Cement-based penetrable crystallized waterproof paint, preparation method and construction method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of osmotic crystallization and waterproof coatings, which is applied in infrastructure engineering, water conservancy engineering, sea area engineering, etc. It can solve problems such as weak waterproof performance, affecting the anti-seepage and waterproof performance of coatings, and poor permeability of concrete structures.
Active Publication Date: 2013-04-10
姜哲 +1
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The present invention provides a cement-based osmotic crystalline waterproof coating and its preparation method and construction method. Poor, weak waterproof performance, poor penetration ability of the coating on the concrete structure, technical problems affecting the anti-seepage and waterproof performance of the coating
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0053] Embodiment 1, this cement-based permeable crystalline waterproof coating is prepared from the following raw materials by weight percentage:
[0054] Cement 65%;
[0055] Modified bentonite 4.5%;
[0056] Modified sodium silicate 2.5%;
[0057] Diffuser 1.5%;
[0058] Penetrant 2.0%;
[0059] Silica fume 3.5%;
[0060] Quartz sand 21%.
Embodiment 2
[0061] Embodiment 2, this cement-based permeable crystalline waterproof coating is prepared from the following raw materials by weight percentage:
[0062] Cement 68%;
[0063] Modified bentonite 3%;
[0064] Modified sodium silicate 2%;
[0065] Diffusion agent 1%;
[0066] Penetrant 1%;
[0067] Silica fume 3%;
[0068] Quartz sand 20%.
Embodiment 3
[0069] Embodiment 3, this cement-based permeable crystalline waterproof coating is prepared from the following raw materials by weight percentage:
[0070] Cement 68%;
[0071] Modified bentonite 5%;
[0072] Modified sodium silicate 3%;
[0073] Diffusion agent 1%;
[0074] Penetrant 1%;
[0075] Silica fume 2%;
[0076] Quartz sand 19.5%;
[0077] Hydroxypropyl Methyl Cellulose 0.5%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a cement-based penetrable crystallized waterproof paint, a preparation method and a construction method thereof. The cement-based penetrable crystallized waterproof paint is prepared from the following raw materials in percentage by weight: 65 to 70 percent of cement, 3 to 10 percent of modified bentonite, 2 to 5 percent of modified sodium silicate, 1 to 5 percent of diffusant, 0.5 to 1 percent of penetrant, 2 to 10 percent of wollastonite and 15 to 25 percent of quartz sand. The waterproof paint can recover minute cracks on concrete interfaces and inhibit the water seepage and damp of base interfaces effectively. In addition, the waterproof paint is high in capacity of freezing resistance, high-temperature resistance, chloridion resistance and acid and alkali resistance, and has a long waterproof effect. According to the cement-based penetrable crystallized waterproof paint, leveling layers on the concrete interfaces are saved, and protective layers are savedafter the concrete interfaces are coated, so the waterproof construction is simple. The cement-based penetrable crystallized waterproof paint is suitable for constructional engineering such as underground engineering, subway tunnels, civil air-defense construction, water ponds, oil sumps, sewage tanks, barns, bathrooms, roof squares, parking platforms, high-grade roadways and the like, and is used for processing defects of cracks, honeycomb pitted surfaces and the like of the concrete interfaces.
Description
technical field [0001] The invention relates to a building waterproof paint, a preparation method and a construction method thereof. Background technique [0002] In industrial and civil reinforced concrete construction projects, due to the poor impermeability and waterproof performance of concrete materials, cracks are prone to occur on the surface of buildings and water leakage occurs. The method of laying waterproof membranes or painting paint on the concrete surface not only has high cost and complicated construction methods, but also has problems such as poor durability and environmental pollution. [0003] In recent years, cement-based permeable crystalline waterproof coatings have been widely used in construction projects such as subways, tunnels, and reservoirs. and other materials (such as the Chinese invention patent application with the publication number CN1472160A, and the Chinese invention patent application with the publication number CN101759414A). The bent...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.