Base station antenna polyvinyl chloride (PVC) profile housing with surface self-cleaning function and preparation method thereof

A technology of base station antennas and profiled materials, which is applied in the direction of the radiation unit cover, etc., can solve the problems of transmission signal influence, high total surface energy, and easy dust adhesion, etc., and achieve low preparation costs, good UV resistance, and reduced dust adhesion. Effect

Active Publication Date: 2011-09-07
NANJING TECH UNIV +1
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PVC is a polar material. Because its structure contains polar chlorine atoms, its total surface energy is high, especially the non-polar part of the surface energy is low, which eventually makes the surface of the material easy to be hydrophilic.
The PVC antenna cover is used outdoors for a long time, and a large amount of dust in the air is easy to adhere to the surface of the cover, which will affect the transmission signal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Base station antenna polyvinyl chloride (PVC) profile housing with surface self-cleaning function and preparation method thereof
  • Base station antenna polyvinyl chloride (PVC) profile housing with surface self-cleaning function and preparation method thereof
  • Base station antenna polyvinyl chloride (PVC) profile housing with surface self-cleaning function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Raw material formula: 100 parts of PVC, 2 parts of organic tin stabilizer, 6 parts of polyacrylate toughening agent, 2 parts of polyacrylate processing aid, 10 parts of rutile titanium dioxide, 5 parts of calcium carbonate, and 0.5 part of silicone oil.

[0028] Preparation:

[0029] High-speed powder mixing: put PVC resin and organotin stabilizer into the high-speed mixer, when the temperature rises to 80°C, put in toughening agent, processing aid and calcium carbonate, and when the temperature rises to 92°C, put in rutile titanium dioxide and hydrophobic Modifier silicone oil; when the temperature continues to rise to 115 ° C, quickly discharge the material into another mixer with jacketed water cooling, and the mixture continues to mix in the mixer with jacketed water cooling, when the temperature drops to 40 ℃ can be discharged to the silo;

[0030] Twin-screw extrusion: Extrude the material in the silo to obtain a self-cleaning PVC profile cover for the base stati...

Embodiment 2

[0032] Raw material formula: 100 parts of PVC, 2.2 parts of organotin stabilizer, 6.5 parts of polyacrylate toughening agent, 2.5 parts of polyacrylate processing aid, 10 parts of rutile titanium dioxide, 5 parts of calcium carbonate, 1 part of calcium stearate , 0.5 part of polyethylene wax.

[0033] Preparation:

[0034] High-speed powder mixing: put PVC resin and organotin stabilizer into the high-speed mixer, when the temperature rises to 80°C, put in toughening agent, processing aid and calcium carbonate, and when the temperature rises to 92°C, put in rutile titanium dioxide and hydrophobic Modifier calcium stearate and polyethylene wax; when the temperature continues to rise to 115°C, quickly discharge the material into another mixer with jacket water cooling, and the mixture is in the mixer with jacket water cooling Continue to mix, when the temperature drops to 40°C, it can discharge to the silo;

[0035] Twin-screw extrusion: Extrude the material in the silo to obta...

Embodiment 3

[0037] Raw material formula: 100 parts of PVC, 1.5 parts of organotin stabilizer, 6 parts of polyacrylate toughening agent, 2 parts of polyacrylate processing aid, 10 parts of rutile titanium dioxide, 5 parts of calcium carbonate, organic fluoride Dynamar TM 1 copy of PPA.

[0038] Preparation:

[0039] High-speed powder mixing: put PVC resin and organotin stabilizer into the high-speed mixer, when the temperature rises to 80°C, put in toughening agent, processing aid and calcium carbonate, and when the temperature rises to 92°C, put in rutile titanium dioxide and hydrophobic Modifier organic fluoride; when the temperature continues to rise to 115°C, quickly discharge the material into another mixer with jacketed water cooling, and the mixture continues to mix in the mixer with jacketed water cooling, when the temperature The material can be discharged to the silo when the temperature drops to 40°C;

[0040] Twin-screw extrusion: Extrude the material in the silo to obtain a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a base station antenna polyvinyl chloride (PVC) profile housing with a surface self-cleaning function. The mechanical properties of the PVC profile housing are improved, the ultraviolet light resistance is greatly increased; and moreover, the non-polarity of the surface energy of the profile is significantly increased, thus the surface water contact angle of the profile is significantly increased, the hydrophobicity is increased and the surface self-cleaning function can be achieved. The base station antenna PVC profile housing with the surface self-cleaning function is prepared from the following raw materials in parts by weight: 100 parts of PVC, 1-3 parts of organotin stabilizer, 5-10 parts of polyacrylate toughening agent, 1-3 parts of polyacrylate processing aid, 5-10 parts of titanium dioxide, 0-5 parts of calcium carbonate, 3-5 parts of calcium stearate, 0.3-1 part of polyethylene wax, 0.2-1.2 parts of silicone oil, 0.3-1.2 parts of fluorosilicone oil and 0.2-1 part of organic fluoride.

Description

technical field [0001] The invention relates to a profiled material cover and a preparation method thereof, more specifically to a PVC profiled material cover for a base station antenna with surface self-cleaning function and a preparation method thereof. Background technique [0002] With the rapid development of the mobile communication industry, mobile phones provide convenience and speed for people's work and life more and more. The base station antenna is an important part of the mobile communication wireless access system. People have higher and higher requirements for call quality, and electronic components that transmit special radio frequency signals play a very important role. At the same time, the antenna cover of the base station also makes a great contribution to protecting the electronic components and making them work normally. Since the microwave communication antenna is placed outdoors for a long time, it is not only required that the outer cover has a low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/10C08K3/22C08K3/26C08K5/57C08K5/098H01Q1/42B29C47/92B29C48/92
CPCB29C48/875B29C48/92B29C2948/92704B29C2948/9259B29C2948/92828B29C2948/92885B29C2948/92895B29C2948/92933B29C48/40
Inventor 张军成静张振陈双俊徐国忠陈浩叶枫韬
Owner NANJING TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com