Nano double helix ecological globoid and preparation and application thereof

A double helix, spherical body technology, applied in the field of environmental protection, can solve the problems of poor firmness and mechanical strength, non-regeneration, poor effect, etc.

Inactive Publication Date: 2008-08-13
冯英昌
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The specific surface area of ​​these materials is very small, and the degree of firmness and mechanical strength are also very poor.
When using these materials, not only a high-strength external mechanical force is required to realize the purification process, which consumes manpower and material resources, but also its purification and filtration efficiency is very low, the effect is very poor, and it cannot be regenerated, and its application has great limitations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano double helix ecological globoid and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0096] Preparation of Spheroids I

[0097] materials and equipment

[0098] Ultrafine calcium carbonate ceramic powder (specification 0.5-5 nanometers) was purchased from Shanghai Institute of Nano Ultrafine Materials Co., Ltd.

[0099] Vinyl chloride monomer was purchased from Chlor-Alkali General Plant

[0100] Stabilizer Rare earth composite stabilizer was purchased from Guangzhou Dayang Auxiliary Factory

[0101] Molding aid ACR was purchased from Changzhou Plastic Additives Factory

[0102] Efficient coupling agent titanate, purchased from Changfeng Chemical

[0103] The twin-helix forming machine was purchased from Shanghai Xin'ao Forming Equipment Co., Ltd.

[0104] method

[0105] The raw materials are taken according to the following table:

[0106] Ultrafine Calcium Carbonate

ceramic powder

Vinyl chloride monomer

Rare earth composite stabilizer

ACR

Titanate

DOP

Weight (kg)

8

85

2.9

...

Embodiment 2

[0116] Preparation of Spheroids II

[0117] materials and equipment

[0118] Same as Example 1

[0119] method

[0120] The raw materials are taken according to the following table:

[0121] Ultrafine Calcium Carbonate

ceramic powder

Vinyl chloride monomer

Rare earth composite stabilizer

Molding Auxiliary ACR

Titanate

DOP

Weight (kg)

9

84

2

3

1

1

[0122] 1. Use ultrasonic waves and 0.2-2% high-efficiency coupling agent: titanate to micro-emulsify the surface of nano-ceramic powder;

[0123] 2. Evenly disperse the microemulsified nano-ceramic powder in the vinyl chloride monomer droplet suspended in the polymerization system, and physically adsorb and chemically react with the polyethylene monomer;

[0124] 3. In the polymerization kettle, according to the conventional suspension polymerization conditions, the vinyl chloride monomer is polymerized in situ on the surface of ...

Embodiment 3

[0130] Performance Testing

[0131] Refer to "Shanghai Sewage Comprehensive Discharge Standard" and "National Standard GB 8978-1996: Sewage Comprehensive Discharge Standard" for operation, and the analysis method is detailed in the above standard 1. Determination of suspended solids SS; 2. Determination of BOD5; 3. 1. Determination of COD; 4. Determination of algae; 5. Determination of total nitrogen; 6. Determination of total phosphorus; 7. Determination of ammonia; 8. Determination of turbidity.

[0132] Performance test methods, etc. and corresponding results:

[0133] Use supporting water treatment equipment to test the effect test of sewage treatment: the sewage is connected with the sewage treatment equipment through the pump to realize the dynamic circulation of water. After about 6 hours of circulation, test the turbidity, algae content and suspended solids of the successive water SS, BOD, COD and other indicators.

[0134] Test indicators

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The inside diameter ofaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Porosityaaaaaaaaaa
Login to View More

Abstract

The present invention provides a double helix nanophase ecosphere, having continuous double-helix, the surface is formed by extending of mass bends or each S shaped part. Each part shows radial arrangement to achieve maximal surface area and provide void ratio. This new design provides countless pleats on the surface of the double-helix, so as to have fantastic specific surface and poriness; and it further has stronger impact strength and tensile yield strength. The conglobulation of the invention contains nano ceramics powder, vinyl chloride monomer and all kinds of stabilizing agent and forming agent. The double helix nanophase ecosphere is used for water treatment, air purification, auto air filter, central air condition cycle water treatment, flowers and trees industry, health products industry, industrial filtering material, chemical fillings, catalyst carrier, the invention also provides a preparing method and use of the ecosphere.

Description

technical field [0001] The invention relates to the field of environmental protection, in particular to an ecological filter material. Background technique [0002] Due to the rapid development of industrialization and urbanization, the total annual discharge of industrial wastewater and urban sewage has reached 50 billion tons, and the treatment rate is low. A large amount of wastewater is discharged into natural water bodies, which has caused about 80% of our country's rivers and lakes to be affected to varying degrees. pollution. In the "Tenth Five-Year Plan" plan, by 2005, the national sewage treatment rate is planned to reach 45%, and the sewage treatment rate in cities with more than 500,000 residents will reach more than 60%, with a daily sewage treatment rate of more than 58 million tons. [0003] The rapid development of the aquaculture industry has changed the farming method from extensive farming to intensive farming. However, while increasing production and incr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J13/18B01D39/04C02F3/10
CPCY02W10/10
Inventor 冯英昌
Owner 冯英昌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products