Environment-friendly neoprene sealant and preparation method thereof

The technology of sealant and chloroprene rubber is applied in the field of environmentally friendly chloroprene sealant and its preparation, which can solve problems such as construction environment hazards, and achieve the effects of good constructability, strong pressure resistance and simple operation.

Active Publication Date: 2013-02-06
GLEIHOW NEW MATERIALS CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional liquid sealants contain a large amount of toxic organic solvents such as benzene, toluene, xy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly neoprene sealant and preparation method thereof
  • Environment-friendly neoprene sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Environmentally friendly neoprene sealant, which includes the following components: neoprene rubber, fillers (including talcum powder, light calcium, magnesium oxide and titanium dioxide), ester solvents (including methyl acetate, ethyl acetate and butyl acetate) , Solvent oil (6# solvent oil and 120# solvent oil), plant extract essential oil (turpentine oil), softener (including stearic acid and transformer oil), antioxidant 300.

[0028] Wherein neoprene rubber, filler, ester solvent, mineral spirits, plant extract essential oil, softening agent, antioxidant 300% by weight are as follows: 14%, 28.9%, 19%, 20%, 10%, 8% %, 0.1%.

[0029] The weight ratio of talcum powder, light calcium, titanium dioxide and magnesium oxide in the filler is 20:5:5:1 in sequence.

[0030] The weight ratio of methyl acetate, ethyl acetate and butyl acetate in the ester solvent is 1:4:5 in sequence.

[0031] The weight ratio of 6# solvent oil and 120# solvent oil in solvent oil is 20:1 in...

Embodiment 2

[0044] Environmentally friendly neoprene sealant, which includes the following components: neoprene rubber, fillers (including talc, kaolin, magnesium oxide and titanium dioxide), ester solvents (including dimethyl carbonate, ethyl acetate and butyl acetate) , Solvent oil (6# solvent oil and 120# solvent oil), plant extract essential oil (turpentine oil and orange oil), softener (including stearic acid and transformer oil), antioxidant 330.

[0045] Wherein neoprene rubber, filler, ester solvent, mineral spirits, plant extract essential oil, softener, antioxidant 330 weight percentage content are as follows: 16%, 26.9%, 19%, 20%, 10%, 8% %, 0.1%.

[0046] The weight ratio of talcum powder, kaolin, titanium dioxide and magnesium oxide in the filler is 5:20:5:1 in sequence.

[0047] The weight ratio of dimethyl carbonate, ethyl acetate and butyl acetate in the ester solvent is 1:4:5 in sequence.

[0048] The weight ratio of 6# solvent oil and 120# solvent oil in solvent oil is...

Embodiment 3

[0057] Environmentally friendly neoprene sealant, which includes the following components: neoprene rubber, fillers (including talc, kaolin, magnesium oxide and titanium dioxide), ester solvents (including dimethyl carbonate, ethyl acetate and butyl acetate) , solvent oil, plant extract essential oil, softener (including stearic acid, transformer oil), antioxidant 330.

[0058] Wherein neoprene rubber, filler, ester solvent, mineral spirits, plant extract essential oil, softening agent, antioxidant 330 weight percentage content are as follows: 20%, 29.9%, 15%, 19%, 10%, 6 %, 0.1%.

[0059] The weight ratio of talcum powder, kaolin, titanium dioxide and magnesium oxide in the filler is 20:5:5:1 in sequence.

[0060]The weight ratio of dimethyl carbonate, ethyl acetate and butyl acetate in the ester solvent is 1:4:5 in sequence.

[0061] The weight ratio of 6# solvent oil and 120# solvent oil in solvent oil is 20:1 in turn.

[0062] The weight ratio of transformer oil and ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of adhesives, and particularly relates to an environment-friendly neoprene sealant and a preparation method thereof. The environment-friendly neoprene sealant comprises the following components: neoprene, filler, esters solvent, solvent oil, phytoextraction essential oil, softener and antioxygen, wherein the filler is a mixture made of one or more than two of talcum powder, light calcium carbonate, titanium dioxide, magnesium oxide, kaolin and blanc fixe; the esters solvent is the mixture made of one type or a mixture of more than two types of methyl acetate, acetic ether, n-butyl acetate, amyl acetate, isoamyl acetate, dimethyl carbonate, ethoxyethyl acetate and propylene glycol monomethyl ether acetate; and the solvent oil is one type or a mixture of more than two types of 6 # solvent oil, 90 # solvent oil, 120 # solvent oil and 200 # solvent oil. The environment-friendly neoprene sealant has the advantages of environmental protection, innocuity, pressure resistance, good sealing performance and high strippable property.

Description

technical field [0001] The invention belongs to the field of adhesives, in particular to an environment-friendly chloroprene sealing adhesive and a preparation method thereof. Background technique [0002] Neoprene sealant is a liquid sealant, also known as liquid sealing gasket and liquid gasket. It is a liquid static sealing material with good air tightness, high pressure resistance, oil resistance, water resistance, and mechanical shock resistance. , and has a wide temperature range. Among them, the semi-dry viscoelastic liquid sealant generally contains organic solvents. The film formed by the solvent volatilization after coating can permanently maintain viscoelasticity, pressure resistance, softness and easy disassembly. It is suitable for the automotive industry and machinery manufacturing. It is the most commonly used liquid sealant for sealing and waterproofing in the industry and construction industry. [0003] Neoprene is produced by emulsion polymerization of ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J111/00C09J11/04C09J11/06
Inventor 周树柏杨猛张连红乔雪冬王德鹏匡广际
Owner GLEIHOW NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap