Formula for preparing brake pads by utilizing acicular ceramic fiber
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of ceramic fiber and brake pads, which is applied in the direction of brake parts, friction linings, mechanical equipment, etc., can solve the problems of high thermal conductivity, unsatisfactory braking performance and braking comfort, etc., to reduce thermal conductivity, Excellent high temperature effect
Inactive Publication Date: 2012-08-01
DONGYING BORUI BRAKE SYST
View PDF5 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, the common problem of brake pads is that the thermal conductivity of the product is high, so the braking performance and braking comfort under high temperature and high speed conditions are not very ideal.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014]
[0015]
[0016]
[0017]
[0018] According to above formula according to the production technology processing sample of prior art is tested, the result is:
[0019] FAW-Volkswagen BORA's original supporting brake pads are metal-less friction pads produced by Germany's TMD company. During use, the braking distance at a speed of 100 kilometers is 52.6 meters. The TP2044 bench test shows that the friction coefficient is the highest at a speed of 160 km / h. 0.26, and the brake friction coefficient is around 0.30 at 500°C.
[0020] After using the processed brake pad of the formula A of the present invention, the braking distance at a speed of 100 kilometers is 43.8 meters. In the TP2044 bench test, the lowest point of the friction coefficient is 0.29 at a speed of 160Km / h, and the friction coefficient is 0.35 at 500°C.
[0021] The original brake pads for FAW-Volkswagen A6 are metal-less friction pads produced by TMD Company in Germany. During use, the braking ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
friction coefficient
aaaaa
aaaaa
friction coefficient
aaaaa
aaaaa
friction coefficient
aaaaa
aaaaa
Login to view more
Abstract
The invention provides a preparing formula of brake pad by utilizing acicular ceramic fiber. Ingredients of the formula comprise (by weight) 5%-10% of adhesive, 15%-20% of reinforced fiber, 20%-30% of abrasive, 15%-25% of lubricant, 10%-15% of modifier and 20%-30% of filler, wherein the adhesive is phenolic resin, or silicon modified phenolic resin, or butyronitrile modified phenolic resin or mixture of the three, the reinforced fiber is acicular ceramic fiber, or aramid pulp, or copper fiber or mixture of the three, the abrasive is zirconium silicate, or iron black, or aluminium oxide or mixture of the three, the lubricant is graphite, or metal sulfide or mixture of the both, the modifier is friction powder, or potassium titanate wafer or mixture of the both, and the filler is barium sulfate, or calcium carbonate or mixture of the both. By the aid of the preparing formula of brake pad by utilizing acicular ceramic fiber, the heat energy generated from rapid brake can be effectively absorbed by the finished brake pad in usage, and the thermal conductivity of the brake pads can be reduced, so that the brake pads have excellent braking performances in terms of high-temperature resistance, rapidness and comfortability.
Description
technical field [0001] The invention relates to a production formula of a brake pad, in particular to a formula for producing a brake pad by using needle-like ceramic fibers. Background technique [0002] The main formulations of the existing brake pads are binders, reinforcing fibers, abrasives, lubricants and necessary regulators. [0003] The processing technology is as follows: mixing materials, hot pressing, heat treatment, grinding, painting, installing accessories, printing labels, packaging. [0004] With the rapid development of the modern automobile industry, the speed of passenger cars is getting higher and higher. This also requires that the brake pads not only have good braking effect, but also have good heat resistance and good braking comfort. At present, the common problem of brake pads is that the thermal conductivity of the product is high, so the braking performance and braking comfort under high temperature and high speed conditions are not very ideal. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.