Water-absorbing antibacterial hair-drying hat and preparation method thereof
A hair drying cap and hair drying technology, which is applied in hairdressing equipment, hair drying devices, hair or scalp washing devices, etc., can solve the problems of cumbersome use, water vapor entering the head, and bacteria generation, etc., and achieve convenient material collection and enhanced Tensile strength, strong antibacterial effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1 Preparation method of water-absorbent antibacterial hair dryer cap
[0031] A preparation method of a water-absorbing antibacterial hair dryer cap includes the following steps:
[0032] (1) Preparation of konjac gel solution: mix the konjac flour with a weight ratio of 1:10 and the acrylic acid solution with a degree of neutralization of 80% in advance with sodium hydroxide, and stir it with an electric mixer at 30°C at 2500r / min Blow nitrogen for 10 minutes to swell the konjac flour; then add 4.5% of the initiator potassium persulfate and 1.0% of the cross-linking agent N, N'-methylene bisacrylamide, stir evenly, and then transfer to 55℃ water bath temperature Carry out the graft polymerization reaction for 3 hours, then add 0.25% sodium carboxymethyl cellulose, 4.5% paraffin wax and heat at 75°C, stir for 10 minutes with a magnetic stirrer with a rotating speed of 1000r / min, to obtain Konjac gel solution I; The oxidation-modified product of manganese: water is 1...
Example Embodiment
[0039] Example 2 A method for preparing water-absorbent antibacterial hair dryer cap
[0040] A preparation method of a water-absorbing antibacterial hair dryer cap includes the following steps:
[0041] (1) Preparation of konjac gel solution: mix the konjac flour with a weight ratio of 1:10 and the acrylic acid solution with a degree of neutralization of 80% pre-neutralized with sodium hydroxide, and stir it with an electric stirrer at 2500r / min at 35℃ Purge the nitrogen for 15 minutes to swell the konjac flour; then add 5% of the initiator potassium persulfate and 1.5% of the cross-linking agent N,N'-methylene bisacrylamide, stir it evenly, and then transfer it to a water bath temperature of 60℃. After the graft polymerization reaction for 3.5 hours, add 0.3% sodium carboxymethyl cellulose and 5.0% paraffin wax and heat at 80℃, stir for 15 minutes with a magnetic stirrer with a rotating speed of 1000r / min to obtain Konjac Gel Solution I; The oxidation-modified product of mannose...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap