Continuous manufacturing method of steel mesh/phenol-urea-formaldehyde foam thermal insulating decoration board

A technology for thermal insulation decorative panels and manufacturing methods, applied to flat products, building structures, covering/lining, etc., can solve the problems of temperature difference between the thermal insulation layer and the decorative layer, long cycle, dry shrinkage deformation, etc., and achieve low construction and installation costs , construction and installation is convenient, the effect of short curing cycle

Inactive Publication Date: 2010-06-09
刘威
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The above-mentioned phenolic composite board, if used for external wall insulation, must be fixed with vertical wall keels to meet the requirements of the "Unified Standard for Construction Quality Acceptance of Construction Engineering" (GB50300), the construction and installation are cumbersome, the cycle is long, and the cost is large; There is no anti-crack reinforcement materi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous manufacturing method of steel mesh/phenol-urea-formaldehyde foam thermal insulating decoration board
  • Continuous manufacturing method of steel mesh/phenol-urea-formaldehyde foam thermal insulating decoration board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Material A: parts by weight

[0062] Phenolic resin: 100

[0063] Surfactant: 5

[0064] Blowing agent (141b): 5

[0065] Material B: curing agent 10

[0066] Surface layer: 0.1mm color aluminum plate on the upper layer,

[0067] Lower layer Phenolic glued paper

[0068] Steel mesh: eye size: 20mm×20mm, steel wire diameter: 1mm.

[0069] After the two components of A and B are prepared according to the requirements in proportion, they are pumped to the high-speed mixing head of the reaction filling machine at constant temperature and in proportion, and the foaming stock solution is sprayed on the middle steel mesh and On the lower layer, enter the laminator to complete foaming and curing, and the internal temperature of the laminator is set to 55°C. It takes 8 minutes for the foaming stock solution to be delivered from the mixing head to the decorative plate.

[0070] The performance of the prepared steel mesh / phenolic foam insulation decorative board:

[0071] ...

Embodiment 2

[0078] Material A: parts by weight

[0079] Phenolic-urea-formaldehyde resin: 100

[0080] Surfactant: 5

[0081] Blowing agent (141b): 5

[0082] Material B: curing agent: 10

[0083] Others are the same as Example 1, carried out according to the process of Example 1, and the properties of the prepared steel mesh / phenolic-urea-formaldehyde resin foam insulation decorative board are as follows.

[0084] (1) Combustion performance

[0085]

[0086] (2) Wind pressure test negative pressure 4500Pa, no cracks; positive pressure 5000Pa, no cracks;

[0087] (3) Density 64.5kg / m 3 , Compressive strength 157KPa.

[0088] (4) During the production process, the entire production line has no obvious formaldehyde smell, which is caused by the reaction between the urea added in the phenolic-urea-formaldehyde resin and the formaldehyde released during the curing process.

[0089] Compared with Example 1, the oxygen index is slightly lower, but it reaches the "GB8264-1997" B1 stand...

Embodiment 3

[0091] According to example 2 formula, only in A material, increase 3% filler, foaming process is the same as example 1. The density of the decorative board is 67kg / m 3 , the oxygen index reaches 43%, the compressive strength is improved to 180KPa, other properties are basically unchanged, the elasticity is improved to a certain extent compared with example 1 and example 2, and the production workshop is tasteless.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a continuous manufacturing method of steel mesh/phenol-urea-formaldehyde foam thermal insulating decoration board. In the method, 7 raw materials: phenol-urea-formaldehyde resin, firming agent, surface active agent, foaming agent, stuffing, accessory ingredient and steel mesh are provided, a steel mesh flattening and positioning device is additionally provided.Through the optimization design of the steel mesh flattening and positioning device and phenol-urea-formaldehyde resin foaming and surface course compound technology, the continuously produced steel mesh/phenol-urea-formaldehyde foam thermal insulating decoration board is applied to outer wall for heat preservation and can meet national requirements on heat insulation and fire prevention, features high production efficiency, low construction and installation cost, short construction period, wide market and obvious economic and social benefits.

Description

Technical field [0001] The invention relates to the technical field of continuous molding of foamed plastic sandwich structures, and more specifically relates to the production technology of continuous manufacturing of steel mesh / phenol-urea-formaldehyde foam insulation and decorative boards. [0002] The steel mesh / phenol-urea-formaldehyde foam thermal insulation decorative panel of the present invention uses phenol-urea-formaldehyde foam plastic as the core material, aluminum, steel plate or glass fiber reinforced plastic thin plate as the outer decorative panel, and a sandwich structure reinforced by steel mesh in the middle of the foam plate. It is characterized by (1) continuous production; (2) foam molding at room temperature or slightly higher temperature (20-60°C); (3) short curing cycle and high efficiency; (4) due to the existence of the core steel mesh, The four corners of the decorative board can be anchored on the base wall with expansion bolts. If the combinatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04F13/075E04F13/077C08L61/34C08K13/04C08J9/14B29C44/32B29C44/34B29C44/60C08K3/32C08K5/42C08K7/22C08K5/053B29L7/00
Inventor 刘威周春华楚楠
Owner 刘威
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap