Coated mist release paper

A technology of release paper and matte surface, which is applied in coating, papermaking, paper coating, etc., can solve the problems of high energy consumption, and achieve the effects of low cost, good film formation and convenient operation

Inactive Publication Date: 2012-10-03
斯迪克新型材料(江苏)有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, a large amount of energy is consumed when preparing release paper in the prior art, so it is necessary to provide a low-energy consumption, quality-controllable coating-type matte release paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1: A coated matte release paper

[0028] A kind of coating type matte release paper, described coating type matte release paper is made by coating on base paper with matte coating release agent, the raw material formula of described matte coating release agent It consists of the following materials in mass percentage:

[0029] Polyvinyl alcohol aqueous solution 15~70%;

[0030] Emulsion type silicone release agent 20~65%;

[0031] Stabilizer 6~12%;

[0032] Emulsifier 0.3~2%;

[0033] Catalyst 1.2~4.5%;

[0034] Cross-linking agent 0.5~3.5%

[0035] Fogging filler 2~10%;

[0036] The stabilizer is at least one of agar, gelatin and water-soluble starch; the emulsifier is at least one of sodium polyphosphate, Tween 80 and tributyl phosphate; Benzoyl oxide; the cross-linking agent is methyl hydrogen-containing silicone oil; the fogging filler is a solid particle with a particle size of 3 to 20 microns.

[0037] A further preferred technical solution of the ...

Embodiment 2 5

[0042] Embodiment 2~5: A kind of coated matte release paper

[0043] A kind of coating type matte release paper, described coating type matte release paper is made by coating on base paper with matte coating release agent, the raw material formula of described matte coating release agent As shown in the following table:

[0044] Embodiment two Embodiment three Embodiment four Embodiment five Aqueous solution of polyvinyl alcohol 16% 65% 43% 31% Emulsion type silicone release agent 62% 21% 35% 47% stabilizer 12% 6% 6% 9% Emulsifier 2% 0.3% 1% 0.7% catalyst 2.5% 1.2% 1.5% 2.3% crosslinking agent 2.5% 0.5% 3.5% 2% fog filler 3% 6% 10% 8%

[0045] Note: 1. The percent sign in the table indicates the mass percent content.

[0046] 2. Polyvinyl alcohol aqueous solution: embodiment two, viscosity is 800 cps; embodiment three, viscosity is 3500 cps; embodiment four, viscosity is 2000 cps; embodiment ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses coated mist release paper which is obtained by coating a matte lamination release agent on raw paper. According to a material formula, the matte lamination release agent consists of 15-70% of polyvinyl alcohol aqueous solution, 20-65% of emulsion type organosilicon release agent, 6-12% of stabilizer, 0.3-2% of emulsifier, 1.2-4.5% of catalyst, 0.5-3.5% of crosslinking agent and 2-10% of matting filler. The stabilizer is at least one of agar, gelatin and water-soluble starch; the emulsifier is at least one of sodium polyphosphate, Twain 80 and tributyl phosphate; the catalyst is platinum catalyst or benzoyl peroxide; and the crosslinking agent is methyl hydrogen polysiloxane oil. The coated mist release paper is simple in production technology flow, low in cost and convenient in operation.

Description

technical field [0001] The invention relates to a coating-type matte release paper, in particular to a matte release paper formed by coating the surface of a base paper with a film-forming material. Background technique [0002] Release paper, also known as release paper and anti-adhesive paper, is a kind of anti-adhesive paper that prevents prepreg from sticking and protects prepreg from contamination. Different organic pressure-sensitive adhesives, such as hot-melt adhesives, acrylic adhesives, and pressure-sensitive adhesives of rubber systems, require different release forces from the release paper. For the different viscosities of the adhesives that need to be isolated, the release force should be Relative adjustment is made to achieve an extremely light and stable release force when peeling. [0003] The release paper is made by pouring a certain thickness of polyethylene film layer on the surface of the base paper, and then coating the silicon release agent on the po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/38D21H19/40D21H19/60D21H19/44D21H19/54D21H21/14
Inventor 金闯周满意陈锋
Owner 斯迪克新型材料(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap