Fantastic artificial jewelry and preparation method thereof

A technology of artificial gemstones and artificial gemstones, applied in jewelry, ion implantation plating, decorative arts, etc., can solve the problems of high production unit cost, less color, and artificial crystals that are not environmentally friendly, and achieve high-strength adhesion and good long-lasting performance Effect

Active Publication Date: 2012-04-11
牟小燕
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of this invention is to solve the problems that the current artificial crystals are not environmentally friendly, have few colors and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fantastic artificial jewelry and preparation method thereof
  • Fantastic artificial jewelry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The original lead-free glass with a super white color, a transmission percentage of 92%, and an iron content of 0.014 is washed and dried by a glass washing machine for the second time and rinsed with pure water, so that the original lead-free glass is fully dried and cleaned. Put the cleaned lead-free glass original into the vacuum coating machine chamber. Quantitative membrane material (silicon dioxide (SiO 2 ) Titanium dioxide (TiO 2 ) Trititanium pentoxide (Ti 3 o 5 )) into the library electron gun crucible. Vacuumize the vacuum machine chamber through various vacuum pump units to reach 1×10 -3 pa, at the same time, the heater is used to heat the vacuum chamber, and the electron gun current is adjusted to withstand high voltage to melt the required membrane material. After the film is completely melted, the multifunctional workpiece rotation method is used, and the vacuum coating is effective for SiO 2 、Ti 3 o 5 Carry out repeated multi-level processing, and...

Embodiment 2

[0047] The original glass sheet with ultra-white color, transmission percentage of 92%, and iron content percentage of 0.014 is washed and dried by a glass washing machine for the second time and rinsed with pure water, so that the original glass sheet is fully dried and cleaned. Put the cleaned glass original into the vacuum coating machine chamber. Quantitative membrane material (silicon dioxide (SiO 2 ) Titanium dioxide (TiO 2 ) Trititanium pentoxide (Ti 3 o 5 )) into the library electron gun crucible. Vacuumize the vacuum machine chamber through various vacuum pump units to reach 1×10 -3pa, at the same time, the heater is used to heat the vacuum chamber, and the electron gun current is adjusted to withstand high voltage to melt the required membrane material. After the film is completely melted, the multifunctional workpiece rotation method is used, and the vacuum coating is effective for SiO 2 、Ti 3 o 5 Carry out repeated multi-level processing, and determine the ...

Embodiment 3

[0049] The original glass sheet with ultra-white color, transmission percentage of 92%, and iron content percentage of 0.014 is washed and dried by a glass washing machine for the second time and rinsed with pure water, so that the original glass sheet is fully dried and cleaned. Put the cleaned glass original into the vacuum coating machine chamber. Quantitative membrane material (silicon dioxide (SiO 2 ) Titanium dioxide (TiO 2 ) Trititanium pentoxide (Ti 3 o 5 )) into the library electron gun crucible. Vacuumize the vacuum machine chamber through various vacuum pump units to reach 1×10 -3 pa, at the same time, the heater is used to heat the vacuum chamber, and the electron gun current is adjusted to withstand high voltage to melt the required membrane material. After the film is completely melted, the multifunctional workpiece rotation method is used, and the vacuum coating is effective for SiO 2 、Ti 3 o 5 Carry out repeated multi-level processing, and determine the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
hardnessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fantastic artificial jewelry and a preparation method thereof. The preparation method comprises the following steps of: coating a color film on leadless glass, connecting the color film with upper and lower layers of unleaded glass by glue, and generating different effects due to the thickness of the color film, the difference of the upper and lower positions of glue adhesion and different glue colors; reforming, cutting and angularly grinding to obtain fantastic stones with different angles, wherein the fantastic stones can be plated or not, and mainly used for jewelry, garments, shoes, luggage, artwares and the like. The fantastic jewelry manufactured according to the invention has different color changes in different angle views through four to five layers of mutual refractions, and has deep crystal effect on a thin crystal layer through light refraction. The fantastic artificial jewelry has strong dazzling degree and rich color change; the color change type can be over ten thousands; the fantastic artificial jewelry has the advantages of low cost, no processing amount requirement, simplicity and rapidness for production and proofing; and the fantastic artificial jewelry is leadless, so that the lead content can realize ROHS environment friendly standard.

Description

technical field [0001] The invention relates to an artificial gemstone and a preparation method thereof, in particular to a magic color artificial gemstone and a preparation method thereof, and belongs to the technical field of artificial gemstone or artificial crystal processing. Background technique [0002] Artificial crystal is high-lead glass, or lead crystal glass, that is, adding 24% lead oxide to ordinary glass (the composition is silicon dioxide), and you will get an artificial crystal with brightness and transparency similar to natural crystal. At present, artificial crystals are made of silica plus more than 24% lead to produce the effect of transparent refraction. The disadvantage is that its lead content is high, which cannot meet the international ROHS environmental protection standards. Moreover, all the colors are plated on the surface of the product, which is easy to wear and tear during processing and use. The color depth caused by the thickness of the gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A44C17/00A44C27/00C23C14/08C23C14/30
CPCA44C17/00A44C27/00B44C1/28C03C17/245B32B7/12C03C17/30B44C1/26C03C27/10A41D19/015A44C27/005
Inventor 牟小燕
Owner 牟小燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com