A kind of UV curable high temperature resistant pressure sensitive adhesive and preparation method thereof

A pressure-sensitive adhesive, ultraviolet light technology, applied in the direction of adhesives, graft polymer adhesives, adhesive types, etc., can solve the problems of non-acrylate pressure-sensitive adhesive modification, etc., to achieve good high temperature shear performance Effect

Inactive Publication Date: 2016-08-31
TONSAN ADHESIVES INC
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The point is that the tape is thermally conductive and does not involve higher temperature resistance or bonding to low-surface-energy materials. The patent does not modify the acrylate pressure-sensitive adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of UV curable high temperature resistant pressure sensitive adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The present invention relates to the preparation of a high temperature resistant pressure sensitive adhesive, the preparation process comprising:

[0042] (a) A solvent-free UV-curable prepolymer consisting of

[0043] ① Contains about 80-98% (by weight) of soft monomer and 2-20% (by weight) of hard monomer. ;

[0044] Soft monomers include one or more mixtures of the following: ethyl acrylate, n-octyl acrylate, isooctyl acrylate, 2-ethylhexyl acrylate, n-butyl acrylate, tert-butyl acrylate, n-nonyl acrylate , isononyl acrylate, n-decyl acrylate, isodecyl acrylate, dodecyl acrylate.

[0045] Hard monomers include one or more of the following mixtures: acrylic acid, methacrylic acid, acrylonitrile, styrene

[0046] (b) one or more functional monomers

[0047] It is selected from:

[0048] ①A monofunctional monomer: (meth)acrylic acid, (meth)hydroxyethyl acrylate, (meth)hydroxypropyl acrylate, (meth)hydroxybutyl acrylate, acrylamide, N-vinyl caprolactam, N-vinylpyrr...

Embodiment 1

[0064] Add 0.15 parts of bis(multi)functional acrylate, 0.1~0.5 parts of photoinitiator to 100 parts of the above prepolymer, stir evenly and remove air bubbles, and apply it between two layers of transparent anti-adhesive films with a thickness of 1.0mm , and then placed in a 40W UV lamp for UV curing.

Embodiment 2

[0066] Add 5-15 parts of vinyl siloxane, 0.15 parts of (multi-) bifunctional acrylate, and 0.1-0.5 parts of photoinitiator to 100 parts of the above-mentioned prepolymer. After stirring evenly and removing air bubbles, spread it between two layers of transparent anti-adhesive films with a thickness of 1.0mm, and then put it into a 40W ultraviolet lamp for curing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is a UV-curable high-temperature-resistant pressure-sensitive adhesive, comprising a solvent-free UV-curable prepolymer of 80-98% by weight of soft monomer and 2-20% of hard monomer; One or more functional monomers, including monofunctional monomers, difunctional or polyfunctional monomers; one or more organosiloxanes with reactive groups or acrylates grafted therefrom; optical Initiator; including free radical cleavage type photoinitiator, hydrogen abstraction type free radical photoinitiator and ionic photoinitiator; the whole process of preparing the pressure sensitive adhesive of the present invention does not contain any volatile organic solvent, and is environmentally friendly; the pressure sensitive adhesive The adhesive tape has good high-temperature shear resistance; the pressure-sensitive adhesive tape has good peel strength for low surface energy materials; Thick products.

Description

technical field [0001] The invention relates to the preparation of pressure-sensitive adhesives and pressure-sensitive adhesive tapes, in particular to a pressure-sensitive adhesive that is environmentally friendly, solvent-free, UV-curable, has certain temperature resistance, and has good bonding strength to low surface energy materials and a method for preparing the pressure-sensitive adhesive tape. Background technique [0002] In recent years, the preparation of pressure-sensitive adhesives and pressure-sensitive tapes that are resistant to high temperatures and suitable for bonding low surface energy materials has mainly focused on solvent-based silicone pressure-sensitive adhesives and solvent-based acrylate pressure-sensitive adhesives, or solvent-based silicone modified adhesives. Research on permanent acrylate pressure sensitive adhesive. The production of these pressure-sensitive adhesives needs to use a large amount of organic solvents such as: toluene, ethyl ace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J151/00C09J133/08C09J7/00C08F220/18C08F220/06
Inventor 王林青王兵林新松李印柏翟海潮
Owner TONSAN ADHESIVES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com