Method for producing wood fiber glued board and application
A technology of plywood and wood fiber, which is used in the joining of wooden veneers, impregnating wood, and impregnating wood, etc., can solve the problems of difficult to guarantee the stability of product quality, different water absorption expansion rates of wood, and difficult to evenly distribute glue, etc. The effect of low water expansion rate, stable product quality and not easy to crack
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] (1) Choose poplar branches with a diameter of 10-80mm, roll them with a machine, peel and remove the small branches, the length is controlled at 60-200cm, and tied according to the length, each 10-25kg;
[0034] (2) put it into 3% hydrogen peroxide and soak it for 2 hours, and carry out degreasing and desugaring and other treatments;
[0035] (3) It is dried, and the moisture content is controlled at 4% to 15%;
[0036] (4) Put the raw material into the spray chamber, and spray glue on it. The glue is selected from commonly used urea-formaldehyde glue, and the spray requires that all branches have glue attached to the surface;
[0037] (5) Put the glue-sprayed small-diameter wood into a cuboid mold of 200*45*80cm, cut off the rope for binding, match the long and short branches evenly, discharge the materials reasonably, and send them to the press for pressing with a pressure of 8Mpa, and then use Screws fix the cover plate and the mold, take out together with the mold,...
Embodiment 2
[0043] (1) select the fast-growing tree pole with a diameter of 10-80 mm, cut the length to 100-200 cm, peel and remove the twigs;
[0044] (2) Send it into the autoclave for cooking treatment, input steam at about 135°C into the autoclave, and control the treatment time within 3 hours;
[0045] (3) It is dried, and the moisture content is controlled at 4% to 15%;
[0046] (4) dipping treatment, using phenolic glue with a solid content of 18 to 25%, dipping for 5 to 15 minutes;
[0047] (5) Drying, the moisture content is controlled at 9% to 15%;
[0048] (6) Put it into a cuboid mold of 200*45*80cm, match the long and short branches evenly, discharge the material reasonably, send it to the press for pressing, the pressure is 7Mpa, and fix the cover plate and the mold with screws after pressing, together with the mold Take it out, and charge 60kg per mold;
[0049] (7) Send it to the curing room together with the mold, heat it to 150°C, and keep it warm for 5 hours to compl...
Embodiment 3
[0052] (1) Select eucalyptus branches with a diameter of 10-60 mm, cut the length to 100-200 cm, peel off the skin and remove the twigs, and roll them mechanically to separate the branches from the skin;
[0053] (2) Soak it in 3% hydrogen peroxide for 1 to 3 hours, and perform degreasing and sugar removal;
[0054] (3) It is dried, and the moisture content is controlled at 4% to 15%;
[0055] (4) put raw material into spray chamber, use urea-formaldehyde glue to carry out glue spraying process to it;
[0056] (5) Put the glue-sprayed small-diameter wood into a cuboid mold of 200*45*80cm, cut off the rope for binding, match the long and short branches evenly, discharge the materials reasonably, and send them to the press for pressing with a pressure of 8Mpa, and then use Screws fix the cover plate and the mold, take out together with the mold, and charge 50kg for each mold;
[0057] (6) Store for 72 hours, remove the mold after the glue is completely cured, and store for ano...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
density | aaaaa | aaaaa |
density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com