Nickel-based nickel titanium hydrotalcite film material, preparation method and application thereof

A nickel-titanium hydrotalcite and thin film technology, applied in metal material coating process, coating, liquid chemical plating and other directions, can solve problems such as limited application, and achieve the effect of not easy to fall off and tightly combined

Active Publication Date: 2014-07-02
BEIJING UNIV OF CHEM TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that its high resistance and mass transfer resistance limit its practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel-based nickel titanium hydrotalcite film material, preparation method and application thereof
  • Nickel-based nickel titanium hydrotalcite film material, preparation method and application thereof
  • Nickel-based nickel titanium hydrotalcite film material, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A. Use nickel foam with a purity greater than 90% as the base material, cut it into 10*15cm pieces, wash it with 30% concentrated hydrochloric acid for 50 seconds, then ultrasonically wash it with deionized water for 3 times, and wash it with absolute ethanol once. Dry in a 60°C oven for later use.

[0037] B. Dissolve 26.4g Ti(SO 4 ) 2 and 58.15gNi(NO 3 ) 2 Prepared into 1000ml solution a, and then 17.5g Na with deionized water 2 CO 3 Prepare 200ml solution b with 18.65g NaOH. Put the nickel foam treated in step A into solution a, then add solution b dropwise into solution a under strong stirring until the pH of the solution reaches 9.5, transfer them to a polytetrafluoroethylene reactor and put them in an oven React at 90°C for 6h. After the reaction was finished, the nickel foam was taken out, excess sediment on the surface was washed off with deionized water, and dried at 60° C. for 12 hours.

[0038] C. Prepare the same 1000ml solution c as solution a in st...

Embodiment 2

[0040] A. Use nickel foam with a purity greater than 90% as the base material, cut it into pieces of 10*15cm in size, wash it with 30% concentrated hydrochloric acid for 50 seconds, then ultrasonically wash it with deionized water for 3 times, and wash it with absolute ethanol once, and put it Dry in a 60°C oven for later use.

[0041] B. Dissolve 39.6g Ti(SO 4 ) 2 and 87.24gNi(NO 3 ) 2 Prepare 800ml solution a, then prepare 28gNOH and 23.3gNa with deionized water 2 CO 3 225ml mixed solution b. Put the nickel foam treated in step A into solution a, then add solution b dropwise into solution a under strong stirring until the pH of the solution reaches 9, then transfer them together to a 1000ml beaker, and seal the beaker with plastic wrap mouth. Stir vigorously in a water bath at 60°C and react for 5 hours. After the reaction, take out the nickel foam and clean it with deionized water, put it in an oven, and dry it at 60°C for 12 hours.

[0042] C. Dissolve 26.4g Ti(SO ...

Embodiment 3

[0044] A. Use nickel foam with a purity greater than 90% as the base material, cut it into pieces of 10*15cm in size, wash it with 30% concentrated hydrochloric acid for 50 seconds, then ultrasonically wash it with deionized water for 3 times, and wash it with absolute ethanol once, and put it Dry in a 60°C oven for later use.

[0045] B. Dissolve 19.8g Ti(SO 4 ) 2 and 43.6g Ni(NO 3 ) 2 Prepare 750ml of solution a, use deionized water to dissolve 14gNOH and 11.85gNa 2 CO 3 Prepare 250ml of solution b, put the nickel foam treated in step A into solution a, then add solution b dropwise into solution a under strong stirring until the pH of the solution reaches 8.5, and then add it to the tetrafluoroethylene removal reaction In the kettle, react at 80°C for 10h. After the reaction, the nickel foam was cleaned, put into an oven, and dried at 60° C. for 12 hours for later use.

[0046] C. Dissolve 19.8g Ti(SO 4 ) 2 and 43.6g Ni(NO 3 ) 2 Prepare 750ml of solution c, then u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a nickel-based nickel titanium hydrotalcite film material, a preparation method and application of the nickel-based nickel titanium hydrotalcite film material. The material can be used as a super capacitance material and an electric adsorption material; the nickel-based nickel titanium hydrotalcite film material takes foam nickel as a base material, and a nickel-titanium hydrotalcite film grows in situ on the surface. The film has the advantages of complete crystal shape, uniform density, and high adhesive force, and does not easily fall off. The preparation method comprises the steps of: placing a foam nickel sheet into mixed solution of nickel nitrate and titanous sulfate, and planting the nickel-titanium hydrotalcite film in situ on the foam nickel sheet by controlling the reaction conditions such as pH, a reaction temperature and time. A nickel source disclosed by the nickel-based nickel titanium hydrotalcite film material is from the foam nickel surface and nickel salt dissolved into a solution. Compared with a pure hydrotalcite film deposited on a substrate, the prepared film is stronger in adhesive force on a base body, and the material has a better super capacitive property and an electric adsorption performance, and can be used as a super capacitance electrode material and an electric adsorption electrode material.

Description

technical field [0001] The invention relates to a hydroslide film material and a preparation method thereof, in particular to a nickel-titanium hydrotalcite film material and a preparation method and application thereof. Background technique [0002] Under the current trend of rapid technological development, electronic components are becoming smaller and electric vehicles are becoming more and more popular, supercapacitors as backup power and memory backup devices have attracted widespread attention. The current mainstream supercapacitor materials are developed from ruthenium oxide thin film systems and carbon double layers. In Electrochem.Solid State Lett, 2000,3(5):205-208, the specific capacity of the ruthenium-chromium composite oxide made by Manthiram et al. is as high as 840F / g. However, the ruthenium material required for large-capacity capacitors in battery-capacitor hybrid systems used in electric vehicle power sources is very expensive, which is also a very impor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C26/00C23C18/00H01G11/30
CPCY02E60/13
Inventor 雷晓东谷耀行孙晓明
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com