Special UV (Ultraviolet) curing antibacterial coating for plastics, and preparation method thereof

An antibacterial coating and plastic technology, used in epoxy resin coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of low hardness, poor adhesion and impact resistance, large shrinkage rate, etc., and achieve leveling The effect of good performance, good flexibility and high production efficiency

Inactive Publication Date: 2014-06-04
WUHU EDISON AUTOMATION EQUIP
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current UV curing materials are various, but there are still some problems to varying degrees. The existing UV curing coatings have a large shrinkage rate after photocuring and produce shrinkage stress, resulting in brittleness of the coating film, adhesion and impact resistance. Poor, poor flexibility and low hardness of the coating film, no corrosion resistance, easy yellowing and aging, etc. These series of problems need to be continuously improved for different purposes, reduce production costs, and expand uses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A special UV curing antibacterial coating for plastics, prepared from the following raw materials in parts by weight (kg): epoxy acrylate 50, polyethylene glycol diacrylate 9, hydroxypropyl acrylate 7, glycidyl acrylate 4, 2 -Methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1-propanone 3, lauric acid methacrylate 12, ethyl acetate 9, polydimethyl Siloxane 1, silane coupling agent KH550 1, nano wollastonite 6, lithopone 3, IPBC1, additive 4;

[0016] The auxiliary agent is made of the following raw materials in parts by weight (kg): barite 10, bamboo charcoal 5, nano-silica 5, epoxy soybean oil 1, lemon essential oil 0.1, lauric acid methacrylate 4, acrylic acid hydroxyl Ethyl ester 3, silane coupling agent KH560 2, hydroxyethyl methacrylate 20; the preparation method is to put barite in a calciner and calcinate at 520-540°C for 3-4 hours, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a special UV (Ultraviolet) curing antibacterial coating for plastics. The special UV curing antibacterial coating for plastics is characterized by being prepared from the following active ingredients in parts by weight: 50-55 parts of epoxy acrylate, 9-12 parts of polyethyleneglycol diacrylate, 7-10 parts of hydroxypropyl acrylate, 4-6 parts of glycidyl acrylate, 3-4 parts of 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1-acetone, 12-15 parts of methacrylate laurate, 9-12 parts of ethyl acetate, 1-2 parts of polydimethyl siloxane, 1-2 parts of silane coupling agent KH550, 6-8 parts of nanometer wollastonite, 3-4 parts of lithopone, 1-2 parts of IPBC (iodopropynyl butylcarbamate), and 4-5 parts of auxiliaries. Due to added IPBC antibacterial substances, the special UV curing antibacterial coating has the effects of oxidation resistance and mildew repression; due to the auxiliaries, the coating is good in leveling property, good in flexibility, hardness, adhesion force, wear resistance and scratch resistance, energy-saving and environment-friendly, and high in production efficiency and application to plastic surfaces.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a special UV curing antibacterial paint for plastics and a preparation method thereof. Background technique [0002] UV curing coatings have become a relatively mature technology, especially with the improvement of people's awareness of environmental protection, production and researchers pay more attention to the development and application of UV curing coatings. UV curing coating is a kind of green and environment-friendly coating, which fully complies with the "4E" principle. Generally, the energy consumption of UV curing is 1 / 5 of that of thermal curing, and UV curing coating contains less volatile components and less pollution. It is most attractive to researchers. And the developer's advantage is that UV curing coatings can reduce raw material consumption, which is beneficial to reduce economic costs. [0003] The current UV curing materials are various, but ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D5/14C09D7/12
CPCY02P20/10
Inventor 汤广顺
Owner WUHU EDISON AUTOMATION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products