High elastic corrosion resistant epoxy sealant and preparation method thereof

An epoxy sealing and corrosion-resistant technology, used in epoxy resin glue, chemical instruments and methods, adhesives, etc., can solve problems such as poor sealing performance, unsatisfactory effect, and easy cracking.

Inactive Publication Date: 2013-01-30
YANTAI DARBOND TECH
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, epoxy resin itself is a brittle material. Although it has been modified flexibly, the effect is not ideal. The concentrated perf

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High elastic corrosion resistant epoxy sealant and preparation method thereof
  • High elastic corrosion resistant epoxy sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1) Preparation of component A:

[0053] The preparation of the A component is: 20 parts by weight of modified epoxy resin elastomer HyPox RA840, 15 parts of epoxy resin EPON862, 15 parts of hyperbranched epoxy resin, 8 parts of xylene formaldehyde resin, Add 12 parts of polypropylene glycol diglycidyl ether, 0.3 parts of coupling agent KH-560, and 0.3 parts of wetting and dispersing agent Texaphor P63 into the double planetary power mixer, and the rotation speed is 500 rpm, and the revolution speed is 15 rpm Under the condition of rotation speed of 800 rpm and revolution speed of 20 rpm, mechanically stir for 0.5 hours; then add 18 parts of quartz powder; then add 10 parts of fumed silica Stir for 20 minutes at a rotation speed of 200 rpm and a revolution speed of 10 rpm, vacuumize to -0.08Mpa until the foam disappears, and obtain component A, which is packaged and placed for use;

[0054] 2) Preparation of component B:

[0055] The preparation of the B component is a...

Embodiment 2

[0058] 1) Preparation of component A:

[0059] The preparation of the A component is as follows: 35 parts by weight of modified epoxy resin elastomer HyPox DA323, 20 parts of epoxy resin NPEF170, 10 parts of hyperbranched epoxy resin, 6 parts of liquid petroleum resin, 1 , Add 10 parts of 4-butanediol diglycidyl ether, 0.2 parts of coupling agent KH-560, and 0.3 parts of wetting and dispersing agent Texaphor P64 into the double planetary power mixing mixer, and at the rotation speed of 400 rpm, revolution Under the condition that the speed is 10 rpm, stir mechanically for 0.5 hours; then add 4 parts of quartz powder and 10 parts of mica powder, and then mechanically stir for 2.5 hours under the conditions of rotation speed of 600 rpm and revolution speed of 15 rpm Add 5 parts of fumed silicon dioxide and stir for 20 minutes under the conditions of rotation speed of 100 rpm and revolution speed of 5 rpm, vacuumize to -0.08Mpa until the foam disappears, and obtain component A. ...

Embodiment 3

[0064] 1) Preparation of component A:

[0065] The preparation of the A component is: 45 parts by weight of modified epoxy resin elastomer NPER-133L, 25 parts of epoxy resin EPON862, 5 parts of hyperbranched epoxy resin, and 2 parts of xylene formaldehyde resin , 5 parts of polypropylene glycol diglycidyl ether, 0.1 part of coupling agent KH-560, and 0.2 part of wetting and dispersing agent Texaphor P64 were added to the double planetary power mixer, and the rotation speed was 700 rpm, and the revolution speed was 20 Under the condition of rotation / minute, mechanically stir for 0.5 hours; then add 15 parts of talcum powder, and then add 15 parts of talcum powder under the conditions of rotation speed of 900 rotation / minute and revolution speed of 25 rotation / minute, mechanically stir for 2.5 hours; then add fumed silica 3 Parts were stirred for 20 minutes under the conditions of rotation speed of 400 rpm and revolution speed of 15 rpm, vacuumed to -0.08Mpa until the foam disap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high elastic corrosion resistant epoxy sealant and a preparation method thereof. The epoxy sealant provided by the invention comprises a component A and a component B in a weight ratio of 100:20-100:25. The epoxy sealant provided by the invention has advantages of high strength, high elasticity, low heat release, cracking resistance, good sealing performance and seawater corrosion resistance, is convenient for construction, and greatly improves sealing of key parts of ship stern tube.

Description

technical field [0001] The invention relates to a highly elastic and corrosion-resistant epoxy sealant and a preparation method thereof, belonging to the field of shipbuilding sealants. Background technique [0002] At present, the world's shipbuilding industry is accelerating its transfer to regions with rich labor force, capital and solid industrial foundation. my country's shipbuilding industry is expected to become the most internationally competitive industry. Information and data show that the proportion of China's shipbuilding industry in the global market is rising significantly, and China has become one of the world's important shipbuilding centers. Huge opportunities are presented in front of Chinese enterprises, providing a broad space for the development of marine sealants. [0003] At present, marine sealants are roughly divided into the following categories: silicone sealants, polyurethane sealants, polysulfide sealants, acrylate sealants, etc. These sealants...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00C09J163/02C09J11/08C09J11/04C09J11/06C09K3/10
Inventor 姜贵琳王建斌陈田安解海华
Owner YANTAI DARBOND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap