Vibration-damping heat-insulation paint and preparation method thereof

A heat-insulating coating and soft filler technology, applied in anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve problems such as poor heat insulation effect and cumbersome construction, achieve strong adhesion and durability, protect the environment and human body, and excellent The effect of weather resistance

Active Publication Date: 2010-05-19
WUXI HUHUANG PAINT
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional thermal insulation coatings are mainly used for energy saving and consumption reduction purposes, such as polystyrene particle mortar type, EPS, XPS board type, etc. for external thermal insulation systems. The construction is cumbersome and the thermal insulation effect is poor. Thick external thermal insulation coating composed of hollow microsphere filler and chemical reflective thermal insulation powder, these are only used for external thermal insulation system of external wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A shock-absorbing and heat-insulating coating, comprising the following components in mass percent:

[0052] Chlorine ether resin 10.5%,

[0053] Binder 5%,

[0054] Melamine Urea Copolymer Resin 4%,

[0055] Environmental solvent 20%,

[0056] Soft Filler I 15.5%,

[0057] Soft Filler II 14%,

[0058] Soft Filler III 19%,

[0059] Plasticizer 5%,

[0060] Titanium dioxide 2%,

[0061] Cenospheres 5%.

[0062] in,

[0063] Described soft filler I is melamine.

[0064] The soft filler II is pentaerythritol.

[0065] The soft filler III is ammonium polyphosphate.

[0066] The content of the chloroether resin is 40% (w / w), and the chloroether resin is prepared according to the following mass percentages: 30% xylene, 30% environmentally friendly solvent, and 40% chloroether resin MP25.

[0067] The content of the binder is 20% (w / w), and the binder is prepared according to the following components in mass percentage: 40% xylene, 40% environmentally friendly solven...

Embodiment 2

[0078] A shock-absorbing and heat-insulating coating, comprising the following components in mass percent:

[0079] Chlorother resin 9.9%,

[0080] Binder 5%,

[0081] Melamine Urea Copolymer Resin 3.5%,

[0082] Environmentally friendly solvent 18%,

[0083] Soft Filler I 14.5%,

[0084] Soft Filler II 15%,

[0085] Soft filler III 20%,

[0086] Plasticizer 5.8%,

[0087] Titanium dioxide 2.3%,

[0088] Cenospheres 6%;

[0089] in,

[0090] Described soft filler I is dicyandiamide.

[0091] The soft filler II is tripentaerythritol.

[0092] The soft filler III is ammonium hydrogen phosphate.

[0093] The content of the chloroether resin is 40% (w / w), and the chloroether resin is prepared according to the following mass percentages: 30% xylene, 30% environmentally friendly solvent, and 40% chloroether resin MP25.

[0094] The content of the binder is 20% (w / w), and the binder is prepared according to the following components in mass percentage: 40% xylene, 40% envi...

Embodiment 3

[0105] A shock-absorbing and heat-insulating coating, comprising the following components in mass percent:

[0106] Chlorother resin 11.5%,

[0107] Binder 6%,

[0108] Melamine Urea Copolymer Resin 4.5%,

[0109] Environmental solvent 21%,

[0110] Soft Filler I 16.5%,

[0111] Soft Filler II 13%,

[0112] Soft Filler III 18%,

[0113] Plasticizer 3.8%,

[0114] Titanium dioxide 1.7%,

[0115] Cenospheres 4%.

[0116] in,

[0117] The soft filler I is a mixture of dicyandiamide and ammonium phosphate in a mass ratio of 1:2.

[0118] The soft filler II is a mixture of starch and tripentaerythritol in a mass ratio of 1:1.

[0119] The soft filler III is a mixture of ammonium polyphosphate and ammonium hydrogen phosphate in a mass ratio of 1:1.

[0120] The content of the chloroether resin is 40% (w / w), and the chloroether resin is prepared according to the following components in mass percentage: xylene 30%, environmental solvent 30%, and chloroether resin MP2540%. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vibration-damping heat-insulation paint which comprises the following components by mass percent: 9.5-11.5% of chlorine ether resin, 5-6% of adhesive, 3.5-4.5% of melamine urea copolymerization resin, 18-21% of environment-friendly solvent, 14.5-16.5% of soft filler I, 13-15% of soft filler II, 18-20% of soft filler III, 3.8-5.8% of plasticizer, 1.5-2.3% of titanium pigment and 4-6% of hollow micro-bead. The invention also discloses a preparation method of the vibration-damping heat-insulation paint. The high-efficiency vibration-damping heat-insulation paint can be coated on various substrates, has advantages in various aspects such as heat insulation, heat preservation, fire prevention, water prevention, crack prevention, noise prevention, weather resistance, acid / alkali resistance, salt-fog resistance, corrosion resistance, vibration damping, durability and the like, is suitable for thermal protection and vibration damping at the external surfaces of spaceflight instruments and data recording instruments of aerospacecrafts and can be used for damping the impact friction and the like of containers and the like.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to a shock-absorbing and heat-insulating coating and a preparation method thereof. Background technique [0002] With the rapid development of the national economy, the application of special coatings has been continuously developed, and various structures, facilities, equipment materials and other surface engineering have put forward higher requirements for surface coatings. Therefore, high-performance special coatings have become the research object of major companies. Thermal insulation and energy-saving coatings are currently an active research field. [0003] Traditional thermal insulation coatings are mainly used for energy saving and consumption reduction purposes, such as polystyrene particle mortar type, EPS, XPS board type, etc. for external thermal insulation systems. The construction is cumbersome and the thermal insulation effect is poor. The thick external...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/06C09D5/00C09D5/18C09D5/08
Inventor 胡胜初牛清平周美君
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com