Anti-radiation latex paint and preparation method thereof

A technology of anti-radiation and latex paint, which is applied in the field of anti-radiation latex paint and its preparation, can solve the problems affecting the effect of electromagnetic radiation protection, and achieve the effects of improving the anti-radiation effect, short construction period, and simple production process

Active Publication Date: 2016-07-20
SKSHU PAINT
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this patent, the anti-electromagnetic radiation effect is only through the absorption of electromagnetic wave clutter by materials such as zinc oxide whiskers, nano-metal nickel powder, and nano-silicon carbide. When the electromagnetic wave is relatively strong, it will directly affect protection against electromagnetic radiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-radiation latex paint and preparation method thereof
  • Anti-radiation latex paint and preparation method thereof
  • Anti-radiation latex paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] The preparation method of above-mentioned anti-radiation latex paint, it comprises the following steps carried out in sequence:

[0045] 1) Mix 10-30 parts of water, 0.1-1.0 parts of cellulose, 0.01-0.5 parts of alkaline pH regulator, 0.1-1.0 parts of wetting agent, 0.1-1.0 parts of dispersing agent under stirring at 200-900r / min , 0.1-1.0 parts of bactericide, 0.1-1.0 parts of fungicide and 0.1-0.5 parts of defoamer are added to the container, and stirred for 5-20min;

[0046] 2) Continue to add 15-25 parts of titanium dioxide, 5-15 parts of calcium carbonate and 3-10 parts of anti-radiation conductive materials into the container under stirring at a speed of 1500-3200r / min, and beat for 15-30 minutes;

[0047]3) After stirring at a speed of 500-1000r / min, continue to add 0.5-3.0 parts of antifreeze, 1.0-5.0 parts of film-forming aids, 20-40 parts of emulsion, and 0.1-0.5 parts of defoamer into the container, and stir evenly Finally, use 0.1-2.0 parts of thickener and...

Embodiment 1

[0056] Anti-radiation latex paint, which is made of the following raw materials in weight ratio:

[0057]

[0058]

[0059] The preparation method of above-mentioned anti-radiation latex paint, it comprises the following steps carried out in sequence:

[0060] 1) Mix 25 parts of water, 0.35 part of cellulose, 0.2 part of alkaline pH regulator, 0.15 part of wetting agent, 0.6 part of dispersant, 0.2 part of fungicide, 0.2 part of antifungal agent under stirring at 600r / min Add 0.3 parts of defoamer to the container and stir for 10 minutes;

[0061] 2) Then, at 2000r / min, continue to add 21.6 parts of titanium dioxide, 5 parts of calcium carbonate and 3 parts of radiation-proof conductive materials into the container, and beat for 20 minutes;

[0062] 3) After stirring at a speed of 900r / min, continue to add 1.5 parts of antifreeze, 1.2 parts of film-forming aids, 35 parts of emulsion, and 0.5 parts of defoamer to the container. After stirring evenly, use 0.2 parts of thi...

Embodiment 2

[0070] Anti-radiation latex paint, which is made of the following raw materials in weight ratio:

[0071]

[0072]

[0073] The preparation method of above-mentioned anti-radiation latex paint, it comprises the following steps carried out in sequence:

[0074] 1) Mix 18 parts of water, 0.5 part of cellulose, 0.5 part of alkaline pH regulator, 0.1 part of wetting agent, 0.5 part of dispersant, 0.1 part of fungicide, 0.5 part of antifungal agent and Add 0.15 parts of defoamer into the container and stir for 15 minutes;

[0075] 2) Continue to add 15 parts of titanium dioxide, 10 parts of calcium carbonate and 8.8 parts of anti-radiation conductive materials into the container under stirring at a speed of 3200r / min, and beat for 30 minutes;

[0076] 3) After stirring at 1000r / min, continue to add 2.0 parts of antifreeze, 1.0 parts of film-forming aid, 40 parts of emulsion, and 0.35 parts of defoamer to the container. After stirring evenly, use 0.5 parts of thickener and 2 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of architectural coatings, and particularly relates to a radiation-proof latex paint and a preparation method thereof; the radiation-proof latex paint is made of the following raw materials in the weight ratio: water: 10-38 parts, cellulose: 0.1 -1.0 parts, alkaline pH regulator: 0.01-0.5 parts, wetting agent: 0.1-1.0 parts, dispersant: 0.1-1.0 parts, fungicide: 0.1-1.0 parts, antifungal agent: 0.1-1.0 parts, defoaming Agent: 0.2-1.0 parts, titanium dioxide: 15-25 parts, calcium carbonate: 5-15 parts, radiation-proof conductive material: 3-10 parts, antifreeze: 0.5-3.0 parts, film-forming aid: 1.0-5.0 parts , emulsion: 20-40 parts, thickener: 0.1-2.0 parts; the radiation-proof conductive material is made of SnO 2 , Sb 2 o 3 The metal oxide nano-ultrafine particle powder prepared according to the weight ratio of 1-10 parts: 0.5-5 parts: 1-15 parts with barite powder; the present invention can greatly improve the effect of radiation protection and reduce the harm of radiation to the human body .

Description

technical field [0001] The invention belongs to the field of architectural coatings, in particular to a radiation-proof latex paint and a preparation method thereof. Background technique [0002] With the continuous progress of human society and the development of science and technology, various electrical products are constantly being born, such as mobile phones, TVs, computers and microwave ovens. These products bring a lot of convenience to people, but also release a lot of electromagnetic radiation. [0003] Although electromagnetic radiation pollution is invisible to us, it is self-evident to people's physical harm, mainly affecting the nervous system, cardiovascular system, immune system, eyes and reproductive system. [0004] The hazards of electromagnetic radiation can cause symptoms such as dizziness, headache, fatigue, inattention, memory loss, insomnia, palpitations, chest tightness, dry mouth, decreased immune function, cataracts, women's menstrual disorders, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D133/04C09D5/02C09D5/24C09D7/12
Inventor 洪杰张育乾
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com