Low-temperature cured epoxy asphalt mortar and preparation method thereof

An epoxy asphalt, curing type technology, applied in the field of low temperature curing epoxy asphalt mortar and preparation, to achieve the effect of fast drying, high permeability and excellent anti-corrosion

Inactive Publication Date: 2013-02-06
CHONGQING SINCERE BOND PAVEMENT MATERIALS
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention mainly starts from the bonding performance, strength, and convenience of construction of materials, and selects epoxy resin with excellent high temperature resistance to plasticity and permanent deformation, low temperature crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Take 10g of Korean SK-70 asphalt, 15g of bisphenol A epoxy resin E-44, 3g of toluene, 2g of ethanol, 5g of aromatic oil, 30g of 10-20 mesh quartz sand, 25g of 40-70 mesh quartz sand, phenolic modified fat Amine curing agent 10g. Prepare low-temperature curing epoxy asphalt mortar as follows:

[0027] (1) Melt 10g of Korean SK-70 asphalt to 120~150℃ and keep the temperature constant for 10~20 minutes;

[0028] (2) Add 5g of aromatic oil, 3g of toluene, 2g of ethanol, 15g of bisphenol A epoxy resin E-44 in step (1), shear at 120~150℃ for 20~40 minutes at high speed, and place at room temperature for 48 Hour.

[0029] (3) In step (2), add 30g of 10-20 mesh quartz sand, 25g of 40-70 mesh quartz sand, 10g of phenolic modified fatty amine curing agent, stir at constant temperature and speed for 3-5 minutes, and obtain a uniform viscous liquid The mixture is the low-temperature curing epoxy asphalt mortar described in the present invention.

[0030] The test results verify...

Embodiment 2

[0032] Take 15g of Korean SK-90 asphalt, 10g of bisphenol A epoxy resin E-44, 3g of coal tar, 2g of acetone, 3g of aromatic oil, 35g of 10-20 mesh emery, 26g of 40-70 mesh quartz sand, cashew nut shell oil Sexual amine curing agent 6g. Prepare low-temperature curing epoxy asphalt mortar as follows:

[0033] (1) Melt 15g of Korean SK-90 asphalt to 120~150℃ and keep the temperature constant for 10~20 minutes;

[0034] (2) Add 3g of aromatic oil, 2g of acetone, 3g of coal tar, 10g of bisphenol A epoxy resin E-44 in step (1), shear at 120~150℃ for 20~40 minutes at high speed, and place at room temperature 48 hours.

[0035] (3) In step (2), add 35g of 10-20 mesh emery, 26g of 40-70 mesh quartz sand, 6g of cashew nut shell oil modified amine curing agent, stir at constant temperature and speed for 3-5 minutes, and obtain a uniform viscous liquid The mixture is the low-temperature curing epoxy asphalt mortar described in the present invention.

[0036] The test results verify th...

Embodiment 3

[0038] Ordinary domestic SBS modified asphalt 20g, bisphenol A type epoxy resin E-51 5g, C12-14 alkyl glycidyl ether 3g, acetone 2g, 10-30 mesh basalt particles 40g, 40-70 mesh quartz sand 27g, modified 3g permanent polyamide curing agent. Prepare low-temperature curing epoxy asphalt mortar as follows:

[0039] (1) Melt 20g of SBS modified asphalt to 120~150℃ and keep the temperature constant for 10~20 minutes;

[0040] (2) In step (1), add 3g of C12-14 alkyl glycidyl ether, 2g of acetone, 5g of bisphenol A epoxy resin E-51, high-speed shearing at 120~150℃ for 20~40 minutes, at room temperature Leave it for 48 hours.

[0041] (3) In step (2), add 40g of 10-30 mesh basalt particles, 27g of 40-70 mesh quartz sand, 3g of modified polyamide curing agent, and stir at constant temperature and speed for 3-5 minutes to obtain a uniform viscous liquid mixture It is the low-temperature curing epoxy asphalt mortar described in the present invention.

[0042]The test results verify th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bond strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-temperature cured epoxy asphalt mortar and a preparation method thereof. The epoxy asphalt mortar comprises the following components in percentage by weight: 10-20% of refined bitumen, 5-15% of epoxy resin, 5-10% of solubilizer, 40-70% of aggregate and 3-10% of curing agent. The low-temperature cured epoxy asphalt mortar has simple preparation process, low equipment requirement and low use cost, can be constructed and cured at normal temperature, not only is convenient to construct, but also has low requirement for equipment and is convenient to popularize and apply.

Description

technical field [0001] The invention relates to the related fields of asphalt pavement maintenance and repair, in particular to a low-temperature curing epoxy asphalt mortar capable of improving the surface layer performance of asphalt concrete pavement and sealing the pavement and a preparation method thereof. Background technique [0002] Under the new situation of rapid development of traffic, highway construction is advancing by leaps and bounds. Asphalt concrete pavement is more and more applied to high-grade highways, and the construction and maintenance quality of asphalt pavement is also paid more attention. Affected by various factors, the winter or low temperature construction of asphalt concrete pavement has become an unavoidable problem in the whole industry. [0003] The construction of asphalt concrete pavement has strict requirements on the construction climate. The "Technical Specifications for Construction of Highway Asphalt Pavement" JTGF40-2004 stipulates...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/26
Inventor 吴祥燕刘帮银
Owner CHONGQING SINCERE BOND PAVEMENT MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap