Water-soluble single component aliphatic polyurethane floor coatings and manufacturing method thereof

A technology of aliphatic polyurethane and floor coatings, applied in the direction of polyurea/polyurethane coatings, coatings, latex paints, etc., can solve the problems of human health hazards, high cost, high requirements for substrates and construction environments, and achieve low VOC Discharge, good anti-settling effect

Inactive Publication Date: 2009-02-11
无锡市南雅化工有限公司
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, domestic industrial floor coatings are basically solvent-based and solvent-free epoxy floor coatings and solvent-based epoxy polyurethane floor coatings. Solvent-based varieties will have more organic solvents in the formula, and these organic solvents are used in production. And during the drying stage of construction, a large amount of volatilization int

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1, water-based one-component aliphatic polyurethane floor paint, each component and weight proportion are: (%)

[0037] Water-based one-component aliphatic polyurethane emulsion Tg≥50℃ 50

[0038] Deionized water 18

[0039] Polycarboxylate ammonium salt dispersant H-34 0.3

[0040] Polyether modified silicone defoamer F111 0.2

[0041] Solvent-free polyurethane associative thickener 3551 0.3

[0042] Glass powder treated with silane coupling agent surface ≥1250 mesh 5

[0043] Rutile titanium dioxide 24.5

[0044] Phthalocyanine blue 0.5

[0045] Water-based preservative 0.1

[0046] Propylene Glycol Methyl Ether and N-Methylpyrrolidone 1:1 Co-solvent 1

[0047] PH regulator (Shenzhen Haichuan Company AMP-95) 0.1

[0048] The production method is: put 30-50% of the water-based one-component aliphatic polyurethane emulsion, deionized water, water-based dispersant, defoamer, filler, pigment, water-based preservative, co-solvent, and matting powder into...

Embodiment 2

[0049] Embodiment 2, water-based one-component aliphatic polyurethane floor paint, each component and weight proportion are: (%)

[0050] Water-based one-component aliphatic polyurethane emulsion Tg≥50℃ 60

[0051] Deionized water 10

[0052] Water-oil amphoteric polymer hyperdispersant O5 0.4

[0053]Polyether modified silicone defoamer F121 0.3

[0054] Solvent-free polyurethane associative thickener 3551 0.35

[0055] Glass powder treated with silane coupling agent surface ≥ 1250 mesh 6

[0056] Ultrafine Barium Sulfate 4

[0057] Rutile titanium dioxide 11.1

[0058] Phthalocyanine blue 1

[0059] Water-based preservative 0.15

[0060] Propylene Glycol Methyl Ether and N-Methylpyrrolidone 1:1 Co-solvent 1.5

[0061] PH regulator (dimethylethanolamine) 0.2

[0062] Ultra-fine silica matting powder 5

[0063] Refer to Example 1 for the manufacturing method.

Embodiment 3

[0064] Embodiment 3, water-based one-component aliphatic polyurethane floor paint, each component and weight proportion are: (%)

[0065] Water-based one-component aliphatic polyurethane emulsion Tg≥50℃ 52.85

[0066] Deionized water 15

[0067] Water-oil amphoteric polymer hyperdispersant O5 0.2

[0068] Polycarboxylate ammonium salt dispersant H-5050 0.3

[0069] Polyether modified silicone defoamer F121 0.4

[0070] Solvent-free polyurethane associative thickener 3551 0.4

[0071] Glass powder treated with silane coupling agent surface ≥1250 mesh 4.5

[0072] Ultrafine Barium Sulfate 3

[0073] High Pigment Carbon Black 5

[0074] Phthalocyanine blue 15

[0075] Water-based preservative 0.2

[0076] Propylene Glycol Methyl Ether and N-Methylpyrrolidone 1:1 Co-solvent 2

[0077] PH regulator (triethanolamine) 0.15

[0078] Ultrafine silica matting powder 1

[0079] Refer to Example 1 for the manufacturing method.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a waterborne single-component aliphatic polyurethane floor coating, relating to the technical field of polyurethane coating. The waterborne single-component aliphatic polyurethane floor coating consists of waterborne single-component aliphatic polyurethane latex, deionized water, waterborne dispersant, polyether modified siloxane defoamer, no-dissolve polyurethane associative thickener, filling material, pigment, waterborne antiseptic, cosolvent compounded by propylene glycol methyl ether and N-methyl pyrrolidone according to the proportion of 1:1, pH regulator and ultra-fine SiO2 extinction powder compatibility, is a floor coating type of high performance, high performance/price ratio and friendly environment, has more excellent wearability and weathering resistance performance correspondingly to coatings such as epoxy, and the like, and can achieve and exceed the mechanical performance and chemical medium resistance of the products such as epoxy, etc.

Description

technical field [0001] The invention relates to the technical field of polyurethane coatings, in particular to a water-based one-component aliphatic polyurethane floor coating. Background technique [0002] At present, domestic industrial floor coatings are basically solvent-based and solvent-free epoxy floor coatings and solvent-based epoxy polyurethane floor coatings. Solvent-based varieties will have more organic solvents in the formula, and these organic solvents are used in production. And during the drying stage of construction, a large amount of volatilization into the atmosphere not only pollutes the environment, but also poses a huge hazard to human health; solvent-free epoxy floors generally contain a small amount of reactive diluents, and commonly used reactive diluents have different levels. Toxicity, and the overall cost of solvent-free varieties is high, and the requirements for substrates and construction environments are relatively high. [0003] Different f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D5/02C09D7/12
Inventor 许彩奎钱旭锋
Owner 无锡市南雅化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap