Aqueous alkyd acrylic resin paint and preparation method thereof
A technology of alkyd acrylic and resin coatings, applied in the direction of coating, etc., can solve the problems of material performance deterioration and achieve the effects of reduced VOC content, good color retention, and good weather resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] The preparation method of water-based alkyd acrylic resin coating, the above-mentioned components are batched, and the steps are:
[0030] The preparation steps of alkyd resin are:
[0031] (1) In a reaction vessel equipped with a stirring device, an oil-water separator and a thermometer, sequentially add soybean oil, pentaerythritol, and benzoic acid according to the formula amount, pass nitrogen protection, turn on stirring and condensate water, and heat up to 180°C within 1 hour;
[0032] (2) When the temperature reaches 120℃, add 35%~40% xylene of the formula;
[0033] (3) When the temperature reaches 180 ℃, the temperature is kept warm for 40 minutes, and the temperature is controlled at 180-200 ℃; 1 / 2 of the formula amount of phthalic anhydride and maleic anhydride and the remaining xylene are added, and the remaining phthalic anhydride and maleic anhydride are added after 10 minutes; Control at 210 ~ 220 ℃, keep warm for 1h;
[0034] (4) Increase the temperatur...
Example Embodiment
[0058] Example 1. Preparation of Alkyd Resin
[0059] In a 500ml four-necked flask equipped with a stirring device, an oil-water separator and a thermometer, add 60g soy oleic acid, 17.54g pentaerythritol, 1.65g benzoic acid successively, pass nitrogen protection, open stirring and condensed water, and be heated to 180°C in 1h (wherein When the temperature reaches 120°C, add 3g of xylene); when the temperature reaches 180°C, the temperature is kept warm for 40 minutes, and the temperature is controlled at 180-200°C; 8.27g of phthalic anhydride, 0.27g of maleic anhydride and 5.46g of xylene are added, and after 10 minutes, the remaining 8.27g phthalic anhydride and 0.27g maleic anhydride; heat up to control the temperature at 210-220°C, hold for 1 hour; continue to heat up to control the temperature at 220-230°C, and start to measure the acid value after holding for 1 hour; start when the acid value is less than 17mgKOH / g Cool down, cool down to 180°C, release water and xylene ...
Example Embodiment
[0060] Example 2. Preparation of drier
[0061] Dissolve 8.33g of emulsifier CO-436 in 88.89g of water, add 2.78g of ethylene glycol, 5.56g of cobalt isooctanoate, 22.22g of manganese isooctanoate, 22.22g of zirconium isooctanoate, disperse at a high speed of 1500r / mim, and stir for 2h. Drying agent for alkyd acrylic hybrid emulsion.
PUM
Property | Measurement | Unit |
---|---|---|
Acid value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap