Flame-retardant double-component adhesive used for color antiskid pavement layer of tunnel

A pavement layer, flame-retardant technology, applied in the field of adhesive preparation, can solve the problem of easy flow of asphalt, and achieve the effects of increasing flame retardancy, improving ignition point, and delaying burning fire.

Active Publication Date: 2012-12-05
SHANXI PROVINCIAL RES INST OF COMM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, asphalt is easy to flow at high temperature, and the detachment of flame retardants and asphaltene poses new problems for the flame retardancy of asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1. Component A: Take 80g of epoxy resin E51, 20g of epoxy resin E44 and 10g of 501 epoxy reactive diluent after heating in a water bath at 100°C for 30 minutes, put them into the reaction kettle, disperse and mix at 25°C, and stir at a speed of 500r / min; After mixing evenly, 120g aluminum hydroxide, 40g magnesium hydroxide, 15g ammonium polyphosphate with a degree of polymerization greater than 1000, 10g composite flame retardant fr-106, 3g coupling agent KH560, 4g plasticizer DOP, 1.5g Add polysulfide rubber LP-23, 10g CYH-277 active toughening agent and 3g smoke suppressant melamine octamolybdate into the reaction kettle, adjust the stirring speed to 1000r / min, and stir for 10min; then add 8g lemon yellow, 1.2 g silicone defoamer BYK-051, 0.4g leveling agent BYK-333, 10g xylene, 2g n-butanol, stir at 1500r / min at high speed for 10min until the mixture is completely mixed; then stir at low speed at 200r / min for 20 minutes Defoaming, filtering to obtain component A;

...

Embodiment 2

[0032] 1. Component A: Take 100g of E51 epoxy resin, 30g of E44 epoxy resin and 15g of 501 epoxy active diluent after heating in a water bath at 100°C for 20 minutes, put them into the reaction kettle, disperse and mix at 25°C, and stir at a speed of 400r / min; After mixing evenly, 100g of aluminum hydroxide, 30g of magnesium hydroxide, 20g of ammonium polyphosphate with a degree of polymerization greater than 1000, 10g of composite flame retardant fr-106, 2g of composite flame retardant fr-2, 5g of coupling agent KH560 , 4g plasticizer DOP, 2g polysulfide rubber LP-23, 10g CYH-277 active toughening agent and 5g melamine octamolybdate were added to the reaction kettle, the stirring speed was adjusted to 1000r / min, and stirred for 10 minutes; then Add 8g iron oxide blue, 2g silicone defoamer BYK-051, 0.7g leveling agent BYK-333, 13g xylene, 3g n-butanol, stir at 1500r / min for 10min until the mixture is completely mixed; then 200r at low speed / min stirred for 20 minutes to defo...

Embodiment 3

[0036] 1. Component A: Take 60g of E51 epoxy resin, 20g of E44 epoxy resin and 10g of 501 epoxy active diluent after heating in a water bath at 100°C for 40 minutes, put them into the reaction kettle, disperse and mix at 20°C, and stir at a speed of 600r / min; After mixing evenly, 60g of aluminum hydroxide, 20g of magnesium hydroxide, 10g of ammonium polyphosphate with a degree of polymerization greater than 1000, 10g of fr-2, 3g of coupling agent KH560, 4g of plasticizer DOP, and 0.5g of polysulfide rubber LP -23. Add 10g CYH-277 active toughening agent, 1g melamine octamolybdate, and 1g molybdenum trioxide into the reaction kettle, adjust the stirring speed to 1000r / min, and stir for 10 minutes; then add 6g lemon yellow, 1g organic Silicon defoamer BYK-051, 0.4g leveling agent BYK-333, 8g xylene, 2g n-butanol, stir at 1500r / min at high speed for 10min until the mixture is completely mixed; then stir at low speed at 200r / min for 20 minutes for defoaming , filtered to obtain c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant double-component adhesive used for a color road surface, belonging to the technical field of adhesive preparation, and suitable for the internal road surface of a long and large tunnel. The flame-retardant double-component adhesive used for the color antiskid pavement layer of a tunnel prepared by the invention comprises a component A and a component B. In application, the two components are uniformly mixed to obtain the flame-retardant double-component adhesive used for the color antiskid pavement layer of the tunnel. The adhesive is an environmentally-friendly, non-toxic, high-reflectivity, flame-retardant and smoke-suppression and high-slip-resistance adhesive used for the color antiskid pavement layer of the tunnel road surface, and can be used in surface pavement of the internal road surface of the long and large tunnel and the pavement of a tunnel gates.

Description

technical field [0001] The invention belongs to the technical field of adhesive preparation, in particular to a flame-retardant two-component epoxy system adhesive for colored pavements, which is suitable for road surfaces in long tunnels. Background technique [0002] At present, problems such as traffic jams, traffic accidents and traffic safety have become increasingly prominent in road transportation. Among many solutions, colored pavement with diversion control traffic functions has been widely used in the field of road management. [0003] With the rapid development of highway traffic in our country, there are more and more highways in various places, and the number of highway tunnels is also increasing. At present, asphalt concrete pavement is commonly used in most tunnel pavements in China to replace cement concrete pavement pavement. Compared with cement concrete pavement, asphalt concrete has the advantages of comfortable driving, low driving noise and good skid r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/10
Inventor 张帅杜素军刘鹏飞张文才舒兴旺王海波杨喜英周亚军
Owner SHANXI PROVINCIAL RES INST OF COMM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com