An environment-friendly, magnesium alloy technology, applied in the direction of molds, cores, mold components, etc., can solve problems such as poor fluidity, poor molding, etc., to reduce poor fluidity, improve workpiece molding quality, and excellent flow properties Effect
Inactive Publication Date: 2010-12-01
QIDONG YUSHIRO CHEMICAL INDUSTRY CO LTD +1
View PDF6 Cites 45 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, most of these parts are thin, so molding problems such as poor fluidity are prone to occur during casting
The magnesium alloy release agents currently on the market are generally water-soluble emulsion type, but when processing thin workpieces such as computer frames, poor molding often occurs, and cannot fully meet the customer's requirements for high-quality processing performance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] Mix and stir the following weight percentages to obtain the product:
[0044] Rust and corrosion inhibitor 1~10% (examples 5%, 15%, 30%)
[0045] Preservative 0.2~2% (example 0.2%, 1%, 2%)
[0046] Surfactant 1~10% (example 1%, 5%, 10%)
[0047] Water 30-80% (examples 33%, 55%, 78%).
[0048] The sum of the above components is 100%.
[0049] Silicone is dimethyl silicone oil (or diethyl silicone oil, methyl phenyl silicone oil, ammonia hydrocarbon-based silicone oil, hydroxyalkyl cinnamon oil, epoxy hydrocarbon-based silicone oil, carboxyl hydrocarbon-based silicone oil, polyether silicone oil, long-chain alkyl cinnamon oil, long Any one of alkoxy silicone oil, mercapto hydrocarbon-based silicone oil, fluorocarbon-based silicone oil, and composite modified...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an environmental-friendly magnesium alloy mold releasing agent which comprises organic silicon, a synthetic macromolecular compound, grease, an antirust corrosion inhibitor, a preservative, a surface active agent and water. The environmental-friendly magnesium alloy mold releasing agent has excellent flowing property, thus the generation of poor flowing property can be greatly reduced. The product has excellent adsorbing performance, thus the lubricating mold releasing performance of the product can be obviously improved; the product has excellent heat insulating performance, thus the molding quality of a workpiece can be obviously improved; meanwhile, the environmental-friendly magnesium alloy compression-casting mold releasing agent has environmental protection and high performance.
Description
Technical field: [0001] The invention relates to a mold release agent used in a magnesium alloy die casting process. Background technique: [0002] Magnesium alloys are mostly used in electronic equipment due to their light weight (the specific gravity is about 2 / 3 that of aluminum and 1 / 4 that of iron), strong electromagnetic interference resistance, good heat dissipation, large elastic modulus, and good shock absorption. (Such as computers, digital cameras, mobile phones, etc.) on the frame. Since the heat capacity of magnesium alloy is only 60% of that of aluminum alloy, it solidifies faster and is easy to form a cold barrier, so it needs to be well formed in a short cooling time. In addition, most of these parts are thin parts, so molding problems such as poor fluidity are likely to occur during casting. Magnesium alloy mold release agents currently on the market are generally water-soluble emulsion type, but when processing thin workpieces such as computer frames, poor mol...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).