Preparation method of biology cellulose composite membrane face-mask material

A bio-cellulose, composite membrane technology, applied in pharmaceutical formulations, cosmetic preparations, cosmetic preparations, etc., can solve the problems of mask performance impact, poor water-holding performance, inconvenient use, etc., to achieve strong moisturizing, high yield The effect of improving and high utilization rate of raw materials

Pending Publication Date: 2008-12-31
吴永辉
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the facial mask beauty products commonly used are mainly in the form of powder, mud and paste, which must be prepared according to certain requirements before use, which is extremely inconvenient to use
In recent years, the types and quantities of facial masks have been increasing, but the mainstream facial masks on the market are still mainly paper masks. This kind of facial mask is to immerse the prepared medicine in a paper carrier and apply it directly to the face when used. The mask is easy to use but its ductility is not good, and the performance of the mask is affected by a specific carrier, and the water holding capacity is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of biology cellulose composite membrane face-mask material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Selection of strains: select Gluconacetobacter xylinum CGMCC No.1.1812;

[0038] (2) Preparation of carboxymethyl cellulose seeds and liquid culture medium: In terms of weight percentage, the formula is composed as follows:

[0039] A: Glucose 2%

[0040] B: Yeast powder 0.5%

[0041] C: Tryptone 0.5%

[0042] D: Na 2 HPO 4 0.5%

[0043] E: Citric acid 0.2%

[0044] F: calcium carbonate 2%

[0045] The balance is water;

[0046] Add 0.2g / L carboxymethyl cellulose to the seed medium or liquid medium, then adjust the pH of the medium to 5, sterilize at 121°C for 20 minutes, and cool to 30°C for later use;

[0047] (3) Cultivation of seed cells: Take 1-2 loops of activated slant seeds and insert them into a liquid culture medium containing carboxymethyl cellulose under aseptic operating conditions, at 28°C on a shaker with a rotation speed of 140r / min Shake culture for 24 hours to obtain seed culture solution;

[0048] (4) Production of bio-cellulose composit...

Embodiment 2

[0051] (1) Selection of strains: select Gluconacetobacter xylinum CGMCC No. 1.2378;

[0052] (2) Preparation of carboxymethyl cellulose seeds and liquid culture medium: In terms of weight percentage, the formula is composed as follows:

[0053] A: Fructose 4%

[0054] B: Yeast powder 1%

[0055] C: Tryptone 1%

[0056] D: Na 2 HPO4 1%

[0057] E: Citric acid 0.3%

[0058] F: calcium carbonate 3%

[0059] The balance is water;

[0060] Add 0.8g / L of carboxymethylcellulose to the seed medium or liquid medium, then adjust the pH of the medium to 6, sterilize at 121°C for 25 minutes, and cool to 30°C for later use;

[0061] (3) Cultivation of seed cells: Take 1-2 loops of activated slant seeds and put them in a liquid culture medium containing carboxymethyl cellulose under aseptic operation conditions at 32°C on a shaker with a rotation speed of 180r / min Shake culture for 36 hours to obtain seed culture solution;

[0062] (4) Static liquid fermentation to produce bio-cellu...

Embodiment 3

[0065] (1) Selection of strain: select Gluconacetobacter xylinum CGMCC No. 1.1812;

[0066] (2) Preparation of carboxymethyl cellulose seeds and liquid culture medium: In terms of weight percentage, the formula is composed as follows:

[0067] A: Sucrose 3%

[0068] B: Yeast powder 0.8%

[0069] C: Tryptone 0.8%

[0070] D: Na 2 HPO 4 0.8%

[0071] E: Citric acid 0.25%

[0072] F: calcium carbonate 2.5%

[0073] The balance is water;

[0074] Add 0.5g / L of carboxymethylcellulose to the seed medium or liquid medium, then adjust the pH of the medium to 6, sterilize at 121°C for 20 minutes, and cool to 30°C for later use;

[0075] (3) Cultivation of seed cells: Take 1-2 loops of activated slant seeds, insert them into a liquid culture medium containing carboxymethyl cellulose under aseptic operation conditions, and place them on a shaker with a rotation speed of 160r / min at 30°C. Shake culture for 30 hours to obtain seed culture solution;

[0076] (4) Production of bio-ce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a preparation method for a biological cellulose composite membrane mask material. In the preparation method, water soluble macromolecular carboxymethyl cellulose is added into a culture medium, and then acetobacter xylinum is switched in for static culturing to obtain a biological cellulose composite membrane. The biological cellulose composite membrane generated after the carboxymethyl cellulose is added has good water retention property and good ventilation property, and the output and the water content of the biological cellulose composite membrane are improved to a certain extent. The biological cellulose composite membrane mask material can be obtained after the generated biological cellulose composite membrane is processed.

Description

Technical field [0001] The invention relates to a method for preparing a bio-cellulose composite film facial mask material, in particular to a method for preparing a bio-cellulose composite film facial mask material by adding carboxymethyl cellulose. Background technique [0002] Biocellulose is a kind of high molecular compound, similar to natural cellulose in structure, both are made of glucose connected by β-1,4-glycosidic bonds, and biocellulose has unique physical structure and properties, such as intricate The network structure, high crystallinity and high degree of polymerization, strong water retention and air permeability, excellent shape maintenance ability and tear resistance, no irritation, biocellulose diameter between 0.01 ~ 0.1μm, tensile strength High strength, high chemical derivatization activity, no lignin, hemicellulose, simple extraction process, high product purity. Therefore, the research and development of this new type of cellulosic material has attracted...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/73A61K8/99A61K8/02
Inventor 吴永辉马霞彭继明黄深宗曾艳武晓云
Owner 吴永辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap