A method for comprehensive utilization of vanadium-titanium magnetite

A technology for vanadium-titanium-magnetite and magnetic separation separation, which is applied in chemical instruments and methods, magnetic separation, and process efficiency improvement, etc. It can solve the problems of serious agglomeration reduction and pulverization, and achieve the effects of being beneficial to environmental protection, short reaction time and shortened production cycle.

Inactive Publication Date: 2011-12-14
UNIV OF SCI & TECH BEIJING
View PDF4 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are some defects in these two processes. The northern process consumes a lot of sodiumizing agent, and the pellets after sodiumizing and extracting vanadium are seriously pulverized; the southern process avoids the shortcomings of the northern process, but the technical difficulty lies in the electric furnace melting process. Among them, the trend of vanadium is difficult to control, and both types of processes are in the research stage
[0006] The application number is 200510020117.7 Chinese patent application "from the method for separating and extracting metal elements from vanadium-titanium-magnetite" proposed vanadium-titanium-magnetite rotary h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for comprehensive utilization of vanadium-titanium magnetite
  • A method for comprehensive utilization of vanadium-titanium magnetite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] What this embodiment adopts is the vanadium-titanium magnetite in Panzhihua area (composition is TFe54.54%, FeO23.16%, SiO 2 2.934%, CaO0.398%, Al 2 o 3 3.54%, MgO3.7%, S0.292%, TiO 2 10.77%, V 2 o 5 0.666%), and add 20% reducing agent (the composition is fixed carbon 86.47%, volatile matter 8.58%, ash 4.95%, S0.31%), flux (CaF 2 2%) and binder (cornmeal 2.5%), mix well, add water, press into a block, dry at 200-300°C, add to the rotary hearth furnace for high temperature reduction, the temperature in the rotary hearth furnace Keep it at 1350-1500°C, and control the reduction time at 15-45 minutes. After the reduction, magnetic separation separates to obtain high-titanium slag and pearl iron. After the high-titanium slag extracts vanadium, the grade of titanium slag is above 48.73%, and the slag is oxidized The content of ferrous iron is less than 2%, which meets the raw material requirements of sulfuric acid titanium dioxide production process; the iron content of...

Embodiment 2

[0026] What this embodiment adopts is the vanadium-titanium magnetite in Panzhihua area (composition is TFe53.54%, FeO28.16%, SiO 2 2.2%, CaO0.338%, Al 2 o 3 2.74%, MgO1.4%, S0.302%, TiO 2 10.82%, V 2 o 5 0.5%), and add 15% reducing agent (the composition is fixed carbon 86.47%, volatile matter 8.58%, ash 4.95%, S0.31%), flux (Na 2 SO 4 3%, CaF 2 2%) and binder (cornmeal 1.5%), mix well, add water, press into a block, dry at 200-300°C, add to the rotary hearth furnace for high temperature reduction, the temperature in the rotary hearth furnace Keep it at 1350-1500°C, and the reduction time is controlled at 15-45min. After the reduction, magnetic separation separates to obtain high-titanium slag and pearl iron. After the high-titanium slag extracts vanadium, the grade of titanium slag is above 49.64%, and the slag is oxidized The content of ferrous iron is less than 2%, which meets the raw material requirements of the sulfuric acid titanium dioxide production process; th...

Embodiment 3

[0028] What this embodiment adopts is the vanadium-titanium magnetite in Panzhihua area (composition is TFe55.34%, FeO29.07%, SiO 2 2.3%, CaO0.32%, Al 2 o 3 2.45%, MgO1.21%, S0.35%, TiO 2 8.27%, V 2 o 5 0.69%), and add 18% reducing agent (the composition is fixed carbon 86.47%, volatile matter 8.58%, ash 4.95%, S0.31%), flux (Na 2 SO 4 1.5%, CaF 2 2.5%) and binder (cornmeal 3.0%), mix thoroughly, add water, press into a block, dry at 200-300°C, add to the rotary hearth furnace for high temperature reduction, the temperature in the rotary hearth furnace Keep it at 1350-1500°C, and the reduction time is controlled at 15-45min. After the reduction, magnetic separation separates to obtain high-titanium slag and pearl iron. The iron content is less than 2%, which meets the raw material requirements of the sulfuric acid titanium dioxide production process; the iron content of pearl iron is more than 96%, which is a high-quality steelmaking raw material for electric furnaces. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for comprehensive utilization of vanadium-titanium magnetite, which belongs to the field of new technology of direct reduction ironmaking in the metallurgical industry. In order to solve the problems of low utilization of iron, vanadium and titanium in vanadium-titanium magnetite, at the same time, due to the sintering process of traditional technology, the comprehensive energy consumption of the overall smelting process is relatively high, and the environmental pollution is serious. The invention provides a method of agglomerating vanadium-titanium magnetite and producing high-titanium slag and pearl iron by high-temperature reduction and melting in a rotary hearth furnace. The technical solution includes pelletizing of vanadium-titanium magnetite, high-temperature reduction in rotary hearth furnace, magnetic separation, and high-temperature reduction in rotary hearth furnace to directly produce high-titanium slag and pearl iron. Applying this method to process vanadium-titanium magnetite can not only effectively solve the problem of recovery of titanium and vanadium resources, but also obtain qualified iron pearls for steelmaking in electric furnaces, making full use of the iron, vanadium, and Valuable elements such as titanium.

Description

technical field [0001] The invention relates to a method for comprehensive utilization of vanadium-titanium magnetite, which belongs to the field of new technology of direct reduction ironmaking in the metallurgical industry. High-grade titanium slag and vanadium slag are obtained by high-temperature reduction melting of rotary hearth furnace to produce high-titanium slag and ferrite pearls. After vanadium is extracted from high-titanium slag, high-grade titanium slag and vanadium slag are obtained to achieve comprehensive recycling of iron, vanadium and titanium in vanadium-titanium magnetite. The purpose of other valuable elements. Background technique [0002] Vanadium-titanium magnetite is a mineral mainly composed of iron, vanadium and titanium, accompanied by a small amount of chromium, gallium, scandium, cobalt, nickel, platinum and other components, which has important comprehensive utilization value. [0003] The main metal minerals in the ore are: titanomagnetite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B13/00C22B1/14C22B7/00C22B3/08B03C1/00C22B34/12
CPCY02P10/20
Inventor 张建良邢相栋刘征建王春龙张旭曹明明任山苏步新焦克新
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap