Magnesium amide nano-particle hydrogen storage material and preparation thereof

A technology of nanoparticles and hydrogen storage materials, which is applied in the field of preparation of metal amino compounds, can solve the problems of Mg that cannot be prepared into single crystals, achieve excellent hydrogen absorption and desorption kinetic properties, improve hydrogen absorption and desorption kinetic properties, and sample purity high effect

Inactive Publication Date: 2008-10-08
PEKING UNIV
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the prior art cannot prepare single crystal Mg(NH 2 ) 2 particles, the resulting Mg(NH 2 ) 2 The particles are all polycrystalline polymers, and their sizes are above the micron level

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium amide nano-particle hydrogen storage material and preparation thereof
  • Magnesium amide nano-particle hydrogen storage material and preparation thereof
  • Magnesium amide nano-particle hydrogen storage material and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1, synthetic Mg (NH 2 ) 2 nanoparticles

[0016] (1) Put the magnesium block in the plasma arc heating furnace, after vacuuming, under 65%Ar / 35%NH with a total pressure of 0.9bar 3 (volume content) atmosphere, apply DC arc plasma to heat and evaporate magnesium and combine with NH 3 The reaction produces Mg 3 N 2 nanoparticles;

[0017] (2) the prepared Mg 3 N 2 Put the nanoparticles into the ammonia reaction furnace, heat the system to 325°C after vacuuming the system, pass through 4bar ammonia gas for 12 hours, and cool to room temperature to obtain Mg(NH 2 ) 2 particles.

Embodiment 2

[0018] Embodiment 2, synthetic Mg (NH 2 ) 2 nanoparticles

[0019] (1) Put the magnesium block in the plasma arc heating furnace, after vacuuming, under 40%N 2 / 60%NH 3 (Volume content) Under the mixed atmosphere, apply DC arc plasma to heat and evaporate magnesium and combine with NH 3 The reaction produces Mg 3 N 2 nanoparticles;

[0020] (2) the prepared Mg 3 N 2 Put the particles into a hydrogen reaction furnace. After the system is evacuated, 4 bar of ammonia gas is introduced, heated to 350°C, reacted for 6 hours, and cooled to room temperature to obtain Mg(NH 2 ) 2 particles.

Embodiment 3

[0021] Embodiment 3, synthetic Mg (NH 2 ) 2 nanoparticles

[0022] (1) Put the magnesium block in the hydrogen plasma electric arc heating furnace, after vacuuming, under the 30%Ar / 70%NH with a total pressure of 0.5bar 3 (Volume content) Under the mixed atmosphere, apply DC arc plasma to heat and evaporate magnesium and combine with NH 3 The reaction produces Mg 3 N 2 nanoparticles;

[0023] (2) the prepared Mg 3 N 2 Put the particles into a hydrogen reactor, heat the system to 250°C after evacuating the system, pass through 4bar ammonia gas for 20 hours, and cool to room temperature to obtain Mg(NH 2 ) 2 particles.

[0024] figure 1 Mg is the product of the above experiment 3 N 2 and Mg(NH 2 ) 2 The XRD (X-ray powder diffraction) figure, can clearly see that the prepared magnesium amido has a higher purity.

[0025] Figure 2a and 2b are the above experimental products Mg 3 N 2 and Mg(NH 2 ) 2 TEM (Transmission Electron Microscopy) image of nanoparticles, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an amino magnesium nano-particle product which can be used as hydrogen storage materials and a preparation method thereof. Nano magnesium nitride is prepared by the method of arc heating and is aminated to obtain Mg (NH2)2 particle product with particle size which is 50-200nm. The nano Mg(NH2)2 particle of the method has high purity and has excellent hydrogen absorption and desorption kinetic properties when used as the hydrogen storage materials, and therefore has very significant application value and wide application prospect in the technical field of hydrogen storage.

Description

technical field [0001] The invention relates to the field of preparation of metal amino compounds and the field of hydrogen storage technology, in particular to magnesium amides with a particle size of nanoscale and a preparation method thereof. Background technique [0002] At present, due to the depletion of traditional energy sources such as coal, oil, and natural gas, and the increasing emphasis on environmental protection issues, the development and utilization of new energy sources has become a topic of close concern around the world. Among them, hydrogen energy is one of the most promising energy sources to be widely used in the 21st century due to its high specific mass energy content and clean and pollution-free characteristics. However, the utilization of hydrogen energy involves the key step of storage, so how to store hydrogen safely and effectively has become an urgent issue to be solved. At present, the research on hydrogen storage materials mainly includes me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B21/092
Inventor 谢镭曲江兰李瑶琦李星国
Owner PEKING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com