A kind of corneal contact lens polishing liquid and preparation method thereof

A technology for contact lenses and polishing fluids, which is applied in the direction of polishing compositions containing abrasives, etc., can solve the problems that the dispersibility of polishing powder cannot be fundamentally improved, the difficulty of uniform dispersion of polishing powder, and the poor dispersibility of inorganic polishing powder, etc., to achieve Excellent polishing effect, long-lasting polishing effect, and gloss-enhancing effect

Active Publication Date: 2016-03-02
AUTEK CHINA
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] (1) The poor dispersion of inorganic polishing powder in the organic system makes it difficult to evenly disperse the polishing powder in the system. Even if it is pre-surface treated, it still cannot fundamentally improve the dispersion of the polishing powder in the organic system
Because the polishing powder is not effectively dispersed, it is easy to agglomerate into larger particles, which directly affects the polishing effect and increases the chance of scratches on the lens surface;
[0005] (2) The cost of the oily system is high, which brings great inconvenience to the subsequent processing of the lens. At the same time, the discarded polishing fluid pollutes the environment and does not conform to the concept of green environmental protection;
[0006] (3) The polishing liquid of the organic system greatly increases the production cost, and organic compounds such as methanol have high toxicity, which puts higher requirements on the production environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of corneal contact lens polishing liquid and preparation method thereof
  • A kind of corneal contact lens polishing liquid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The method for preparing the contact lens polishing solution of the present invention, the steps are:

[0033] (1) Mix 18 Al 2 o 3 Add 2 parts of polyacrylamide to 100 parts of 90°C water at one time, stir until the water temperature drops to 25°C;

[0034] (2) Add 10 parts of xanthan gum to the above mixture, and continue to stir until it is completely dissolved;

[0035] (3) Add 18 parts of glycerin, 0.5 parts of coconut oil diethanolamide, 0.5 parts of stearic acid diethanolamide, 0.5 parts of lauryl dimethyl betaine, 0.5 parts of lauryl amidopropylamine oxide, 0.17 parts of ten Dialkyl dimethyl amine oxide, 0.1 part cocamidopropyl amine oxide, 0.08 part lauryl dimethyl benzyl ammonium chloride, 0.09 part cetyl trimethyl ammonium chloride, 0.21 part ten Octyltrimethylammonium chloride, 0.5 part of dodecylbenzenesulfonic acid, 0.6 part of sodium lauryl sulfate, 0.12 part of isopropyl myristate, 0.1 part of isopropyl palmitate, 0.15 part of mono Glyceryl stearate, ...

Embodiment 2

[0037] The method for preparing the contact lens polishing solution of the present invention, the steps are:

[0038] (1) Add 6 copies of Al 2 o 3 , 9 parts of SiO 2 , Add 3 parts of polyethylene glycol and 2 parts of ammonium polyacrylate to 100 parts of water at 60°C at one time, and stir until the water temperature drops to 25°C;

[0039] (2) Take 1 part of xanthan gum and add it to the above mixture, and continue to stir until it is completely dissolved;

[0040] (3) Add 5 parts of sodium hyaluronate, 5 parts of glycerin, 5 parts of propylene glycol, 5 parts of butanediol, 5 parts of xylitol, 5 parts of sorbitol and 3 parts of coconut oil diethanolamide into the above mixture at the same time , stirred and mixed at room temperature for 6 hours.

Embodiment 3

[0042] The method for preparing the contact lens polishing solution of the present invention, the steps are:

[0043] (1) Mix 5 Al 2 o 3 , 5 parts of SiO 2 , 5 parts CeO 2 , 5 parts of ZrO 2 Add 5 parts of polyacrylic acid amine to 100 parts of water at 100°C at one time, and stir until the water temperature drops to 25°C;

[0044](2) Add 15 parts of xanthan gum to the above mixture, and continue to stir until it is completely decomposed;

[0045] (3) Add 20 parts of xylitol, 10 parts of sorbitol, 3 parts of stearic acid diethanolamide, and 2 parts of dodecyl dimethyl betaine to the above mixture at one time, and stir at room temperature Mix for 6.5 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a corneal contact lens polishing solution which comprises the following components in parts by weight: 10-30 parts of inorganic polishing powder, 0.5-5 parts of dispersing agent, 1-15 parts of thickening agent, 10-30 parts of moistening agent, 0.1-5 parts of surfactant and 100 parts of water. A preparation method of the corneal contact lens polishing solution comprises the following steps: (1) putting 100 parts by weight of hot water into a beaker, adding 10-30 parts by weight of inorganic polishing powder and 0.5-5 parts by weight of dispersing agent into the hot water, and stirring and dispersing till the water temperature is reduced to be the room temperature, so as to obtain suspension; (2) adding 1-15 parts by weight of thickening agent into the suspension, and stirring till the thickening agent is completely decomposed so as to obtain a mixture solution; (3) adding 10-30 parts by weight of moistening agent and 0.1-5 parts by weight of surfactant into the mixture solution of the step (2) at one time, and continuing stirring till a uniform mixture solution is obtained, that is, the high-performance polishing solution for hard contact lenses.

Description

technical field [0001] The invention relates to the field of corneal contact lenses, in particular to a contact lens polishing solution and a preparation method thereof. Background technique [0002] RGP is a kind of rigid contact lens that can provide good optical quality. It is mostly used clinically to treat diseases such as keratoconus, high myopia, and anisometropia. In recent years, it has also been gradually used to treat myopia in children and adolescents. As a special RGP lens, orthokeratology lenses have the outstanding advantage of being used for "orthopedics", that is, to improve vision by changing the shape of the cornea collection. Its orthokeratology effect is similar to that of laser surgery, but different from laser surgery, the effect of orthokeratology lens is temporary and recoverable, and it is an effective and reversible treatment method for non-surgical removal of myopia glasses. Effectively reduce the risk of irreversible damage caused by surgery. W...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02
Inventor 柳翠英许鹏
Owner AUTEK CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap