Anti-fouling separation membrane and preparation method thereof

A separation membrane and anti-pollution technology, applied in semi-permeable membrane separation, chemical instruments and methods, membrane technology, etc.

Active Publication Date: 2014-10-15
TIANJIN POLYTECHNIC UNIV
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the shortcomings of the current anti-pollution PVDF separation membrane preparation technology, the present invention provides a new method for preparing anti-microbial pollution PVDF separation membrane

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Synthesis of copolymer: Add 0.25mol MMA, 0.05mol DMC and 0.05mol AMPS into a three-necked flask containing 100ml DMF, add 0.082g AIBN under nitrogen protection, and react for 24h under heating in an oil bath at 60°C. After the reaction is completed, wash with a large amount of ethanol and water for several times, and after drying, immerse the crude product in tetrahydrofuran solution to remove the homopolymer. Finally dry to obtain the refined copolymer, stand-by;

[0025] The added DMF quality in the step (1) is 2 times of the total mass of the reaction solution;

[0026] The THF quality used in the step is 2 times of the precipitate quality;

[0027] (2) Preparation of casting solution: take a certain amount of PVDF powder, copolymer powder, polyethylene glycol (PEG) and DMF (accounting for 76% of the total mass of casting solution) to prepare casting solution;

[0028] The PVDF / copolymer quality is 16% of the casting liquid quality, and the mass ratio of PVDF a...

Embodiment 2

[0034] (1) preparation of copolymer: with embodiment 1;

[0035] (2) Preparation of casting solution: take a certain amount of PVDF powder, copolymer powder, polyethylene glycol (PEG) and dissolve in DMF (accounting for 70% of the total mass of casting solution) to prepare casting solution;

[0036] The quality of the PVDF / copolymer is 20% of the quality of the casting solution, and the mass ratio of PVDF to the copolymer is 7 / 3;

[0037] The polyethylene glycol (PEG) molecular weight is 10000, and the addition amount is 10% of the casting solution quality;

[0038] The added amount of DMF is 70% of the total mass of the casting solution;

[0039] (3) Preparation of flat film: the film casting solution prepared in the step (2), after degassing treatment, scrape flat film with a scraper, and solidify into film in water;

[0040] In the step (3), the degassing treatment time of the casting solution is 24 hours, the specification of the scraper is 300 μm, and the temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-pollution separation membrane and a preparation method, wherein aiming at the shortages of a preparation technology for the present anti-pollution PVDF (polyvinylidene fluoride) separation membrane, the invention provides a novel method for preparing an anti-microbial pollution PVDF separation membrane. The novel method provided by the invention comprises the following steps of: synthesising the random copolymer with a zwitterionic structure, of MMA (methl methacrylate), DMC (dimethyl carbonate) and AMPS (2-acrylamido-2-methylpropane sulfonic acid) via free radical polymerization at first, adding the copolymer and a porogenic agent, i.e., polyethylene glycol (PEG) in PVDF, and preparing the anti-pollution separation membrane by using N,N-dimethyl formamide (DMF) as a solvent and using water as a coagulating agent through a phase inversion method. Electropositive quaternary amine group and electronegative sulfonic group exist in the structure of the copolymer simultaneously, and have a binding capacity for water molecules which is much stronger than the binding capacity of traditional polyethylene glycol and the derivatives of the traditional polyethylene glycol, and the formed hydration layer is more stable; therefore, the prepared novel PVDF membrane is lasting in anti-pollution performance.

Description

technical field [0001] The invention belongs to the technical field of polymer membranes, and relates to a polymer separation membrane resistant to microbial contamination. Background technique [0002] In recent years, membrane separation technology is gradually replacing traditional separation technologies such as chromatography and distillation due to its advantages of high separation efficiency, low energy consumption, no phase change, no pollution to the environment, and simple and easy to scale-up process in water treatment, petrochemical industry, etc. , biopharmaceuticals, environment, energy, food and medical care and other fields have played a huge role and achieved huge economic and social benefits. The core of membrane technology is membrane material and its separation membrane. As a common separation membrane material, polyvinylidene fluoride (PVDF) has excellent mechanical properties, chemical and thermal stability. Its strong hydrophobicity makes it an ideal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/34B01D69/02B01D69/06B01D67/00
Inventor 陈莉申向赵义平冯霞刘捷
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com