Convex rib winding reinforced polyvinyl chloride hose for sand transportation and preparation method thereof

A polyvinyl chloride, winding reinforced technology, applied in the direction of hoses, pipes, mechanical equipment, etc., can solve the problems of inconvenient observation of material flow, poor corrosion resistance and wear resistance, poor connection and use flexibility, etc. The effect of high thermal and light stabilization efficiency, good weather resistance, and easy troubleshooting

Active Publication Date: 2011-09-21
漯河科莱堡科技有限公司
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The connection and use flexibility of steel pipes are poor, the corrosion resistance and wear resistance are poor, and the service life is relatively short
[0004] 2. The transparency of the rubber tube is poor, it is not convenient to observe the flow of materials and deal with related faults, and the processing cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Example 1: A reinforced polyvinyl chloride hose wound with ribs for sand transportation and its preparation method

[0045] The polyvinyl chloride hose reinforced by winding ribs for sand transportation in the present invention is prepared from 60% soft polyvinyl chloride mixture and 40% hard polyvinyl chloride mixture;

[0046] The composition of the polyvinyl chloride compound soft material is: 50 parts of suspension method polyvinyl chloride SPVC (polymerization degree is 1200-1400), 50 parts of high molecular weight polyvinyl chloride HMWPVC (polymerization degree is 2000-3000), tricitric acid Butyl ATBC 60 parts, MBS resin 15 parts, chlorinated polyethylene CPE 12 parts, acrylate copolymer ACR 11 parts, mercaptan methyl tin 6 parts, calcium zinc composite stabilizer 3 parts, rare earth stabilizer 3 parts, hard 3 parts of fatty acid, 5 parts of titanium dioxide, 1.2 parts of light stabilizer UV-531 and 10 parts of calcium carbonate;

[0047] The composition of the ...

Embodiment 2

[0053] Embodiment two: basically the same as embodiment one, the difference is:

[0054] The polyvinyl chloride hose reinforced by twisting ribs for sand transportation in the present invention is prepared from 55% soft polyvinyl chloride mixture and 45% hard polyvinyl chloride mixture;

[0055] The composition of the polyvinyl chloride compound soft material is: 30 parts of suspension polyvinyl chloride SPVC (polymerization degree 1200-1400), 30 parts of high molecular weight polyvinyl chloride HMWPVC (polymerization degree 2000-3000), sebacic acid 30 parts of dioctyl ester DOS, 5 parts of styrene-butadiene-styrene copolymer SBS, 3 parts of polyolefin elastomer POE, 2 parts of acrylate copolymer ACR, 2 parts of organotin maleate, calcium-zinc composite stabilizer 1 part of rare earth stabilizer, 0.5 part of polyethylene wax, 0.5 part of chromium oxide green, 0.2 part of light stabilizer UV-9 and 1 part of talcum powder;

[0056] The composition of the polyvinyl chloride mixt...

Embodiment 3

[0061] Embodiment three: basically the same as embodiment one, the difference is:

[0062] The present invention uses ribbed winding reinforced polyvinyl chloride hose for sand transportation, and the ribbed reinforced polyvinyl chloride hose is prepared from 58% of soft polyvinyl chloride mixture and 42% of hard polyvinyl chloride mixture;

[0063] The composition of the polyvinyl chloride compound soft material is: 70 parts of suspension polyvinyl chloride SPVC (polymerization degree is 1200-1400), 70 parts of high molecular weight polyvinyl chloride HMWPVC (polymerization degree is 2000-3000), phthalate Dioctyl formate DOP 90 parts, acrylonitrile-butadiene-styrene terpolymer ABS 25 parts, EPDM EPDM 20 parts, acrylate copolymer ACR 20 parts, dibutyltin dilaurate 10 parts, 6 parts of calcium zinc composite stabilizer, 5 parts of rare earth stabilizer, 5 parts of polyethylene oxide, 10 parts of iron oxide yellow, 2 parts of light stabilizer UV-101 and 20 parts of calcium carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Wall thicknessaaaaaaaaaa
Outer diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a convex rib winding reinforced polyvinyl chloride hose for sand transportation and a preparation method thereof. The convex rib winding reinforced polyvinyl chloride hose for sand transportation is prepared from a polyvinyl chloride soft mixture and a polyvinyl chloride hard mixture, wherein the polyvinyl chloride soft mixture is prepared from suspension-process polyvinylchloride, high-molecular-weight polyvinyl chloride, plasticizer, anti-shock modifier, toughener, processing modifier, organotin stabilizer, calcium-zinc composite stabilizer, rare-earth stabilizer, lubricant, light stabilizer, filler and other assistants; and the polyvinyl chloride hard mixture is prepared from suspension-process polyvinyl chloride, chlorinated polyvinyl chloride, anti-shock modifier, toughener, processing modifier, organotin stabilizer, calcium-zinc composite stabilizer, lubricant, light stabilizer, filler and other assistants. The product prepared by the technical scheme ofthe invention has the advantages of favorable wear resistance, heat resistance, freezing resistance, fatigue resistance, bending resistance, energy saving and low cost, and is a new product expected in sand transportation industry.

Description

technical field [0001] The invention relates to a pipe material for sand transportation and a preparation method thereof, in particular to a rib-wound reinforced polyvinyl chloride hose for sand transportation and a preparation method thereof. Background technique [0002] At present, the sand conveying pipes are mainly steel pipes and rubber pipes, and the steel pipes and rubber pipes are used for sand conveying. The main defects in their performance are: [0003] 1. The connection and use flexibility of the steel pipe is poor, the corrosion resistance and wear resistance are poor, and the service life is relatively short. [0004] 2. The transparency of the rubber tube is poor, it is not convenient to observe the flow of materials and deal with related faults, and the processing cost is relatively high. [0005] In view of the current further requirements on the wear resistance, transparency and processing cost of sand conveying pipes, it is necessary to further develop s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L27/24C08K13/02F16L11/08F16L11/10B29C47/92B29C48/92
CPCB29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895B29C2948/92904B29C2948/92923B29C2948/92933
Inventor 李拴成李蕾李崇勋张向前
Owner 漯河科莱堡科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com