Method for preparing manganese sulfate by using manganese dioxide ore pulp to absorb sulfur dioxide in flue gases

A technology of manganese dioxide ore and sulfur dioxide, which is applied in the fields of manganese sulfate, chemical industry, climate sustainability, etc., can solve the problems of large floor area, large reactor investment, and narrow airflow channel, and achieve high manganese content and solid The effect of low amount and low solid content

Active Publication Date: 2012-12-12
贵州大龙汇成新材料有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These existing processes are mainly divided into two types: one is to use manganese dioxide dry powder to desulfurize at a high temperature in a reaction bed, no matter using a fixed bed reactor, a moving bed reactor or a fluidized bed reactor, this is the same as the second The process of reducing and roasting manganese oxide is similar, but its disadvantages are that the reactor has a large investment, a large floor area, and poor operating conditions, and the fixed bed reactor needs intermittent operation, which is labor intensive. After the reaction, it is necessary to ball mill the absorbent and then dissolve it , the process is long; this kind of treatment process is still in the laboratory stage or pilot test stage in China, and industrial production has not been realized; a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing manganese sulfate by using manganese dioxide ore pulp to absorb sulfur dioxide in flue gases

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Table 1: The component content analysis table of raw material manganese dioxide manganese ore in embodiment 1

[0044] element Content μg / g (except %) element Content μg / g (except %) element Content μg / g (except %) mn 42.60% Ca 5.9 S 197.6 Hg 50 In 20 As 10.1 Se 20 Au 1 Mo 2.4 sn 513.3 B 8.1 P 1120 Zn 20 Pt 1 K 9200 Sb 34.2 Mg 2181 Na 2300 Ce 383.7 V 2.7 Fe 6% Pb 342 Al 4% 　 　

[0045] The high-temperature flue gas raw material used in this example is boiler flue gas with a temperature as high as 146° C. after electrostatic precipitating, and its composition content is shown in Table 2 below.

[0046] Table 2: Composition data analysis table of boiler flue gas in embodiment 1

[0047] project temperature SO 2 concentration N 2 O 2 NO NO 2 data result 146℃ 12000mg / Nm 3 82% 6.2% 620mg / Nm 3 240mg / Nm 3

[0048] like ...

Embodiment 2

[0069] Table 4: The component content analysis table of raw material manganese dioxide ore in embodiment 2

[0070] element Content μg / g (except %) element Content μg / g (except %) element Content μg / g (except %) mn 46% Cd 5 S 649.3 Hg 5 In 20 As 6 Se 20 Au 1 Mo 24 sn 22.7 B 17.1 P 1120 Zn 25 Pt 1 K 9400 Sb 20 Mg 1% Na 3400 Ce 100 V 335.8 Fe 6.30% Pb 22.2 Al 4.30% 　 　

[0071] The high-temperature flue gas raw material used in this example is the boiler flue gas with a temperature as high as 146° C. after electrostatic precipitating in Example 1, and its composition content is shown in Table 2 above.

[0072] like figure 1 Shown, a kind of method that absorbs sulfur dioxide in boiler flue gas with above-mentioned manganese dioxide ore produces manganese sulfate, comprises the following steps:

[0073] (1) Grinding: The maximum particle size of the imported manganese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing manganese sulfate by using a manganese dioxide ore pulp to absorb sulfur dioxide in flue gases. The method includes following steps of subjecting manganese dioxide ore to wet ball milling and grading to obtain an initial ore pulp, and smashing the initial ore pulp through a vertical type stirring mill to obtain a reaction ore pulp; adding a manganese sulfate solution containing Fe<3+> and/or Fe<2+> to the obtained reaction ore pulp, then subjecting the reaction ore pulp and the high temperature flue gases containing the sulfur dioxide to absorption reaction with the reaction temperature controlled between 90 DEG C and 95 DEG C; and subjecting reaction products obtained after the absorption reaction to solid-liquid separation, iron removing and heavy metal removing, and then performing ordinary pressure concentration and crystallization to obtain the manganese sulfate monohydrate, wherein particle sizes of ore materials in the initial ore pulp are smaller than 149 mu m, and particle sizes of 90% of the ore materials in the reaction ore pulp below 50 mu m. The method for preparing the manganese sulfate by using the manganese dioxide ore pulp to absorb the sulfur dioxide in the flue gases has the advantages of being energy-saving, environment-friendly, high in resource utilization rate, high in product additional value, good in flue gas desulfurization effects, continuous and thorough in reaction, low in costs and the like.

Description

technical field [0001] The invention belongs to the interdisciplinary technical field of hydrometallurgy, environmental protection and energy saving, and in particular relates to a method for preparing industrial-grade manganese salt by reacting high-grade natural manganese dioxide pulp with flue gas. Background technique [0002] Solid manganese sulfate monohydrate is an important chemical raw material, which can be used as fertilizer and feed additive, and is also the basic raw material of almost all manganese products. The annual demand in China alone is over one million tons, and it is also exported to other countries in large quantities. There are many domestic enterprises producing solid manganese sulfate monohydrate, which is also one of the traditional products of manganese products in China. [0003] Rhodochrosite can be used to produce manganese sulfate, but because rhodochrosite is generally symbiotic with calcium carbonate and magnesium carbonate, few domestic an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G45/10
CPCY02P20/10
Inventor 姚文德彭天剑申喜元林亲勇刘静
Owner 贵州大龙汇成新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap