by weight ratio. ~55 parts of copper oxide, 6~75 parts of heat stabilizer, 4~60 parts of plasticizer and 4~65 parts of compatibilizer; the intumescent flame retardant is made of pentaerythritol, ammonium polyphosphate and melamine according to 3:8 : The mass ratio is 6 and the degree of polymerization of ammonium polyphosphate is 1500-4000.

[0014] In this embodiment, the lignocellulosic material is mainly composed of polyhydroxy cellulose, hemicellulose, and lignin with a cross-linked structure. It is easy to be pyrolyzed and carbonized under acid catalysis. Therefore, the lignocellulosic fiber itself can also be used as an intumescent flame retardant Auxiliary char-forming agent to improve the flame retardant effect of intum...

Example Embodiment

[0015] Specific embodiment two: this embodiment is different from specific embodiment one in that the wood fiber-polyvinyl chloride composite material further includes 0.5-15 parts of lubricant, 6-195 parts of impact modifier, 0.2-6 parts colorant and / or 0.2-13 parts antioxidant. Others are the same as the first embodiment.

Example Embodiment

[0016] Specific embodiment three: This embodiment is different from specific embodiment two in that the lubricant is stearic acid, calcium stearate, zinc stearate, paraffin wax, polyethylene wax or chlorinated paraffin wax. Others are the same as the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a wood fiber-PVC composite material and a preparation method thereof, and relates to the composite material and the preparation method and solves the problem that: the wood fiber-PVC composite material has high combustibility and can produce a plurality of black smoke and noxious gas when in burning. The wood fiber-PVC composite material is mainly formed by weight part asfollow: 100 to 600 parts of PVC resin, 30 to 700 parts of wood fiber material, 3 to 145 parts of expansion flame retardant, 1 to 55 parts of copper oxide, 6 to 75 parts of heat stabilizer, 4 to 60 parts of plasticizer and 4 to 65 parts of compatibilizer. The preparation method is as follows: firstly, the material is mixed in advance; secondly, the material is squeezed out for shaping. The wood fiber-PVC composite material of the invention is tested according to the GB/T8924-2005 standard; the wood fiber-PVC composite material of the invention has an oxygen index bigger than 35 percent, has longignition time and does not produce drop melting, and belongs to nonflammable material. The preparation method for the wood fiber-PVC composite material of the invention is simple and easy for operati on, has low requirement to devices and is convenient for spreading and application.

Description

Technical field [0001] The invention relates to a composite material and a preparation method thereof. Background technique [0002] Wood fiber-polyvinyl chloride composite material is a new type of composite material formed by adding a large amount of wood fiber, wood powder, bamboo powder, straw powder and other wood fiber materials to polyvinyl chloride (PVC) resin (referred to as PVC-based wood plastic) Composite materials), with good processing properties, mechanical properties, price advantages and excellent woodiness. PVC-based wood-plastic composite material has low density and higher mechanical strength than wood, so it can be used instead of wood in packaging, load-bearing and other fields; in addition, the raw materials used are mainly forestry and agricultural wastes, so it is an economical and environmentally friendly material. There is great potential for applications in the fields of architecture, decoration, and furniture. [0003] Although polyvinyl chloride (PVC...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L97/02C08K5/57B29C47/40B29C47/92C08L51/06C08K5/541B29C48/92B29C48/40
CPCB29C48/92B29C2948/92704B29C2948/92895B29C2948/92904B29C48/40
Inventor 王清文白晓艳隋淑娟
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products