Preparation method for transference resistance leather dye

A migration-resistant, leather-based technology that is applied in dyeing, organic dyes, textiles, and papermaking. It can solve the problems of poor color fastness of leather, casein resistance to light, and migration resistance, and achieve good color and transparency. , easy control of functionality, and stable performance of dyes

Inactive Publication Date: 2012-10-24
CHINA LEATHER & FOOTWEAR IND RES INST
View PDF7 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the use of a three-roller grinding machine, the pigment particles are coarse and uneven in size, and the coloring power and hiding power are not ideal, so that the leather finishing layer is thick, and the smoothness and fineness are poor, which affects the quality of finishing.
Casein as a stabilizer is not light fast, it will affect the whiteness of white leather and the brightness of colored leather, and it is easy to spoil
And the coloring method of adding pigment paste often leads to poor color fastness of leather, especially serious color fading by wet f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] The preparation process of the migration resistant leather polymer dye of the present invention is as follows:

[0032] Add a metered amount of isocyanate, polyol and catalyst into the reaction kettle, wherein the molar ratio of isocyanate to polyol is 1:0.10~0.50, preferably 1:0.15~0.45, and the catalyst is 0.02%~ of the total weight of isocyanate, polyol and reactive dye. 0.06%, preferably 0.03%-0.05%, stirred and reacted at 60-90°C for 60-180min, preferably 70-80°C, 90-130min, to form polyurethane prepolymer; add a suitable amount of solvent to adjust the viscosity of the reactant, the amount of solvent is isocyanate, The total weight of polyol and reactive dye is 50%-100%; when reactive dye is added, the molar ratio of isocyanate to reactive dye is 1:0.65~0.90, preferably 1:0.70~0.80, and the reaction is stirred at 60~95℃ for 60~180min , Preferably 75~90℃, 90~150min; adding chain extender, the molar ratio of isocyanate to chain extender is 1:0.10~0.60, preferably 1:0.2...

Example Embodiment

[0034] Example 1

[0035] Add 672.8kg HDI, 2000kg polypropylene glycol 2000, 2.01kg dibutyltin dilaurate to the reaction kettle, stir and react at 75℃ for 120min to form polyurethane prepolymer; add 4000kg N,N-dimethylformamide and stir evenly; add 1145.5kg Reactint-Black X41LV (hydroxyl value: 137), react at 90°C for 120min, then add 212.7kg of hexanediol, react at 80°C for 60min; then add 2515kg N,N-dimethylformamide dropwise to obtain a solid content of 38.22 % Of migration resistant leather dyes.

Example Embodiment

[0036] Example 2

[0037] Add 1111.5kg of IPDI, 1500kg of polypropylene glycol 1500, 1.71kg of dibutyltin dilaurate to the reactor, stir and react at 80℃ for 90min to form polyurethane prepolymer; add 3500kg of tetrahydrofuran and stir evenly; add 1468.9kg of reactint-red X64 (Hydroxyl value: 180), react at 80°C for 150min, then add 188.5kg 2-aminoethylethanolamine, react at 75°C for 50min; add 3000kg tetrahydrofuran dropwise to obtain a migration-resistant leather dye with a solid content of 39.64%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a preparation method for a transference resistance leather dye, wherein an active group-containing dye, an anti-yellowing isocyanate compound, a hydroxyl group-containing polymer, a compound containing a hydroxyl group and a hydrophilic functional group, a chain extender, and the like are subjected to polymerization to obtain a product of the present invention. The dye prepared by the method of the present invention has the following advantages that: performance is stable, and transference resistance of products dyed by the dye is excellent. The method of the present invention has advantages of simple synthetic route, molecular weight adjusting, easy functionality control, and the like. The dye prepared by the method of the present invention can be used for leather dyeing, and colorant components in leather coating and synthetic leather coating.

Description

technical field [0001] The invention relates to a preparation method for preparing polyurethane polymer migration-resistant leather dye, which belongs to the field of leather chemical materials. The dye obtained by the preparation method of the invention can be applied to leather dyeing and colorant components in leather and synthetic leather coatings. Background technique [0002] In the production process of leather, the leather is further colored by adding pigment paste to the polymer resin slurry in the bottom or middle layer coating or adding dye water in the top layer coating in the finishing process, so as to prepare rich-colored leather materials. The pigment paste used in the finishing process is generally a paste made by mixing and grinding pigments, casein, sulfated oil, preservatives, etc. It has strong hiding power, bright color and certain air permeability. It can be mixed with resin film former to prepare finishing paste, which is used for bottom and middle l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09B69/10C08G18/66C08G18/48D06P3/32D06P1/38
Inventor 庞晓燕陈永芳丁志文
Owner CHINA LEATHER & FOOTWEAR IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap