Preparation method for styrene-coated ammonium perchlorate

An ammonium perchlorate and styrene technology, which is applied to ammonium perchlorate compositions, explosives, etc., can solve the problems of high surface activity, complex preparation method, and high mechanical sensitivity, and achieves good dispersibility and regularity. Safe and reliable, low production cost effect

Inactive Publication Date: 2013-05-08
SHAANXI NORMAL UNIV
View PDF15 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ammonium perchlorate has the characteristics of large specific surface area, high surface energy, and high surface activity. It is easy to agglomerate or adsorb with other substances during preparation, storage, and transportation to reduce the surface energy. Application of ammonium chlorate in fields with high safety requirements
[0003] The Chinese patent with the patent publication number CN201010198073.8 discloses a method for preparing nano-catalytic composite materials using the integrated process of ultrasonic-membrane-anti-solvent method. The anti-solvent method is used to precipitate ammonium perchlorate from its saturated solution and evenly disperse it in the Nano-catalyst composite materials are formed on nano-catalyst particles, but there are disadvantages such as complicated preparation methods, high equipment requirements, and high energy consumption.
But its yield is low, easy to agglomerate, moisture absorption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for styrene-coated ammonium perchlorate
  • Preparation method for styrene-coated ammonium perchlorate
  • Preparation method for styrene-coated ammonium perchlorate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Taking used raw material ammonium perchlorate 1g as example, the preparation method of its styrene coating ammonium perchlorate is made up of following steps:

[0035] 1. Preparation of styrene monomer

[0036] Styrene was extracted with 7.5% sodium hydroxide aqueous solution, the volume ratio of styrene to 7.5% sodium hydroxide aqueous solution was 1:1, and it was left to stand for 12 hours with anhydrous magnesium sulfate to dry and remove water. Distilled under reduced pressure at 0.09GPa to obtain styrene monomer.

[0037] 2. Ultrasonic dispersion

[0038] Get 1g ammonium perchlorate and join in the flask, add sherwood oil anti-solvent 32.5g, add styrene monomer 0.9g again, the mass ratio of ammonium perchlorate and styrene monomer, sherwood oil anti-solvent is 1:0.9: 32.5, ultrasonically disperse with an ultrasonic cleaner with a power of 300W.

[0039] 3. Styrene coated ammonium perchlorate

[0040] The ultrasonically dispersed solution was stirred and reacted...

Embodiment 2

[0044] Taking used raw material ammonium perchlorate 1g as example, the preparation method of its styrene coating ammonium perchlorate is made up of following steps:

[0045] In step 1 of preparing styrene monomer, styrene is extracted with an aqueous sodium hydroxide solution with a mass concentration of 5%, and the volume ratio of styrene to an aqueous sodium hydroxide solution with a mass concentration of 5% is 1:1. Magnesium sulfate was left to stand for 12 hours to dry and remove water, and 0.09GPa was distilled under reduced pressure to obtain styrene monomer. In ultrasonic dispersion step 2, get 1g ammonium perchlorate and join in the flask, add sherwood oil anti-solvent 32.5g, add styrene monomer 0.6g again, the mixture of ammonium perchlorate and styrene monomer, sherwood oil anti-solvent The mass ratio is 1:0.6:32.5, and ultrasonically disperses with an ultrasonic cleaner with a power of 300W. In step 3 of coating ammonium perchlorate with styrene, the ultrasonicall...

Embodiment 3

[0047] Taking used raw material ammonium perchlorate 1g as example, the preparation method of its styrene coating ammonium perchlorate is made up of following steps:

[0048] In step 1 of preparing styrene monomer, styrene is extracted with 10% sodium hydroxide aqueous solution, the volume ratio of styrene to 10% sodium hydroxide aqueous solution is 1:1, and anhydrous Magnesium sulfate was left to stand for 12 hours to dry and remove water, and 0.09GPa was distilled under reduced pressure to obtain styrene monomer. In ultrasonic dispersion step 2, get 1g ammonium perchlorate and join in the flask, add sherwood oil anti-solvent 32.5g, add styrene monomer 1.2g again, the mixture of ammonium perchlorate and styrene monomer, sherwood oil anti-solvent The mass ratio is 1:1.2:32.5, and ultrasonically disperses with an ultrasonic cleaner with a power of 300W. In step 3 of coating ammonium perchlorate with styrene, the ultrasonically dispersed solution was stirred and reacted at 60° ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for styrene-coated ammonium perchlorate. The preparation method comprises the following steps of: preparing a styrene monomer; ultrasonically dispersing; coating ammonium perchlorate with the styrene; and preparing styrene-coated ammonium perchlorate. According to the preparation method disclosed by the invention, the surface of the ammonium perchlorate is coated by adopting styrene; the coating film is very thin, and the mass of the coating film is smaller than that of the ammonium perchlorate; the influence to the energy characteristic of the propellant is very small; the dispersion and regularity are good; the grain size range is 10 microns to 30 microns; the film coating thickness is controllable; and petroleum ether is adopted as an anti-solvent, so that the styrene-coated ammonium perchlorate material can be prepared within a short time. The preparation method disclosed by the invention has the advantages of being safe and reliable, convenient to operate and low in production cost. The ammonium perchlorate has spherical appearance, good dispersion and uniform grain size after being coated, and so the preparation method can be used for coating the ammonium perchlorate.

Description

technical field [0001] The invention belongs to the technical field of solid propellant materials, in particular to the surface treatment of ammonium perchlorate. Background technique [0002] The main oxidant commonly used in composite solid propellants and mixed explosives is ammonium perchlorate, and the combustion performance of composite solid propellants and mixed explosives is mainly determined by the combustion performance of ammonium perchlorate. Ammonium perchlorate has the characteristics of large specific surface area, high surface energy, and high surface activity. During preparation, storage, and transportation, it is easy to agglomerate or adsorb with other substances to reduce the surface energy. Ammonium chlorate is used in fields with high safety requirements. [0003] The Chinese patent with the patent publication number CN201010198073.8 discloses a method for preparing nano-catalytic composite materials using the integrated process of ultrasonic-membrane...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C06B45/32C06B29/22
Inventor 高子伟张伟强张国防崔丹李子美朱序阳南宝江张文刚
Owner SHAANXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com