A multi-purpose, industrial technology, applied in the direction of adhesive types, adhesives, unsaturated alcohol copolymer adhesives, etc., can solve problems such as poor water resistance and moisture resistance, creep, and decrease in bonding strength. High effect of deformation and moisture resistance

Active Publication Date: 2011-03-09
山东韩师傅新材料有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantages are poor water resistance and moisture resistance, easy to absorb moisture in humid air, creep phenomenon will occur when used at high temperature, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] formula:

[0027] Proportion name

[0028] 3% polyvinyl alcohol (model 1788; 0588)

[0029] 20% vinyl acetate

[0030] 0.1% ammonium persulfate (initiator)

[0031] 0.2% OP-10,

[0032] 0.05% dodecyl

[0033] 0.7% butyl acrylate

[0034] 8% VAE emulsion

[0035] 6% Dioctyl Fat

[0036] 6% dibutyl

[0037] 0.2% acrylic acid

[0038] 0.2% methanol

[0039] 0.1% sodium acetate

[0040] 0.01% water-based defoamer

[0041] 0.03% ethylene glycol

[0042] Manufacturing process:

[0043] (1) Add about 450 kilograms of distilled water to it. If stirring, slowly add polyvinyl alcohol (about 15 kilograms for 1788, about 25 kilograms for 0588) in order.

[0044] (2) Put in sodium acetate and water-based defoamer, start to heat the reactor to 90 degrees Celsius, when the temperature is stable and maintain this temperature for 30 minutes, then drop to 70 degrees Celsius, add dodecyl and OP-10, Let it be fully emulsified, put in methanol after 10 minutes, and at the same time put in the initiator ammonium ...

Embodiment 2

[0049] formula:

[0050] Proportion name

[0051] 4% polyvinyl alcohol (model 1788; 0588)

[0052] 25% vinyl acetate

[0053] 0.2% ammonium persulfate (initiator)

[0054] 0.3% OP-10,

[0055] 0.1% dodecyl

[0056] 0.8% butyl acrylate

[0057] 10% VAE emulsion

[0058] 8% dioctyl ester

[0059] 8% dibutyl

[0060] 0.3% acrylic acid

[0061] 0.3% methanol

[0062] 0.15% sodium acetate

[0063] 0.02% water-based defoamer

[0064] 0.05% ethylene glycol

[0065] Manufacturing process:

[0066] (1) Add about 450 kilograms of distilled water to it. If stirring, slowly add polyvinyl alcohol (about 15 kilograms for 1788, about 25 kilograms for 0588) in order.

[0067] (2) Put in sodium acetate and water-based defoamer, start to heat the reactor to 90 degrees Celsius, when the temperature is stable and maintain this temperature for 30 minutes, then drop to 70 degrees Celsius, add dodecyl and OP-10, Let it be fully emulsified, put in methanol after 10 minutes, and at the same time put in the initiator ammoni...

Embodiment 3

[0072] formula:

[0073] Proportion name

[0074] 5% (3-5%) polyvinyl alcohol (model 1788; 0588)

[0075] 30% (20-30%) vinyl acetate

[0076] 0.3% (0.1-0.3%) ammonium persulfate (initiator)

[0077] 0.4% (0.2-0.4%) OP-10,

[0078] 0.15% (0.05-0.15%) dodecyl

[0079] 0.9% (0.7-0.9%) butyl acrylate

[0080] 12% (8-12%) VAE emulsion

[0081] 10% (6-10%) dioctyl ester

[0082] 10% (6-10%) dibutyl ester

[0083] 0.4% (0.2-0.4%) acrylic acid

[0084] 0.4% (0.2-0.4%) methanol

[0085] 0.2% (0.1-0.2%) sodium acetate

[0086] 0.03% (0.01-0.03%) water-based defoamer

[0087] 0.07% (0.03-0.07%) ethylene glycol

[0088] Manufacturing process:

[0089] (1) Add about 450 kilograms of distilled water to it. If stirring, slowly add polyvinyl alcohol (about 15 kilograms for 1788, about 25 kilograms for 0588) in order.

[0090] (2) Put in sodium acetate and water-based defoamer, start to heat the reactor to 90 degrees Celsius, when the temperature is stable and maintain this temperature for 30 minutes, then drop to 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a multipurpose environmental protection adhesive for industrial use. The invention is obtained by polymerization reaction of methanol, VAE latex, dioctyl phthalate, butyl acrylate, sodium dodecyl sulfate, plasticizer, vinyl acetate (VAC), polyvinyl alcohol, acrylic acid and OP-10. The invention has the advantages of water resistance, waterlogging tolerance, notoxicity, non-formaldehyde performance, scarce deformation under wet or hot condition and antifreeze function, thus is necessary for domestic fitments.

Description

Technical field [0001] The invention relates to an industrial multi-purpose environmental protection adhesive. Background technique [0002] Industrial multi-purpose environmentally friendly adhesive is referred to as PVAC emulsion chemical name polyvinyl acetate adhesive. It is widely used in printing and binding and furniture manufacturing. It is used as a binder for paper, wood, cloth, leather, ceramics, etc. It can also be used as phenolic resin. , Urine formaldehyde resin and other adhesive modifiers, used in the manufacture of polyvinyl acetate latex paint. [0003] The traditional industrial multi-purpose environmental protection adhesive is a water-soluble adhesive, which is composed of vinyl acetate (VAC) monomer in the initiator (polyvinyl alcohol, alkyl polyoxyethylene ether, starch, acetic acid, formaldehyde, water). A thermoplastic adhesive made by polymerization reaction. Its shortcomings are poor water resistance and moisture resistance, easy to absorb moisture in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J131/04C09J123/08C09J129/04
Inventor 韩志龙
Owner 山东韩师傅新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap