Plasma-etching-resistant granulated yttrium oxide for hot spraying and preparation method thereof

A technology of ion corrosion and yttrium oxide, which is applied in the field of thermal spraying, can solve the problems of uneven plasma corrosion resistance of thermal spraying coatings, uneven thickness of thermal spraying coatings, and influence on powder stability, etc., so as to improve energy utilization rate, Uniform plasma corrosion resistance and stable supply

Active Publication Date: 2013-12-18
CHANGZHOU GEOQUIN NANO NEW MATERIALS
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sphericity of the thermal spray powder will also have a certain impact on the quality of the thermal spray coating. If the sphericity is not good, it will affect the stability of the powder supply during thermal spraying, and the thickness of the thermal spraying coating will be uneven. Therefore, it will also cause uneven plasma corrosion resistance of thermal sprayed coatings.
In order to improve the sphericity of the thermal spray powder after sintering, it is often necessary to use some methods to spheroidize it, which undoubtedly increases the investment in equipment and increases the production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plasma-etching-resistant granulated yttrium oxide for hot spraying and preparation method thereof
  • Plasma-etching-resistant granulated yttrium oxide for hot spraying and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1）

[0032] A preparation method of granulated yttrium oxide for plasma corrosion-resistant thermal spraying of the present invention is carried out according to the following steps:

[0033] (1) Mix 10kg of yttrium oxide powder with a purity of ≥99.99% and a particle size of 0.2 μm with deionized water at a weight ratio of 1:2, and stir evenly to prepare a slurry;

[0034] (2) Inject the slurry into the depolymerization machine for depolymerization and reduction, and the depolymerization time is 30 minutes; the D50 of the slurry after depolymerization is 0.4 μm;

[0035] (3) Stir the slurry after depolymerization and reduction, take 80g of malic acid crystals and add 160g of deionized water to fully dissolve it, add it to the slurry, and accelerate the stirring. The pH value of the slurry is 6, and the viscosity is 15mPa·s;

[0036] (4) Pass the slurry through thermal expansion ball making equipment to make yttrium oxide spherical powder;

[0037] (5) The yttrium oxide spherical ...

Embodiment 2）

[0040] A preparation method of granulated yttrium oxide for plasma corrosion-resistant thermal spraying of the present invention is carried out according to the following steps:

[0041] (1) Mix 10kg of yttrium oxide powder with a purity of ≥99.99% and a particle size of 0.07um with absolute ethanol at a weight ratio of 1:2, and stir evenly to prepare a slurry;

[0042] (2) Inject the slurry into the depolymerization machine for depolymerization and reduction, and the depolymerization time is 30 minutes; the D50 of the slurry after depolymerization is 0.1 μm;

[0043] (3) Stir the slurry after depolymerization and reduction, take 100g of a crystal mixture of malic acid, acetic acid, and oxalic acid (4:3:3 by weight) and add 200g of deionized water to fully dissolve it, add it to the slurry, and accelerate Stir, the pH value of the slurry is 6, and the viscosity is 17mPa·s;

[0044] (4) Pass the slurry through thermal expansion ball making equipment to make yttrium oxide spheric...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
sizeaaaaaaaaaa
bulk densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of hot spraying, and particularly relates to plasma-etching-resistant granulated yttrium oxide for hot spraying and a preparation method thereof. The preparation method of the plasma-etching-resistant granulated yttrium oxide for hot spraying comprises the following steps: preparing nano or ultrafine yttrium oxide powder and deionized water or an organic solution into a paste, performing depolymerization and reduction, adding surface activity activator into the paste for preparation, and performing hot expansion balling and high-temperature densification treatment to obtain the granulated yttrium oxide for hot spraying. According to the invention, the surface activity activator is added into the paste before hot expansion balling, so that the prepared granulated yttrium oxide for hot spraying is favorable in spherical degree, and the high-spherical-degree favorable-flowability high-density granulated yttrium oxide for hot spraying can be obtained without later spheroidization, thereby achieving favorable flowability during hot spraying, ensuring that the supply of the granulated yttrium oxide for hot spraying is more stable, and providing a guarantee for obtaining a hot spray coating having a uniform thickness.

Description

technical field [0001] The invention belongs to the technical field of thermal spraying, and in particular relates to a granulated yttrium oxide for plasma corrosion-resistant thermal spraying and a preparation method thereof. Background technique [0002] Yttrium oxide has high melting point, phase stability and low thermal expansion, and is an important raw material for preparing high-performance electronic ceramics and anti-plasma corrosion spray powder. And the application of yttrium oxide in the fields of aviation, aerospace, and ceramics also shows its superior performance. It is mainly used to manufacture magnetic materials for microwaves and important materials for military industry. It is also used as an additive for optical glass, ceramic materials, and high-brightness for large-screen TVs. Phosphors and other kinescope coatings. It is also used to manufacture high-temperature strong heat-resistant alloys, aircraft nozzles, etc. In recent years, yttrium oxide powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/505C04B35/622C04B35/632
Inventor 施丽萍
Owner CHANGZHOU GEOQUIN NANO NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com