Flexible oil-proof modified polyvinyl chloride (PVC) cable sheath material

A polyvinyl chloride cable, polyvinyl chloride technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of poor chemical stability, threat to life and property safety, short service life, etc., and achieve good processing performance and mechanical properties. Performance, broad market application prospects, chemical resistance effect

Inactive Publication Date: 2014-02-05
LVBAO CABLE GROUP
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten the safety of people's lives and property. Therefore, it is urgent to change the original sheath material formula and improve the material performance to meet the diverse needs of the cable market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0009] This embodiment contains the following raw materials in parts by weight: SG-4 polyvinyl chloride 35, EVA 18, metallocene linear low-density polyethylene 16, beryllium oxide 4, silicon carbide 15, attapulgite 6, accelerator Na-22 2, Epoxy linseed oil 18, N660 carbon black 28, zinc oxide 4, stearic acid 4, antioxidant 4010 2, asbestos powder 4, tributyl citrate 21, additives 15.

[0010] The auxiliary agent contains the following raw materials in parts by weight: lapis lazuli 25, crosslinking agent TAC 5, trimethylolpropane triacrylate 3, accelerator TMTD 2, polyisobutylene 3, aluminate coupling agent DL-411 2. Ferrocene 3, lead dibasic phosphite 2, aluminum nitride powder 3, nano jade powder 3, methyl acrylate 3, Zanthoxylum bungeanum seed oil 2; the preparation method is to put lapis lazuli in a calciner at 570°C Calcined for 4 hours, cooled, crushed into 80 mesh, soaked in 15% hydrochloric acid solution for 3 hours, filtered out lapis lazuli powder, washed with water, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cable material, and in particular relates to a flexible oil-proof modified polyvinyl chloride (PVC) cable sheath material. The material is prepared from the following raw materials in parts by weight: 32-35 parts of SG-4PVC, 14-18 parts of EVA (ethylene-vinyl acetate), 14-16 parts of metallocene linear low-density polyethylene, 3-4 parts of beryllium oxide, 11-15 parts of silicon carbide, 4-6 parts of attapulgite, 1-2 parts of accelerator Na-22, 16-19 parts of epoxy linseed oil, 24-28 parts of N660 carbon black, 3-4 parts of zinc oxide, 3-4 parts of stearic acid, 1-2 parts of anti-aging agent 4010, 3-4 parts of asbestos powder, 17-21 parts of tributyl citrate, and 14-16 parts of additive; the advantages of the raw materials such as SG-4PVC, the EVA and the metallocene linear low-density polyethylene are combined through the insulating material, the prepared material is firm and flexible, oil permeation resistant, low temperature embrittling resistant, chemical medicine erosion resistant, and safe and reliable in use, and can be widely used for manufacturing various cable sheath insulating materials, and the market demand prospect is wide.

Description

technical field [0001] The invention relates to a cable material, in particular to a flexible oil-resistant modified polyvinyl chloride cable sheath material and a preparation method thereof. Background technique [0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten people's life and property safety, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/08C08K13/06C08K9/02C08K3/22C08K3/34C08K5/151C08K3/04C08K5/09C08K5/11H01B3/44
Inventor 谢华
Owner LVBAO CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products