Cation high performance slurry

A high-performance, cationic technology, applied in the direction of plant fibers, etc., can solve problems such as difficult handling and environmental pollution, and achieve the effects of easy handling, good fluidity, and good anti-aging properties.

Inactive Publication Date: 2012-10-17
YIXING JUNDA SLURRY TECH
View PDF2 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the price of polyvinyl alcohol (PVA) sizing is much higher than that of starch sizing, coupled with polyvinyl alcohol (PVA) s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cation high performance slurry
  • Cation high performance slurry
  • Cation high performance slurry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Put 85kg of cornstarch, 10kg of trimethylamine hydrochloride, 3kg of sodium hydroxide, and 2kg of calcium persulfate into the reaction tank respectively, carry out compound mixing reaction at 38°C for 1.5h, then terminate the reaction, unload and pack, and store. When the customer is using it, add clear water to gelatinize and heat up to 95°C or add clear water in a high-pressure tank to heat up to 125°C and keep warm for 30-45 minutes to carry out etherification and oxidation compound reactions to obtain an emulsion for sizing fabrics.

Embodiment 2

[0026] Put 88kg of cornstarch, 8kg of trimethylamine hydrochloride, 2kg of sodium hydroxide, and 2kg of potassium hydrogen persulfate into the reaction tank respectively, carry out the compound mixing reaction at 38°C for 1.5 hours, then stop the reaction, unload and pack, and store . When the customer is using it, add clear water to gelatinize and heat up to 95°C or add clear water in a high-pressure tank to heat up to 125°C and keep it warm for 30-45 minutes to carry out etherification and oxidation compound reactions to obtain a fabric sizing emulsion.

Embodiment 3

[0028] Put 92kg of cornstarch, 6kg of trimethylamine hydrochloride, 1kg of sodium hydroxide, and 1kg of ammonium persulfate into the reaction tank, carry out compound mixing reaction at 38°C for 1.5 hours, then stop the reaction, unload and pack, and store. When the customer is using it, add clear water to gelatinize and heat up to 95°C or add clear water in a high-pressure tank to heat up to 125°C and keep it warm for 30-45 minutes to carry out etherification and oxidation compound reactions to obtain a fabric sizing emulsion.

[0029] All or part of the emulsion size obtained in the above examples is used to replace the polyvinyl alcohol, high-performance starch and ordinary starch in the existing size formula, and the fabric is sized in actual production, and the existing formula is used for comparative experiments . The formulations and production conditions of each group are shown in the table below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses cation high performance slurry. The slurry is formed by commixture reaction of raw materials including corn starch, sodium hydroxide, trimethylamine hydrochloride and persulfate with the following quality content: 80-95% of the corn starch, 1-10% of the sodium hydroxide, 1-15% of the trimethylamine hydrochloride, and 0.1-15% of persulfate. The cation high performance slurry has the advantages of strong adhesive force, good film formation property, tenacious chorion and good elasticity, the flexibility (anti-fatigue property) is improved by 3-4 times compared with common modified starch slurry, the cation high performance slurry has good wear-resisting property and ageing resistance, and a serous fluid has good liquidity and stable viscosity under an I normal temperature condition; and the slurry contains no polyvinyl alcohol, when a spinning purified cotton yarn is subjected to a sizing process, a variety with 60 yarns with common compactness can be processed without polyvinyl alcohol, when sash cotton or purified cotton yarn with more than 60 yarns is subjected to sizing process, little polyvinyl alcohol or no polyvinyl alcohol is used, desizing is easy, waste water of serous fluid is easy to process, pollution of the waste water to the environment is small, and zero-pollution discharge in the production process is realized.

Description

technical field [0001] The invention belongs to the field of textile industry, and in particular relates to a size in the yarn sizing process of the textile industry. Background technique [0002] In the yarn sizing process in the textile industry, because polyvinyl alcohol (PVA) size has excellent film-forming properties, adhesion and better compatibility with other sizes, it is considered to solve the problem of polyester-cotton blending. The most ideal size for spinning and pure cotton fine size, high density and high difficulty varieties. However, since the price of polyvinyl alcohol (PVA) sizing is much higher than that of starch sizing, coupled with polyvinyl alcohol (PVA) sizing and some refractory sizing, it is difficult to treat the sizing wastewater after desizing, causing environmental pollution. pollute. The damage to the environment and pollution problems have attracted widespread attention, especially the fabrics sized with polyvinyl alcohol (PVA) sizing have...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/11C08B31/12C08B31/18D06M101/06D06M101/32
Inventor 刘定国丁奎刚吴燕
Owner YIXING JUNDA SLURRY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap