Method for constructing hemocompatible material surface with bionic periodic structure

A technology of blood compatibility and construction method, applied in the field of bionic micro-nano structure design and manufacture, can solve problems such as coagulation, and achieve the effects of improving surface friction of materials, improving blood compatibility, and safe and reliable use.

Inactive Publication Date: 2014-07-16
EAST CHINA JIAOTONG UNIVERSITY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of the material should avoid blood stagnation or eddy currents. The higher the roughness of the material, the greater the area exposed to the blood, and the greater the possibility of coagulation; but on the contrary, the smooth surface of the glass is also very serious.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for constructing hemocompatible material surface with bionic periodic structure
  • Method for constructing hemocompatible material surface with bionic periodic structure
  • Method for constructing hemocompatible material surface with bionic periodic structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Periodic surface structure design. According to the designed geometric model, the apparent contact angle calculation formula of the periodic structure surface is deduced based on the classical wetting theory, and the appropriate geometric structure size is determined according to the formula to meet the ideal superhydrophobic surface requirements. take side length a 10 mm, square column spacing b 20 mm, height h The apparent contact angle of the lower surface of the structure of this size is greater than 150°, which is superhydrophobic.

[0035] 2. Production of silicon-based hard (rigid) templates. Use photolithography to carve a periodic array of square pillars on the silicon substrate according to a pre-designed periodic microstructure pattern, and the side length of the micropillars a 10 mm, square column spacing b 20 mm, height his 5 mm. First, clean the silicon wafer sample, and treat it at 180°C for more than 4 hours to remove surface water molecules, a...

Embodiment 2

[0041] 1. Periodic surface structure design. take side length a 20 mm, square column spacing b 50 mm, height h The apparent contact angle of the lower surface of this size structure is greater than 150°, which is superhydrophobic.

[0042] 2. Production of K9 glass hard template. Use photolithography to carve a periodic array of square pillars on the silicon substrate according to a pre-designed periodic microstructure pattern, and the side length of the micropillars a 20 mm, square column spacing b 50 mm, height h is 20 mm. First, clean the K9 glass sample, and treat it at 180°C for more than 4 hours to remove surface water molecules, and use a thick glue spinner (Karl Suss, Germany, RC8) to spin-coat SU with the required thickness on the surface of K9 glass. -8 photosensitive resin, the thickness of the SU-8 layer can be controlled by adjusting the speed and time of glue rejection. Then, pre-baking the SU-8 glue was performed in a programmed oven, and a photoresist m...

Embodiment 3

[0048] 1. Periodic surface structure design. take side length a 50 mm, square column spacing b 100 mm, height h The apparent contact angle of the lower surface of this size structure is greater than 150°, which is superhydrophobic.

[0049] 2. Production of titanium dioxide hard template. Use photolithography to carve a periodic array of square pillars on the silicon substrate according to a pre-designed periodic microstructure pattern, and the side length of the micropillars a 50 mm, square column spacing b 100 mm, height h is 25mm. Firstly, the titanium dioxide sample was cleaned and treated at 180°C for more than 4 hours to remove surface water molecules, and the surface of the silicon wafer was spin-coated with SU- 8 Photosensitive resin, the thickness of the SU-8 layer can be controlled by adjusting the speed and time of glue rejection. Then, pre-baking the SU-8 glue was performed in a programmed oven, and a photoresist model was obtained by contact exposure on a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for constructing a blood-compatible biomaterial surface with a bionic periodic structure. The steps are as follows: According to the surface model of the micro-square column, the theoretical prediction formula of the apparent contact angle of the periodic microstructure surface is derived, and according to this formula, it is determined whether the designed microstructure surface has ideal superhydrophobicity; according to the periodic microstructure, etching A hard template with micro-square columns with an array structure is produced, and PDMS is poured on the hard template to make it cross-linked and solidified, and the cured film is peeled off as an elastic template; then the prepolymer is cast on it, and after curing, the polymer surface Micropatterns that are complementary to the elastic template but similar to the source template are formed. The bionic blood compatibility material with a periodic structure constructed by the present invention can effectively inhibit the adhesion and deformation of platelets, avoid activating the coagulation pathway, prolong the life of anticoagulant blood, and improve the wetting of the interface by rationally regulating the surface geometry. wettability, thereby improving the blood compatibility of the material.

Description

technical field [0001] The invention relates to a method for constructing a blood-compatible material surface with a bionic periodic structure, and belongs to the technical field of design and manufacture of bionic micro-nano structures. Background technique [0002] Contact between blood and materials can lead to adverse consequences such as hemolysis and thrombosis. Over the years, researchers have been developing new biomaterials and surface modification of existing biomaterials through various approaches. For the former, such ideal blood-compatible materials have not been found yet. For the latter, it is often modified by coating antithrombotic drugs (anticoagulants) on the surface of materials without blood compatibility or poor compatibility, in order to reduce the occurrence of blood coagulation, but this method uses After anticoagulants such as heparin enter the blood circulation, they will interfere with the self-stabilization of the blood coagulation system and b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C39/02B29C39/22B29C33/38C08J7/12C08L83/04
Inventor 李刚
Owner EAST CHINA JIAOTONG UNIVERSITY