PET (polyethylene glycol terephthalate) fiber/teflon fiber composite sound absorbing cotton and preparation method of PET fiber/teflon fiber composite sound absorbing cotton

A polytetrafluoroethylene and fiber composite technology, applied in the field of non-woven fabrics, can solve problems such as insufficient adhesion of products, no flame-retardant treatment, and poor tensile strength, so as to improve sound absorption effect, good adhesion of products, and production high efficiency effect

Inactive Publication Date: 2013-03-13
芜湖跃飞新型吸音材料股份有限公司
View PDF5 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many deficiencies in the existing sound-absorbing cotton products and their manufacturing methods. The main performances are: the original manual operation, the use of knife stacks, low productivity; no flame-retardant treatment; insufficient adhesion of the product, easy to loose, tension Poor strength, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A PET fiber / polytetrafluoroethylene fiber composite sound-absorbing cotton, made of the following raw materials in parts by weight: 78 parts of PET fiber, 42 parts of polytetrafluoroethylene fiber, 14 parts of emulsifier OP-30, 8 parts of Pingpingjia O-20 85 parts of PP, 35 parts of HIPS, 16 parts of activated clay, 15 parts of modified diatomaceous earth, 2.5 parts of stearic acid, 6 parts of dioctyl adipate, 5 parts of toluene diphenyl phosphate, 2 parts of liquid paraffin , 1.5 parts of 3-aminopropyltrimethoxysilane, 2 parts of calcium stearate, 1.5 parts of barium stearate, 0.8 parts of antioxidant RD, and 1.5 parts of antioxidant DLTP.

[0017] Wherein, the modified diatomite is prepared by the following method: put the dried diatomite into a ball mill, add 28% graphite, 2% vermiculite powder, 3% sepiolite powder, 4% light Calcium carbonate, 2.5% water glass and 4% polyvinyl alcohol, ball milled for 10 hours, calcined at 1150°C for 2 hours, crushed and gro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses PET (polyethylene glycol terephthalate) fiber / teflon fiber composite sound absorbing cotton, which is prepared from the following ingredients in parts by weight: 70 to 80 parts of PET fibers, 40 to 50 parts of teflon fibers, 10 to 15 parts of emulsifying agents OP-30, 5 to 10 parts of peregal O-20, 80 to 100 parts of PP (propene polymer), 30 to 40 parts of HIPS (high impact polystyrene), 15 to 20 parts of activated clay, 10 to 15 parts of modified kieselguhr, 2 to 3 parts of stearic acid, 5 to 8 parts of dioctyl adipate, 4 to 6 parts of cresyl diphenyl phosphate, 2 to 3 parts of liquid paraffin, 1 to 2 parts of 3-aminopropyltrimethoxysilane, 2 to 3 parts of calcium stearate, 1 to 2 parts of barium stearate, 0.5 to 1.5 parts of anti-aging agents RD and 1 to 2 parts of antioxidants DLTP (dilauryl thiodipropionate). The sound absorbing cotton prepared by the invention has the advantages that the appearance evenness is good, the thickness is uniform, the hand feeling is soft, the product bonding degree is good, the tensile performance is high, the sound absorbing performance is excellent, the flame retardant effect is good, and the like.

Description

technical field [0001] The invention relates to nonwoven fabric technology, in particular to a PET fiber / polytetrafluoroethylene fiber composite sound-absorbing cotton and a preparation method thereof. Background technique [0002] Noise is one of the three major public hazards that pollute the environment in modern society. Noise directly affects people's health. With the progress of society, people put forward higher and higher requirements for the prevention and control of noise that pollutes the environment. Sound-absorbing cotton can convert the vibration energy of medium and high-frequency noise generated in life into the kinetic energy of the fine denier fibers inside the sound-absorbing cotton, and convert it into heat energy and disappear, achieving the function of sound absorption and noise reduction. Therefore, sound-absorbing cotton has good sound-absorbing, heat-insulating and warm-keeping properties, and has been widely used in the fields of building materials,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/435D04H1/4318D04H1/4382D04H1/70D04H1/4291D01F8/06D01F1/10C09C1/28C09C3/06C09C3/10C09C3/04G10K11/162
Inventor 王黎明孙益民章云厉曼
Owner 芜湖跃飞新型吸音材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products