Preparation method of rosin-based shape-memory polyurethane

A polyurethane and rosin-based technology is applied in the field of preparation of rosin-based shape memory polyurethane to achieve the effects of easy implementation, high recovery and easy industrial production

Active Publication Date: 2014-12-03
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, so far, the synthesis of thermoplastic shape memory polymers with high recovery performance using biomass resources as raw materials has not been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of rosin-based shape-memory polyurethane
  • Preparation method of rosin-based shape-memory polyurethane
  • Preparation method of rosin-based shape-memory polyurethane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Rosin diacid (formula III, R 1 benzene ring segment) 51.926g, ethylene glycol (HO-R 2 -OH, R 2 for C 2 aliphatic segment) 12.4g, sulfuric acid 0.04g, reacted at 150°C for 5h under nitrogen protection, washed with 0.1mol NaOH aqueous solution after the reaction, removed excess ethylene glycol and possibly unreacted rosin diacid to obtain crude product, The crude product was washed with methanol and dried under vacuum to obtain a rosin-based chain extender with the structure of formula I (ie, ethylene glycol rosin dioate).

[0054]

[0055] The NMR spectrum of the rosin-based chain extender of the formula I structure prepared in Example 1 is as figure 1 As shown, the solvent is deuterated chloroform, and the internal standard is tetramethylsilane. δ=5.5ppm is the hydrogen on the double bond on the rosin skeleton (shown at position a on the figure), and its integral area is 1, which can prove the existence of the rosin skeleton. The four groups of peaks at δ=3.8ppm...

Embodiment 2

[0058] Rosin diacid (formula IV) 37.4g, ethylene glycol (HO-R 2 -OH,R 2 for C 2 aliphatic segment) 12.4g, p-toluenesulfonic acid 0.04g, reacted at 150°C for 5h under nitrogen protection, washed with 0.1mol NaOH aqueous solution after the reaction, removed excess ethylene glycol and possibly unreacted abietic diacid to obtain crude product , the crude product was washed with ethanol, and dried in vacuum to obtain a rosin-based chain extender with a structure of formula II (ie, ethylene glycol rosin dioate).

[0059]

[0060] Among them, R 2 for

[0061] The NMR spectrum of the rosin-based chain extender of the formula II structure prepared in Example 2 is as follows figure 2 As shown, the solvent is deuterated chloroform, and the internal standard is tetramethylsilane. δ=5.5ppm is the hydrogen on the double bond on the rosin skeleton (shown at position a on the figure), and its integral area is 1, which can prove the existence of the rosin skeleton. δ=3.8ppm-3.9ppm,...

Embodiment 3

[0063] Rosin diacid (formula III, R 1 Methylene) 45.73g, methanol 6.4g, phosphoric acid 0.036g, react at 45°C for 5h, distill off excess methanol under reduced pressure to obtain dimethyl abietate. Then add 36g of 1,3-propanediol (HO-R 2 -OH, R 2 for C 3 The aliphatic chain segment) was reacted at 150°C, methanol was distilled off during the reaction, and the reaction ended after 5 hours. After the reaction, wash with water to wash off excess 1,3-propanediol to obtain a crude product, then wash with methanol, and dry in vacuum to obtain a rosin-based chain extender with the structure of formula I (ie propylene glycol rosindialate). It can be proved that the prepared rosin-based chain extender has the structure of formula I by proton nuclear magnetic spectrum and infrared spectrum.

[0064]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of rosin-based shape-memory polyurethane. According to the preparation method, the rosin-based shape-memory polyurethane is obtained in a manner that polylol, diisocyanate and a rosin-based chain extender are synthesized under the action of a catalyst by a one-step or two-step method; and the rosin-based chain extender is a compound with the structure of a formula I or II (shown in drawings). According to the preparation method of the rosin-based shape-memory polyurethane, disclosed by the invention, the preparation is simple, the implementation is easy, and the operability is strong, so that the large-scale industrial production is facilitated; and meanwhile, the prepared rosin-based shape-memory polyurethane has excellent resilience, is very suitable for serving as a shape memory material and expresses excellent shape-memory properties.

Description

technical field [0001] The invention relates to the field of polyurethane shape-memory polymer materials, in particular to a preparation method of rosin-based shape-memory polyurethane. Background technique [0002] Shape memory materials are a class of stimuli-responsive smart materials. The so-called shape memory means that the material can be restored under external stimuli (such as light, heat, electricity, magnetism, pH, etc.) to the properties of the initial shape. [0003] In the 1960s, people first discovered the shape memory function of Ni-Ti alloy, and then shape memory materials attracted worldwide attention. In the 1980s, Ota.SLl and others found that the obtained material had a very good thermal recovery shape memory effect through the method of radiation cross-linked polyethylene, becoming the world's first shape memory polymer (SMP, Shape Memory Polymer) material ( Ota. S. The heat shrinkage properties of polyethylene [J]. Radiate Physics Chemistry, 1981, (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/67C08L75/14
Inventor 张立生熊竹张传芝朱锦
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI