High solid content latent curing polyurethane acroleic acid hybrid emulsion

A polyurethane acrylic, high solid content technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of inconvenient application and construction of wood coatings, increasing the cost of emulsions, and decreasing the storage stability of emulsions.

Inactive Publication Date: 2011-06-08
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cross-linking modification includes: based on Michael reaction, aziridine or carboimide / carboxylic acid, siloxane hydrolysis condensation, acetoacetyl group / polyamine, active carbonyl group / hydrazide (ketohydrazine) and cyclic carbonate / amine However, for PUA systems, the storage stability of the emulsion will be reduced, the cost of the emulsion will be increased, or the volatile organic compound content of the emulsion will be increased, or the application of two-component packaging will bring harm to the application and construction of wood coatings. inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High solid content latent curing polyurethane acroleic acid hybrid emulsion
  • High solid content latent curing polyurethane acroleic acid hybrid emulsion
  • High solid content latent curing polyurethane acroleic acid hybrid emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The latent curing polyurethane acrylic hybrid emulsion with high solid content is used, and its formulation components are listed in Table 2.

[0052] Table 2 High solid content latent curing polyurethane acrylic hybrid emulsion

[0053]

[0054] Under the protection of dry nitrogen, the dehydrated polyether glycol N210, N220, BDO and DMPA were added to a 1000ml four-necked flask equipped with a thermometer, a stirring device and a reflux condenser, and a small amount of N-methylpyrrolidone was added to raise the temperature. Stir at 60°C, start adding TDI dropwise when the reaction system becomes transparent, and finish dropping in 1 hour. React at 70°C-80°C for 3-5 hours, and use n-butylamine titration method to determine the end point of the reaction. After reaching the end point, cool down to 40°C, add triethylamine to neutralize, add acetone to dilute, emulsify in normal temperature water, and use ethylenediamine to extend the chain to obtain an aqueous polyure...

Embodiment 2

[0057] Using the high-solid-content latent-curing polyurethane-acrylic hybrid emulsion prepared in Example 1, the wood coating formulation was prepared as shown in Table 3.

[0058] Table 3 Waterborne Wood Coating Formulation

[0059] serial number

[0060] The preparation method is as follows: firstly add the No. 2-9 raw materials into the stirring tank, disperse with a high-speed disperser for 10-30 minutes, then slowly add the PUA emulsion into the stirring tank, stir at a medium speed for 30-60 minutes, use AMP-95 Adjust the pH value of the paint, and when the pH value is greater than 7.0, filter, discharge and pack. Properties of the prepared wood coating: Appearance: Milky white slightly transparent liquid without mechanical impurities; PH=7-9; solid content 35-42%, viscosity 30-200cps. Wood coating film performance: Pencil hardness of coating film: H; Water resistance: no obvious change after immersion in water for 96 hours; Adhesion: Grade 1; Impact resistan...

example 3

[0062] Polyester diol and aliphatic diisocyanate were used to prepare latently cured polyurethane-acrylic hybrid emulsion with high solid content. The raw materials used are listed in Table 4.

[0063] Table 4 High solid content latent curing polyurethane acrylic hybrid emulsion

[0064]

[0065]

[0066] Under the protection of dry nitrogen, the dehydrated polyether glycol N210, T1136, BDO and DMPA were added to a 1000ml four-necked flask equipped with a thermometer, a stirring device and a reflux condenser, a small amount of N-methylpyrrolidone was added, and the temperature was raised Stir at 60°C, start to add IPDI dropwise when the reaction system becomes transparent, finish dropping in 1 hour, then add catalyst, react at 70°C-80°C for 3-5 hours, use n-butylamine titration method to judge the reaction end point. After reaching the end point, cool down to 40°C, add triethylamine to neutralize, add acetone to dilute, emulsify in normal temperature water, and use ethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a high solid content latent cured polyurethane acrylic acid heterozygous latex and an application thereof. The preparation method comprises the following steps: pre-polymerizing polyester polyalcohol, hydrophilic chain extender and diisocyanate monomer to obtain the polyurethane prepolymer containing a hydrophilic group (carboxyl or sulfo group) anda terminal NCO group; then, neutralizing the polymer into salt and dispersing the salt in water to prepare the polyurethane water dispersoid; finally, using the dispersoid as macro molecular emulsifying agent and reactant to emulsify and disperse the acrylic ester monomer, initiating the polymerization by heating, dropping initiator to perform the latex polymerization, and regulating the pH of the latex by adding a latent curing agent to obtain the high solid content latent cured polyurethane acrylic acid heterozygous latex. The high solid content latent cured polyurethane acrylic acid heterozygous latex has a solid content of above 45%; the storage of the high solid content latent cured polyurethane acrylic acid heterozygous latex is stable; and high hardness film coating can be formed at the room temperature. Compared with acrylic acid latex and polyurethane latex, the high solid content latent cured polyurethane acrylic acid heterozygous latex has better film forming performance, water resistance, alcohol resistance, pollution resistance, dry / wet cleaning resistance and chemical solvent resistance, as well as high hardness.

Description

technical field [0001] The present invention relates to high solid content latent curing polyurethane acrylic hybrid emulsions. technical background [0002] With the emergence of resource and energy crises and the continuous enhancement of people's awareness of environment and health, water-based wood coatings are increasingly valued. Existing water-based wood coatings include wood coatings such as polyacrylate (PA) emulsions, polyurethane (PU) aqueous dispersions and acrylic polyurethane composite (PUA) emulsions. PU emulsion coating has excellent solvent resistance, abrasion resistance, scratch resistance, good flexibility and elasticity, etc., but it is not as good in stability, self-thickening, solid content, gloss, cost, etc. Satisfactory; PA emulsion coating has the advantages of high hardness, good weather resistance and appearance, and relatively low cost, but poor flexibility, abrasion resistance, and chemical resistance. The PUA emulsion combines the two emulsio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/67C08G18/10C08G18/40C08J3/03C09D175/04
Inventor 瞿金清黎永津黄洪陈焕钦
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com