Fluidized coating method for flavoring essence micropills for tobacco
A subtle and coating technology, applied in essential oils/spices, tobacco, applications, etc., can solve the problems of easy adhesion of the coating, low coating yield, low drying capacity, etc., to improve coating drying capacity, coating High yield and the effect of overcoming adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] Example 1
[0014] Take 20 parts of methyl cellulose, add it to 800 parts of absolute ethanol, stir for about 30-40 minutes to completely dissolve it, then add 0.5 part of polyethylene glycol, 1 part of stearic acid, 0.5 part of talc, 0.5 part of talc Pigment, and then stir for 30 minutes to make it evenly dispersed, that is, to obtain a coating liquid.
[0015] Add 1000 parts of essence pellets to the FLP type fluidized bed coater, spread them evenly on the mesh at the bottom of the fluidized bed, and send hot air at 40°C with a blast rate of 1.5 to 2.5 m 3 / min, blow the pellets from the bottom of the fluidized bed to a maximum of about 0.3 m, and then throw them down to the bottom of the fluidized bed under the action of gravity. Take 120 parts of the above-mentioned coating liquid for coating, spray the coating liquid from the bottom, so that the coating liquid is coated on the surface of the pellets, and the spraying speed is about 20-35 mL / min, and at the s...
Example Embodiment
[0016] Example 2
[0017] Take 35 parts of hydroxypropyl methylcellulose, add it to a mixture of 100 parts of water and 800 parts of absolute ethanol, stir for about 40-60 minutes to completely dissolve it, then add 1.0 parts of polyethylene glycol, 1 part of hard Magnesium fatty acid, 0.5 part of talcum powder, 0.5 part of pigment, and stirring for 30 minutes to make it evenly dispersed to obtain a coating liquid.
[0018] Add 1000 parts of essence pellets to the FLP type fluidized bed coater, spread them evenly on the mesh at the bottom of the fluidized bed, and send hot air at 50°C with a blast rate of 1.5 to 2.5 m 3 / min, blow the pellets from the bottom of the fluidized bed to a maximum of about 0.3 m, and then throw them down to the bottom of the fluidized bed under the action of gravity. Take 100 parts of the above-mentioned coating solution for coating, spray the coating solution from the bottom, and coat the surface of the pellets with a spraying speed of about...
Example Embodiment
[0019] Example 3
[0020] Take 40 parts of sodium carboxymethyl cellulose, add it to 800 parts of water, stir for about 40-60 minutes to completely dissolve it, then add 0.5 parts of polyvinyl alcohol, 0.5 parts of sodium stearate, 0.5 parts of micropowder silica gel, and 0.5 parts of pigments , and then stirred for 30 minutes to make it evenly dispersed, that is, the coating solution was obtained.
[0021] Add 1000 parts of essence pellets to the FLP type fluidized bed coater, spread them evenly on the mesh at the bottom of the fluidized bed, and send hot air at 55°C with a blast rate of 1.5-2.5 m 3 / min, blow the pellets from the bottom of the fluidized bed to a maximum of about 0.3 m, and then throw them down to the bottom of the fluidized bed under the action of gravity. Take 50 parts of the above-mentioned coating solution for coating, spray the coating solution from the bottom, and coat the surface of the pellets with a spraying speed of about 20-25 mL / min, and at...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap